Abstract

The present invention relates to the use of a filament comprising a core material (CM) comprising a ceramic material precursor (CMP) and the core material (CM) is coated with a layer of shell material (SM) comprising a thermoplastic polymer as a support material in a fused filament fabrication process. Further, the invention relates to three-dimensional objects and a process for the preparation thereof.

First claim

The invention claimed is:

1. A process for producing a three-dimensional object by a fused filament fabrication process comprising the steps:
i) depositing a support material into a build chamber using a layer-based additive technique to form a support structure,
ii) depositing a modeling material into the build chamber using the layer based additive technique to form the three-dimensional object, wherein the three-dimensional object comprises at least one region supported by the support structure, wherein the support material comprises a filament, said filament comprising a core material (CM) coated with a layer of shell material (SM) as a support material in a fused filament fabrication process, wherein the core material (CM) comprises the components a) to c)
a) 30 to 80% by volume, based on the total volume of the core material (CM) of at least ceramic material precursor (CMP),
b) 20 to 70% by volume, based on the total volume of the core material (CM) of at least one binder (B) comprising component b1)
b1) at least one polymer (P)
c) 0 to 20% by volume, based on the total volume of the core material (CM) of at least one additive (A),
and the shell material (SM) comprises the components d) to f)
d) 75 to 100% by volume, based on the total volume of the shell material (SM) of at least one thermoplastic polymer (TP),
e) 0 to 20% by volume, based on the total volume of the shell material (SM) of the at least one ceramic material precursor (CMP),
f) 0 to 25% by volume, based on the total weight of the shell material (SM) of the at least one additive (A), wherein the thickness of the layer of shell material is 0.05 to 0.5 mm;

wherein the polymer (P) in component (b1) is a polyoxymethylene (POM) copolymer which is prepared by polymerization of
from at least 50 mol-% of a formaldehyde source (b1a),
from 0.01 to 20 mol-% of at least one first comonomer (b1b) of formula (II)

R 1 to R 4 are each independently of one another selected from the group consisting of H, C 1 -C 4 -alkyl and halogen-substituted C 1 -C 4 -alkyl;
R 5 is selected from the group consisting of a chemical bond, a (—CR 5a R 5b —) group and a (—CR 5a R 5b O—) group, wherein
R 5a and R 5b are each independently of one another selected from the group consisting of Hand unsubstituted or at least monosubstituted C 1 -C 4 -alkyl,
wherein the substituents are selected from the group consisting of F, Cl, Br, OH and C 1 -C 4 -alkyl;
n is 0, 1, 2, or 3; and
from 0 to 20 mol-% of at least one second comonomer (b1c) selected from the group consisting of a compound of formula (III) and a compound of formula (IV)

Z is selected from the group consisting of a chemical bond, an (—O—) group and an (—O—R 6 —O—) group, wherein
R 6 is selected from the group consisting of unsubstituted C 1 -C 8 -alkylene and C 3 -C 8 -cycloalkylene.

2. The process according to claim 1 , wherein the binder (B)
i) comprises from 50 to 96% by weight of the at least one polymer (P), based on the total weight of the binder, and/or
ii) the at least one polymer (P) is a polyoxymethylene (POM).

3. The process according to claim 1 , wherein the binder
(B) in the core material (CM) further comprises components b2) and/or b3)
b2) at least one polyolefin (PO),
b3) at least one further polymer (FP), in case component b) is a polyoxymethylene (POM).

4. The process according to claim 3 , wherein the binder (B) comprises 2 to 35% by weight of component b2), based on the weight of the binder (B), and/or from 2 to 40% by weight of component b3), based on the weight of the binder (B).

5. The process according to claim 1 , wherein
i) the diameter of the filament is 1.5 to 3.5 mm, and/or
ii) the diameter of the core material is 1.5 to 3.0 mm, and/or
iii) the thickness of the layer of shell material (SM) is 0.04 to 0.5 mm, and/or
iv) the particle size of the ceramic material precursor is from 0.1 to 80 μm, and/or
v) the ceramic material precursor is selected from the group consisting of SiO 2 , CaCO 3 , CaSiO 3 , CaO, Al 2 O 3 , xAl 2 O 3 , ySiO 2 , zH 2 O, TiO 2 , NaAlSi 3 O 8 , KAlSi 3 O 8 CaAl 2 Si 2 O 8 , iron oxide (FeO, Fe 2 O 3 , Fe 3 O 4 ), BaO, and K 2 O and mixtures thereof, and/or
vi) the at least one thermoplastic polymer (TP) of the shell material (SM) is selected from the group consisting of polyoxymethylene (POM), polyolefins (PE), polyurethanes (PU), polyamides (PA), polyethers (PETH), polycarbonates (PC), polyesters (PES) and blends thereof.

6. The process according to claim 3 , wherein the further polymer (FP) is at least one further polymer (FP) selected from the group consisting of a polyether, a polyurethane, a polyepoxide, a polyamide, a vinyl aromatic polymer, a poly(vinyl ester), a poly(vinyl ether), a poly(alkyl (meth)acrylate) and copolymers thereof.

7. The process according to claim 1 , wherein the modeling material comprises a filament comprising a core material (CM) coated with a layer of shell material (SM), wherein the core material (CM) comprises the components a) to c)
a) 30 to 80% by volume, based on the total volume of the core material (CM) of a powder of at least one metal, or metal alloy (ME),
b) 20 to 70% by volume, based on the total volume of the core material (CM) of at least one binder (B) comprising component b1),
b1) at least one polymer (P),
c) 0 to 20% by volume, based on the total volume of the core material (CM) of at least one additive (A),
and the shell material (SM) comprises the components d) to f),
d) 75 to 100% by volume, based on the total volume of the shell material (SM) of at least one thermoplastic polymer (TP),
e) 0 to 20% by volume, based on the total volume of the shell material (SM) of the at least one metal, or metal alloy,
f) 0 to 25% by volume, based on the total weight of the shell material (SM) of the at least one additive (A), wherein the thickness of the layer of shell material is 0.05 to 0.5 mm.

8. The process according to claim 1 , wherein step ii) is followed by a step iii), in which the three-dimensional object obtained in step ii) is debinded to remove organic polymer.

9. The process according to claim 1 , wherein step iii) is followed by a step iv), in which the three-dimensional object obtained in step iii) is sintered to form a three-dimensional sintered object and the support structure is removed from the three-dimensional sintered object.

Assignees

• Basf Se

Inventors

• Kopping Jordan Thomas
• Hermant Marie-Claire
• Schmidt Kris
• Nestle Nikolaus
• Koehler Alexander

Classifications

• B33Y70/00

  Materials specially adapted for additive manufacturing · CPC title

• B33Y70/10

  Composites of different types of material, e.g. mixtures of ceramics and polymers or mixtures of metals and biomaterials · CPC title

• B29C64/106

  using only liquids or viscous materials, e.g. depositing a continuous bead of viscous material · CPC title