Filaments based on a coated core material

Patent metadata

Field	Value
Publication number	US-2018202076-A1
Application number	US-201615744428-A
Country	US
Kind code	A1
Filing date	Jul 7, 2016
Priority date	Jul 14, 2015
Publication date	Jul 19, 2018
Grant date	—

Abstract

The invention relates to a filament comprising a core material (CM) comprising an inorganic powder (IP) and the core material (CM) is coated with a layer of shell material (SM) comprising a thermoplastic polymer. Further, the invention relates to a process for the preparation of said filament, as well as to three-dimensional objects and a process for the preparation thereof.

First claim

1 .- 14 . (canceled)

15 . A filament comprising a core material (CM) coated with a layer of shell material (SM), wherein
the core material (CM) comprises the components a) to c) a) 30 to 80% by volume, based on the total volume of the core material (CM) of at least one inorganic powder (IP), b) 20 to 70% by volume, based on the total volume of the core material (CM) of at least one binder (B) comprising component b1) b1) at least one polymer (P) c) 0 to 20% by volume, based on the total volume of the core material (CM) of at least one additive (A), wherein the at least one polymer (P) is a polyoxymethylene (POM) homopolymer, a polyoxymethylene (POM) copolymer or polyoxymethylene (POM) terpolymer and wherein at least some of the OH-end groups of the polyoxymethylene (POM) homopolymer are capped, and the shell material (SM) comprises the components d) to f) d) 75 to 100% by volume, based on the total volume of the shell material (SM) of at least one thermoplastic polymer (TP) e) 0 to 20% by volume, based on the total volume of the shell material (SM) of the at least one inorganic powder (IP), f) 0 to 25% by volume, based on the total weight of the shell material (SM) of the at least one additive (A), wherein the thickness of the layer of shell material is 0.05 to 0.5 mm.

16 . The filament according to claim 15 , wherein the binder (B))
i) comprises from 50 to 96% by weight or the at least one polymer (P), based on the total weight of the binder.

17 . The filament according to claim 15 , wherein the binder (B) in the core material (CM) further comprises components b2) or b3)
b2) at least one polyolefin (PO), b3) at least one further polymer (FP), in case component b) is a polyoxymethylene (POM).

18 . The filament according to claim 17 , wherein the binder (13) comprises 2 to 35% by weight of component b2), based on the total weight of the binder (B), or from 2 to 40% by weight of component b3), based on the total weight of the binder (B).

19 . The filament according to claim 15 , wherein
i) the diameter of the filament is 1.5 to 3.5 mm, or ii) the diameter of the core material is 1.5 to 3.0 mm, or iii) the thickness of the layer of shell material (SM) is 0.09 to 0.3 mm, or iv) the particle size of the inorganic powder (IP) is from 0.1 to 80 μm, or v) the inorganic powder (IP) is a powder of at least one inorganic material selected from the group consisting of a metal, a metal alloy and a ceramic material, or vi) the at least one thermoplastic polymer (TP) of the shell material (SM) is selected from the group of polyoxymethylene (POM), polyolefins (PE) such as polypropylene or polyethylene, polyurethanes (PU), polyamides (PA), polyethers (PETH), polycarbonates (PC), or polyesters (PES) such as polylactic acid and blends thereof.

20 . The filament according to claim 15 , wherein the polymer (P) in component (b1) is a polyoxymethylene (POM) copolymer which is prepared by polymerization of
from at least 50 mol-% of a formaldehyde source (b1a), from 0.01 to 20 mol-% of at least one first comonomer (b1b) of the general formula (II)

wherein
R 1 to R 4 are each independently of one another selected from the group consisting of H, C 1 -C 4 -alkyl and halogen-substituted C 1 -C 4 -alkyl;
R 5 is selected from the group consisting of a chemical bond, a (—CR 5a R 5b —) group and a (—CR 5a R 5b O—) group,
wherein
R 5a and R 5b are each independently of one another selected from the group consisting of H and unsubstituted or at least monosubstituted C 1 -C 4 -alkyl,
wherein the substituents are selected from the group consisting of F, Cl, Br, OH and C 1 -C 4 -alkyl;
n is 0, 1, 2 or 3;
and

from 0 to 20 mol-% of at least one second comonomer (b1c) selected from the group consisting of a compound of formula (III) and a compound of formula (IV)

wherein
Z is selected from the group consisting of a chemical bond, an (—O—) group and an (—O—R 6 —O) group,
wherein
R 6 is selected from the group consisting of unsubstituted C 1 -C 8 -alkylene and C 3 -C 8 -cycloalkylene.

21 . The filament according to claim 17 , wherein the further polymer (FP) is at least one further polymer (FP) selected from the group consisting of a polyether, a polyurethane, a polyepoxide, a polyamide, a vinyl aromatic polymer, a poly(vinyl ester), a poly(vinyl ether), a poly(alkyl (meth)acrylate) and copolymers thereof.

22 . A process for the preparation of a filament according to claim 15 , wherein a core material (CM) is coated with a layer of a shell material (SM) by co-extrusion of the core material (CM) with the shell material (SM).

23 . A process for preparation of a three-dimensional green body, by a fused filament fabrication process, comprising at least the steps a), b), c),
a) providing the filament according to claim 15 on a spool to a noozle, b) heating the filament to a temperature (T M ), c) depositing of the heated filament obtained in step b) in a build chamber using a layer based additive technique in order to form the three dimensional green-body.

24 . The process according to claim 23 , wherein the temperature (TM) in step b) is 140 to 240° C.

25 . The process according to claim 23 , wherein step c) is followed by a step d) in which at least a part of the binder (B) or at least a part of the shell material (SM) is removed from the three-dimensional green body in order to form a three-dimensional brown body.

26 . The process according to claim 25 , wherein in step d)
i) the binder (B) or the shell material (SM) is removed by acidic treatment or ii) the binder (B) or the shell material (SM) is removed at a temperature below the melting point of the binder (B) or the shell material (SM).

27 . The process according to claim 25 , wherein step d) is followed by a step e), in which the three-dimensional brown body is sintered to form a three-dimensional sintered body.

28 . A three-dimensional green-body, prepared by the process according to claim 23 .

29 . The filament according to claim 15 , wherein
i) the diameter of the filament is 2.0 to 3.1 mm, or ii) the diameter of the core material is 1.9 to 2.7 mm, or iii) the thickness of the layer of shell material (SM) is 0.1 to 0.25 mm, or iv) the particle size of the inorganic powder (IP) is from 0.5 to 50 μm.

Assignees

• Basf Se

Inventors

• Van Der Schaaf Paul
• Inderbitzin Bruno
• Hermant Marie-Claire
• Schömer Martina

Classifications

• C04B35/581

  based on aluminium nitride · CPC title

• C04B35/057

  based on calcium oxide · CPC title

• C04B35/111

  Fine ceramics · CPC title

• C04B35/01

  based on oxide ceramics · CPC title

• D01F8/04

  from synthetic polymers · CPC title