Method for producing a copper-infiltrated valve seat ring

Patent metadata

Field	Value
Publication number	US-11098619-B2
Application number	US-201916686096-A
Country	US
Kind code	B2
Filing date	Nov 15, 2019
Priority date	Nov 16, 2018
Publication date	Aug 24, 2021
Grant date	Aug 24, 2021

Abstract

A method for producing a copper-infiltrated valve seat ring and a valve seat ring are disclosed. The method includes introducing a copper powder and a functional material powder mixture into a joint cavity, simultaneously forming the copper powder and the functional material powder mixture into a green body comprising a functional section and a copper section in the joint cavity by the mold element, and sintering the green body formed in step b) to produce the valve seat ring where the copper section liquefies during the sintering and infiltrates pores present in the functional section.

First claim

The invention claimed is:

1. A method for producing a copper-infiltrated valve seat ring,
comprising the following steps:
a) Introducing a copper-based powder and a functional material powder mixture into a joint cavity provided in a mold element of a molding device,
b) Simultaneously forming the copper-based powder introduced in step a) and the functional material powder mixture introduced in step a) into a green body comprising a functional section and a copper section in the joint cavity by the mold element, and
c) Sintering the green body formed in step b) to produce the valve seat ring, wherein the copper section liquefies during the sintering and infiltrates pores present in the functional section;
wherein while performing step a) the copper-based powder and the functional material powder mixture are essentially not mixed with one another,
wherein the functional material powder mixture introduced in step a) includes iron, between 0 and 15% by weight of each of Mo, Si, W, V, C, P, Ni, Cr, Cu, Co, N, and Mn, and production-related impurities, and
wherein 90% of the particles of the functional material powder mixture have a maximum diameter of between 25 μm and 344 μm, 20% or less of the particles of the functional material powder mixture have a maximum diameter of less than 40 μm, and 10% or less of the particles of the functional material powder mixture have a maximum diameter of larger than 300 μm.

2. The method according to claim 1 , wherein step a) includes introducing the copper-based powder into the joint cavity prior to the functional material powder mixture or vice versa.

3. The method according to claim 1 , wherein step a) includes introducing the copper-based powder and the functional material powder mixture simultaneously into the joint cavity.

4. The method according to claim 1 ,
wherein the copper-based powder introduced in step a) is pre-formed by a pre-forming device.

5. The method according to claim 1 , wherein at least one of:
the copper-based powder introduced in step a) includes production-related impurities and up to 10% by weight of alloying elements, and
5% or less of the particles of the copper powder have a maximum diameter of larger than 177 μm.

6. The method according to claim 1 , wherein after performing step b), the copper section has a height of less than 1 mm measured along the axial direction (A).

7. The method according to claim 1 , wherein after performing step b), further including arranging the copper section and the functional section next to one another along an axial direction.

8. The method according to claim 1 , wherein after performing step b), a surface that completely separates the functional section and the copper section extends in a plane perpendicular to an axial direction.

9. A valve seat ring, comprising:
a sintered green body including a copper section and a functional section;
wherein the copper section is composed of copper and infiltrates pores present in the functional section;
wherein the functional section is composed of a functional material powder mixture including iron, between 0 and 15% by weight of each of Mo, Si, W, V, C, P, Ni, Cr, Cu, Co, N, and Mn, and production-related impurities; and
wherein 90% of the particles of the functional material powder mixture have a maximum diameter of between 25 μm and 344 μm, 20% or less of the particles of the functional material powder mixture have a maximum diameter of less than 40 μm, and 10% or less of the particles of the functional material powder mixture have a maximum diameter of larger than 300 μm.

10. The valve seat ring according to claim 9 , wherein the valve seat ring has a height of less than 4 mm, measured along an axial direction.

11. A tribological system, comprising:
a valve seat ring, the valve seat ring including:
a green body including a copper section and a functional section; and
wherein the copper section is composed of copper and infiltrates pores present in the functional section;
wherein the functional section is composed of a functional material powder mixture including iron, between 0 and 15% by weight of each of Mo, Si, W, V, C, P, Ni, Cr, Cu, Co, N, and Mn, and production-related impurities, and wherein 90% of the particles of the functional material powder mixture have a maximum diameter of between 25 μm and 344 μm, 20% or less of the particles of the functional material powder mixture have a maximum diameter of less than 40 μm, and 10% or less of the particles of the functional material powder mixture have a maximum diameter of larger than 300 μm; and
wherein the copper of the copper section is composed of includes production-related impurities and up to 5% by weight of each of Fe, Mn, Sn, Zn, Al and Ni, and wherein 5% or less of the particles of the copper powder have a maximum diameter of larger than 177 μm.

12. An internal combustion engine for a motor vehicle, comprising a valve seat ring as claimed in claim 9 .

13. The method according to claim 1 , wherein step b) of simultaneously forming the copper-based powder and the functional material powder mixture includes pressing the copper powder and the functional material powder mixture into the green body.

14. The method according to claim 1 , wherein the copper-based powder introduced in step a) includes production-related impurities and between 0 and 5% by weight of each of Fe, Mn, Sn, Zn, Al and Ni.

15. The method according to claim 1 , further comprising pre-forming the copper-based powder via pressing prior to introducing the copper-based powder and the functional material powder mixture into the joint cavity.

16. The method according to claim 6 , wherein the height of the copper section is less than 0.7 mm after performing step b).

Assignees

• Mahle Int Gmbh
• Mhale Int Gmbh

Inventors

• Grueneberg Heiko
• Heckendorn Heiko
• Sutter Patrick
• Wintrich Klaus

Classifications

• B22F1/09

  Mixtures of metallic powders · CPC title

• B22F3/1035

  Liquid phase sintering · CPC title

• F01L3/02 Primary

  Selecting particular materials for valve-members or valve-seats; Valve-members or valve-seats composed of two or more materials · CPC title

• F01L2303/01

  Tools for producing, mounting or adjusting, e.g. some part of the distribution · CPC title

• B22F7/064

  using an intermediate powder layer · CPC title