Method and apparatus for producing electrolytic aluminum foil

Patent metadata

Field	Value
Publication number	US-11519090-B2
Application number	US-201916438324-A
Country	US
Kind code	B2
Filing date	Jun 11, 2019
Priority date	Dec 16, 2016
Publication date	Dec 6, 2022
Grant date	Dec 6, 2022

Abstract

The method for producing an electrolytic aluminum foil of the present disclosure is a method for producing an electrolytic aluminum foil, the method including supplying an electrolytic solution in an electrolytic cell provided with a diaphragm between an anode and a cathode and depositing an aluminum foil on a surface of the cathode by electrolysis, wherein the diaphragm is made of aluminum having a purity of 85.0% or more and has a plurality of pores having an average pore diameter of 100 to 1000 μm.

First claim

What is claimed is:

1. A method for producing an electrolytic aluminum foil, the method comprising:
supplying an electrolytic solution in an electrolytic cell provided with a diaphragm between an anode and a cathode, wherein the electrolytic solution is a molten salt containing an alkylimidazolium halide or an alkylpyridinium halide and an aluminum halide;
depositing an aluminum foil on a surface of the cathode by electrolysis, wherein
the diaphragm is made of aluminum having a purity of 85.0% or more and less than 99.9% and has a plurality of pores having an average pore diameter of 100 to 1000 μm; and
trapping an impurity, by at least one of the plurality of pores of the diaphragm.

2. The method for producing an electrolytic aluminum foil according to claim 1 , wherein the diaphragm is prepared by mixing and sintering an aluminum powder and a substance for forming pores and thereafter removing the substance for forming pores.

3. The method for producing an electrolytic aluminum foil according to claim 1 , wherein the electrolytic solution is a molten salt containing an alkylimidazolium chloride or an alkylpyridinium chloride and aluminum chloride.

4. The method for producing an electrolytic aluminum foil according to claim 1 , wherein
the cathode is made of titanium; and
the anode is made of aluminum having a purity of 95.0 to 99.9%.

5. An apparatus for producing an electrolytic aluminum foil, comprising:
an electrolytic cell in which an electrolytic solution is supplied, wherein the electrolytic solution is a molten salt containing an alkylimidazolium halide or an alkylpyridinium halide and an aluminum halide;
an anode and a cathode each to be immersed in the electrolytic solution; and
a diaphragm provided between the anode and the cathode, and
the apparatus depositing an aluminum foil on a surface of the cathode by electrolysis,
wherein the diaphragm is made of aluminum having a purity of 85.0% or more and less than 99.9% and has a plurality of pores having an average pore diameter of 100 to 1000 μm, and wherein the plurality of pores of the diaphragm is configured to trap an impurity.

6. The method of claim 1 , wherein the diaphragm has a porosity of 80 to 90%.

7. A method for producing an electrolytic aluminum foil, the method comprising:
supplying an electrolytic solution in an electrolytic cell provided with a diaphragm between an anode and a cathode;
depositing an aluminum foil on a surface of the cathode by electrolysis, wherein
the diaphragm is made of aluminum having a purity of 85.0% or more and has a plurality of pores having an average pore diameter of 100 to 1000 μm, wherein the diaphragm is prepared by mixing and sintering an aluminum powder and a substance for forming pores and thereafter removing the substance for forming pores; and
trapping an impurity; by at least one of the plurality of pores of the diaphragm, further comprising:
press-molding a mixture of the aluminum powder and the substance for forming pores at a pressure of 200 to 300 MPa.

8. The method of claim 7 , wherein a temperature of the sintering is raised from room temperature to 665° C. over one hour in a vacuum of less than 10 −2 Pa, and wherein the sintering is performed at a temperature of 665° C. for 5 to 20 minutes.

9. The method of claim 1 , wherein the impurity comprises a noble metal dissolved from the anode.

10. The apparatus of claim 5 , wherein the impurity comprises a noble metal dissolved from the anode.

Assignees

• Uacj Corp

Inventors

• Honkawa Yukio
• NUNOMURA Junji
• Kojima Yoichi

Classifications

• C25D1/00 Primary

  Electroforming · CPC title

• C25D1/04

  Wires; Strips; Foils · CPC title

• C25D3/66

  from melts · CPC title

• C25C7/04

  Diaphragms; Spacing elements · CPC title

• C25C3/18 Primary

  Electrolytes · CPC title