Three-dimensional lignin porous carbon/zinc oxide composite material and its preparation and application in the field of photocatalysis

Patent metadata

Field	Value
Publication number	US-11059031-B2
Application number	US-201716318916-A
Country	US
Kind code	B2
Filing date	Nov 16, 2017
Priority date	May 11, 2017
Publication date	Jul 13, 2021
Grant date	Jul 13, 2021

Abstract

A three-dimensional lignin porous carbon/zinc oxide composite material and its preparation and application in the field of photocatalysis are disclosed. The method includes preparing a lignin/zinc oxide precursor composite by a hydrothermal method from a zinc salt, a weak alkali salt and an industrial lignin, and preparing a three-dimensional lignin porous carbon/zinc oxide composite material by high temperature calcination of the lignin/zinc oxide precursor composite. The composite material has a regular three-dimensional pore structure, with zinc oxide nanoparticles uniformly embedded among the three-dimensional lignin porous carbon nanosheets. Application of the composite material to the field of photocatalysis, especially as a photocatalyst for photocatalytic degradation of organic dye pollutants, can significantly improve the degradation efficiency and rate, and has potential application value in the field of photocatalytic degradation of organic pollutants.

First claim

The invention claimed is:

1. A method for preparing a three-dimensional lignin porous carbon/zinc oxide composite material, comprising (1) preparing a lignin/zinc oxide precursor composite by a hydrothermal method from a zinc salt, a weak alkali salt and an industrial lignin, and (2) preparing a three-dimensional lignin porous carbon/zinc oxide composite material by high temperature calcination of the lignin/zinc oxide precursor composite;
wherein step (1) comprises:
(1.1) adding a weak alkali salt solution to a zinc salt solution to produce a zinc oxide precursor solution;
(1.2) adding industrial lignin to the zinc oxide precursor solution, stirring uniformly, and keeping the temperature at 70° C. to 150° C. for 1-8 hours to produce a lignin/zinc oxide precursor composite.

2. The method for preparing the three-dimensional lignin porous carbon/zinc oxide composite material according to claim 1 ,
wherein the amount of each reactant in step (1) is as follows in parts by weight:
10 parts of industrial lignin; 5-30 parts of zinc salt; and 5-30 parts of weak alkali salt.

3. The method for preparing the three-dimensional lignin porous carbon/zinc oxide composite material according to claim 2 , wherein the mass concentration of the zinc salt solution is from 20% to 40%; and the mass concentration of the weak alkali salt solution is from 20% to 40%.

4. The method for preparing the three-dimensional lignin porous carbon/zinc oxide composite material according to claim 2 , wherein after adding the industrial lignin to the zinc oxide precursor solution, the solution is stirred for 10-30 min to become uniform; and keeping the temperature is achieved by placing the system in a hydrothermal reactor.

5. The method for preparing the three-dimensional lignin porous carbon/zinc oxide composite material according to claim 1 , wherein the industrial lignin is at least one of wood pulp alkali lignin, bamboo pulp alkali lignin, wheat straw pulp alkali lignin, reed pulp alkali lignin, bagasse pulp alkali lignin, Chinese alpine rush pulp alkali lignin or biorefinery enzymatic lignin;
the zinc salt is at least one of zinc oxalate, zinc acetate, zinc nitrate, zinc chloride, zinc carbonate or zinc sulfate; and
the weak alkali salt is at least one of sodium oxalate, sodium carbonate or sodium bicarbonate.

6. The method for preparing the three-dimensional lignin porous carbon/zinc oxide composite material according to claim 1 , wherein the zinc salt is at least one of zinc oxalate, zinc nitrate or zinc acetate; and the weak alkali salt is sodium bicarbonate.

7. A three-dimensional lignin porous carbon/zinc oxide composite material, obtained by the preparation method according to claim 1 .

8. A photocatalyst comprising the three-dimensional lignin porous carbon/zinc oxide composite material according to claim 7 .

9. A method for photocatalytic degradation of organic dye pollutants, comprising treating the organic dye pollutants with the photocatalyst according to claim 8 .

10. The method for preparing the three-dimensional lignin porous carbon/zinc oxide composite material according to claim 1 , wherein step (2) comprises: separating and drying the lignin/zinc oxide precursor composite, grinding it into powder, and calcining at 500° C. to 750° C. for 1.5-3 h in an inert gas atmosphere to produce a three-dimensional lignin porous carbon/zinc oxide composite material.

11. The method for preparing the three-dimensional lignin porous carbon/zinc oxide composite material according to claim 10 , wherein the separating and drying is carried out by suction filtration of the lignin/zinc oxide precursor composite, and then drying the filter cake.

Assignees

• Univ South China Tech

Inventors

• Yang Dongjie
• Qian Yong
• Qiu Xueqing
• Lou Hongming
• Liu Weifeng
• Ouyang Xinping
• Fang Zhiqiang
• Pang Yuxia
• Yi Conghua

Classifications

• B01J23/06 Primary

  of zinc, cadmium or mercury · CPC title

• C02F1/30

  by irradiation · CPC title

• C02F2101/308

  Dyes; Colorants; Fluorescent agents · CPC title

• B01J37/084

  Decomposition of carbon-containing compounds into carbon · CPC title

• C02F2101/38

  containing nitrogen · CPC title