Dipping bath compositions for treating reinforcing inserts

Patent metadata

Field	Value
Publication number	US-11059950-B2
Application number	US-201916515119-A
Country	US
Kind code	B2
Filing date	Jul 18, 2019
Priority date	Jul 19, 2018
Publication date	Jul 13, 2021
Grant date	Jul 13, 2021

Abstract

The present invention relates to an aqueous, solids-containing dipping bath composition for treating reinforcing inserts for rubber products comprising the following components or consisting of these components, (A) at least one blocked MDI mixture, the MDI mixture comprising MDI oligomers of formula (I), n being a whole number from 1 to 8, and MDI monomers; (B) at least one resorcinol-formaldehyde latex; and (C) possibly at least one additive, wherein the dipping bath composition is essentially free of epoxides.

First claim

The invention claimed is:

1. An aqueous, solids-containing dipping bath composition for treating reinforcing inserts for rubber products comprising the following components:
(A) at least one blocked MDI mixture,
the MDI mixture comprising MDI oligomers of formula (I), n being a whole number from 1 to 8,

and MDI monomers;
(B) at least one resorcinol-formaldehyde latex; and
(C) optionally at least one additive,
wherein the dipping bath composition is essentially free of epoxides.

2. The aqueous, solids-containing dipping bath composition according to claim 1 , wherein the proportion of the solids is 2 to 40% by weight relative to the total weight of the dipping bath composition.

3. The aqueous, solids-containing dipping bath composition according to claim 1 , wherein the bath has the following composition, the parts by weight respectively relative to the total weight of the dipping bath composition:
(A) 0.1 to 20 parts by weight,
(B) 5 to 200 parts by weight, and
(C) 0 to 20 parts by weight.

4. The aqueous, solids-containing dipping bath composition according to claim 1 , wherein the blocked MDI mixture (A) comprises MDI derivatives selected from the group consisting of MDI uretdione, adducts of MDI, and MDI oligomers with other compounds.

5. The aqueous, solids-containing dipping bath composition according to claim 4 , wherein the MDI is selected from the group consisting of 4,4′-MDI, 2,4′-MDI, 2,2′-MDI and mixtures thereof, the proportion of 2,4′-MDI and 2,2′-MDI being less than 10% by weight, relative to the MDI mixture.

6. The aqueous, solids-containing dipping bath composition according to claim 1 , wherein the MDI mixture has the following composition:
(i) 25 to 60% by weight of MDI monomers;
(ii) 40 to 75% by weight of MDI oligomers; and
(iii) 0 to 9% by weight of MDI derivatives;
the proportions of components (i) to (iii) adding up to 100% by weight.

7. The aqueous, solids-containing dipping bath composition according to claim 1 , wherein:
in the case of the at least one resorcinol-formaldehyde latex (B), the latex is selected from the group consisting of styrene-butadiene-vinylpyridine copolymer, styrene-butadiene-vinylpyridine copolymer modified with carboxylic acid, styrene-butadiene copolymer, styrene-butadiene copolymer modified with carboxylic acid, nitrile-butadiene copolymer, natural latex, chloroprene latex, and mixtures thereof.

8. The aqueous, solids-containing dipping bath composition according to claim 1 , wherein the at least one additive (C) is selected from the group consisting of surfactants, defoamers, fillers, colourants, preservatives, thickening agents, acids, lyes, multivalent alcohols, and mixtures thereof.

9. The aqueous, solids-containing dipping bath composition according to claim 1 , wherein the MDI mixture (A) is blocked with a compound which is selected from the group consisting of monophenols, lactams, oximes, enol-forming compounds, acetyl acetone, and mixtures thereof.

10. The aqueous, solids-containing dipping bath composition according to claim 1 , wherein:
the average particle diameter d 50 of the blocked MDI mixture is at most 2 μm; and/or
the particle diameter d 100 of the blocked MDI mixture is at most 6 μm; and/or
the blocked MDI mixture has a number-average molar mass M n in the range of 550 to 1,200 g/mol.

11. A method for producing an adhesive reinforcing insert which comprises at least the following steps:
a) providing at least one reinforcing insert;
b) dipping the reinforcing insert in at least one dipping bath composition according to claim 1 ;
c) drying the reinforcing insert from step b) at 100 to 240° C.; and
d) annealing the reinforcing insert from step c) at 200 to 250° C.

12. The method according to claim 11 , wherein:
the reinforcing insert is selected from the group consisting of polyamide 6, polyamide 66, polyethylene terephthalate, polyethylene naphthalate, rayon, aramide, cotton, basalt fibres, sisal, hemp, flax, coconut fibres, and mixtures thereof.

13. The method according to claim 11 , wherein:
the reinforcing insert is dipped, before step b), in an aqueous, solids-containing dipping bath composition which comprises at least one blocked MDI mixture or which comprises no other components besides the at least one blocked MDI mixture,
the MDI mixture comprising MDI oligomers of formula (I), n being a whole number from 1 to 8,

and MDI monomers.

14. A method for producing a reinforced rubber product, which comprises the following steps:
providing at least one layer of an adhesive reinforcing insert produced by the method according to claim 11 ;
(ii) embedding at least one layer of an adhesive reinforcing insert from step (i) in a rubber matrix in a pressing mould;
(iii) pressing the product from step (ii);
(iv) vulcanising the product from step (iii) at 140 to 210° C. and 5 to 110 bar for 5 to 45 minutes; and
(v) removing the reinforced rubber product from step (iv) from the pressing mould.

15. An adhesive reinforcing insert produced by the method according to claim 11 .

16. A method of producing reinforced rubber products comprising utilizing the adhesive reinforcing insert according to claim 15 .

17. A method for coating reinforcing inserts for rubber products comprising utilizing the aqueous, solids-containing dipping bath composition according to claim 1 .

Assignees

• Ems Patent Ag

Inventors

• Holzschuh Martin
• Kaplan Andreas

Classifications

• C09J11/06

  organic · CPC title

• B60C2001/0066

  Compositions of the belt layers · CPC title

• C08L61/12

  with polyhydric phenols · CPC title

• B60C2001/0083

  Compositions of the cap ply layers · CPC title

• C08G18/7664 Primary

  containing alkylene polyphenyl groups · CPC title