Cathode mixture and method for producing the same

Patent metadata

Field	Value
Publication number	US-11437612-B2
Application number	US-201816040216-A
Country	US
Kind code	B2
Filing date	Jul 19, 2018
Priority date	Aug 9, 2017
Publication date	Sep 6, 2022
Grant date	Sep 6, 2022

Abstract

An object of the present disclosure is to produce a cathode mixture capable of increasing the charge-discharge capacity of a sulfur battery. The present disclosure achieves the object by providing a cathode mixture used for a sulfur battery and a method for producing the same, wherein the cathode mixture is produced by a mechanical milling treatment of a raw material mixture including Li2S and MxSy wherein M is selected from P, Si, Ge, B, Al, or Sn, and x and y are integers that confer an electroneutrality with respect to S according to a kind of M; a cathode active material including a sulfur simple substance; and a conductive aid including a carbon material.

First claim

What is claimed is:

1. A method for producing a cathode mixture used for a sulfur battery, the method comprising:
forming a raw material mixture by combining as separate starting materials each of
(1) Li 2 S,
(2) P 2 S 5 and GeS 2 ,
(3) a cathode active material comprising a sulfur simple substance, and
(4) a conductive aid comprising vapor-grown carbon fiber, the raw material mixture comprised of each of the separate starting materials, and

mechanical milling the raw material mixture to produce the cathode mixture,
wherein, in the produced cathode mixture, when a diffraction intensity of a peak at 2θ=23.05°±1.00° is regarded as I A , and a diffraction intensity of a peak at 2θ=27.05°±1.00° is regarded as I B , in X-ray diffraction measurement using a CuKα ray, a value of I B is more than a value of I A ;
wherein the raw material mixture comprises the Li 2 S and the P 2 S 5 at a rate in a range of 75:25 to 90:10 in a molar ratio;
wherein an atomic ratio of the Ge to the P in the raw material mixture is 0.08 or more and 1.23 or less; and
wherein an intensity ratio of a diffraction peak of the Li 2 S (111) surface to diffraction peak of the GeS 2 (111) surface in the cathode mixture is 0.9 or more and 10.4 or less.

2. The method according to claim 1 , wherein the mechanical milling treatment is carried out by using a planetary type ball mill.

Assignees

• Toyota Motor Co Ltd

Inventors

• Nose Masafumi

Classifications

• H01M4/628

  Inhibitors, e.g. gassing inhibitors, corrosion inhibitors · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M4/625

  Carbon or graphite · CPC title

• H01M4/38

  of elements or alloys · CPC title

• H01M2004/028

  Positive electrodes · CPC title