Two-dimensional clay based composite phosphorus removing agent and preparation method and application thereof

Patent metadata

Field	Value
Publication number	US-11053128-B2
Application number	US-201916726812-A
Country	US
Kind code	B2
Filing date	Dec 24, 2019
Priority date	Jun 6, 2019
Publication date	Jul 6, 2021
Grant date	Jul 6, 2021

Abstract

The present invention belongs to the field of material preparation, and particularly relates to a two-dimensional clay based composite phosphorus removing agent and a preparation method. The two-dimensional clay based composite phosphorus removing agent provided by the present invention takes two-dimensional clay, hydroxide (such as lanthanum hydroxide, calcium hydroxide, magnesium hydroxide and aluminum hydroxide) and urea as raw materials, and the composite phosphorus removing agent with high property is prepared by a roasting method. Through a combined physical and chemical method, phosphorus in the phosphorus-containing wastewater is effectively removed by the synergic interaction between components of the composite phosphorus removing agent. The invention overcomes the defects of large consumption and secondary pollution easily caused by using metal hydroxides, metal oxides and metal salts separately as chemical phosphorus removing agents, and simultaneously expands the application fields of the two-dimensional clay.

First claim

What is claimed is:

1. A two-dimensional clay based composite phosphorus removing agent, comprising:
two-dimensional clay; and
oxide of M metal composited on a surface of the two-dimensional clay in situ;
wherein the M metal is a metal capable of forming insoluble precipitate with phosphate, and a content of the oxide of the M metal is 15-50%.

2. The two-dimensional clay based composite phosphorus removing agent according to claim 1 , wherein the two-dimensional clay is at least one of kaolinite, montmorillonite and rectorite.

3. The two-dimensional clay based composite phosphorus removing agent according to claim 1 , wherein the M metal is at least one of calcium, magnesium, lanthanum and aluminum.

4. A preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 1 , wherein the two-dimensional clay based composite phosphorus removing agent is obtained by roasting mixed raw materials comprising the two-dimensional clay, hydroxide of the M metal and urea.

5. The preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 4 , wherein the hydroxide of the M metal is at least one of calcium hydroxide, magnesium hydroxide, lanthanum hydroxide and aluminum hydroxide.

6. The preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 4 , wherein a weight ratio of the two-dimensional clay powder to the hydroxide of the M metal is 1:0.2-3.

7. The preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 6 , wherein the weight ratio of the two-dimensional clay powder to the hydroxide of the M metal is 1:1-3.

8. The preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 4 , wherein a weight ratio of a mixture of the two-dimensional clay and the hydroxide of the M metal to the urea is 1:2.5-20.

9. The preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 8 , wherein the weight ratio of a mixture of the two-dimensional clay and the hydroxide of the M metal to the urea is 1:5-20.

10. The preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 4 , wherein a roasting process is performed under an oxygen-containing atmosphere.

11. The preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 4 , wherein roasting temperature of the roasting process is not lower than temperature at which the hydroxide of the M metal is converted into corresponding oxide.

12. The preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 11 , wherein the roasting temperature is 400-600° C., and roasting time is 1-5 h.

13. A preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 2 , wherein the two-dimensional clay based composite phosphorus removing agent is obtained by roasting mixed raw materials comprising the two-dimensional clay, hydroxide of the M metal and urea.

14. A preparation method of the two-dimensional clay based composite phosphorus removing agent according to claim 3 , wherein the two-dimensional clay based composite phosphorus removing agent is obtained by roasting mixed raw materials comprising the two-dimensional clay, hydroxide of the M metal and urea.

15. A method for adsorption of phosphorus-containing wastewater, comprising using the two-dimensional clay based composite phosphorus removing agent according to claim 1 .

16. A method for adsorption of phosphorus-containing wastewater, comprising using the two-dimensional clay based composite phosphorus removing agent prepared according to the preparation method of claim 4 .

Assignees

• Univ Central South

Inventors

• Yang Huaming
• Chen Hongyun
• Ouyang Jing
• Fu Liangjie
• Zhang Yi
• Liu Sainan

Classifications

• C02F1/281

  using inorganic sorbents · CPC title

• B01J20/3078

  Thermal treatment, e.g. calcining or pyrolizing · CPC title

• B01J20/16

  Alumino-silicates (B01J20/12 takes precedence) · CPC title

• C01P2004/20

  extending in two dimensions, e.g. plate-like · CPC title

• C02F2101/105

  Phosphorus compounds · CPC title