PCC with reduced portlandite content

Patent metadata

Field	Value
Publication number	US-11021374-B2
Application number	US-201916365278-A
Country	US
Kind code	B2
Filing date	Mar 26, 2019
Priority date	Oct 24, 2014
Publication date	Jun 1, 2021
Grant date	Jun 1, 2021

Abstract

The present invention is directed to a process for producing an aqueous suspension of precipitated calcium carbonate, wherein a milk of lime is prepared by mixing water, a calcium oxide containing material, and a precipitation enhancer, and subsequently, the milk of lime is carbonated to form an aqueous suspension of precipitated calcium carbonate.

First claim

The invention claimed is:

1. An aqueous suspension of precipitated calcium carbonate having a low portlandite content, obtained by a process comprising the steps of:
i) providing a calcium oxide containing material having a calcium oxide content of at least 90 wt.-%,
ii) providing a water-soluble calcium salt as a precipitation enhancer wherein the water-soluble calcium salt is an anhydrous salt or hydrate salt,
iii) preparing a milk of lime by mixing, in any order, water, the calcium oxide containing material of step i), and the precipitation enhancer of step ii), wherein the precipitation enhancer is included in an amount from 0.01 to 25 wt.-%, based on the total weight of the calcium oxide containing material, and
iv) carbonating the milk of lime obtained from step iii) until an aqueous suspension of precipitated calcium carbonate having a portlandite content of less than 1 wt.-%, based on the total dry weight of the precipitated calcium carbonate, is obtained, wherein the obtained aqueous suspension of precipitated calcium carbonate has a solids content of from 10 to 50 wt.-%, based on the total weight of the suspension.

2. The aqueous suspension of claim 1 , wherein step iii) comprises the steps of:
a1) mixing the calcium oxide containing material of step i) with water, and
a2) adding the precipitation enhancer of step ii) to the mixture of step a1); or
b1) mixing the precipitation enhancer of step ii) with water, and
b2) adding the calcium oxide containing material of step i) to the mixture of step b1).

3. The aqueous suspension of claim 1 , wherein the obtained precipitated calcium carbonate has a portlandite content of less than 0.1 wt.-%, based on the total dry weight of the precipitated calcium carbonate.

4. The aqueous suspension of claim 1 , wherein the milk of lime is screened after step iii) and before step iv), with a screen having a sieve size from 100 to 300 p.m.

5. The aqueous suspension of claim 1 , wherein the obtained suspension of precipitated calcium carbonate has a solids content of at least 5 wt.-%, based on the total weight of the suspension.

6. The aqueous suspension of claim 1 , wherein the water-soluble calcium salt is selected from the group consisting of calcium nitrate, calcium sulfate, calcium acetate, calcium benzoate, calcium bicarbonate, calcium bromate, calcium bromide, calcium chlorate, calcium chloride, calcium iodite, calcium nitrite, calcium perchlorate, calcium permanganate, hydrates thereof, and any mixture thereof.

7. The aqueous suspension of claim 1 , wherein the water-soluble calcium salt is selected from the group consisting of calcium nitrate, calcium sulfate, calcium acetate, calcium benzoate, calcium bicarbonate, calcium bromate, calcium bromide, calcium chlorate, calcium chloride, calcium iodite, calcium nitrite, calcium perchlorate, calcium permanganate, calcium nitrate tetrahydrate, calcium chloride dihydrate, and any mixture thereof.

8. The aqueous suspension of claim 1 , wherein the water-soluble calcium salt is selected from the group consisting of calcium nitrate, calcium nitrate tetra hydrate, calcium chloride, calcium chloride dihydrate, and any mixture thereof.

9. The aqueous suspension of claim 1 , wherein the precipitation enhancer of step ii) is added in an amount from 0.1 to 20 wt.-%, based on the total weight of the calcium oxide containing material.

10. The aqueous suspension of claim 1 , wherein the precipitation enhancer of step ii) is added in an amount from 1 to 15 wt.-%, based on the total weight of the calcium oxide containing material.

11. The aqueous suspension of claim 1 , wherein the precipitation enhancer of step ii) is added in an amount from 5 to 10 wt.-%, based on the total weight of the calcium oxide containing material.

12. The aqueous suspension of claim 1 , wherein a slaking additive is added before, during or after step iii).

13. The aqueous suspension of claim 12 , wherein the slaking additive is added in an amount from 0.01 to 2 wt.-%, based on the total amount of calcium oxide containing material.

14. An aqueous suspension of precipitated calcium carbonate having a low portlandite content, obtained by a process comprising the steps of:
i) providing a calcium oxide containing material having a calcium oxide content of at least 90 wt.-%,
ii) providing a precipitation enhancer comprising calcium carbonate nanoparticles, the calcium carbonate nanoparticles having a number based median particle size d 50 of from 30 to 70 nm, and a portlandite content of less than 1 wt.-%, based on the total dry weight of the calcium carbonate nanoparticles,
iii) preparing a milk of lime by mixing, in any order, water, the calcium oxide containing material of step i), and the precipitation enhancer of step ii), wherein the precipitation enhancer is included in an amount from 0.01 to 25 wt.-%, based on the total weight of the calcium oxide containing material, and
iv) carbonating the milk of lime obtained from step iii) until an aqueous suspension of precipitated calcium carbonate having a clustered scalenohedral crystal structure and a portlandite content of less than 1 wt.-%, based on the total dry weight of the precipitated calcium carbonate, and a solids content of from 10 to 50 wt.-%, based on the total weight of the suspension, is obtained.

15. The aqueous suspension of claim 14 , wherein the precipitation enhancer further comprises a water-soluble calcium salt, and wherein the calcium carbonate nanoparticles and the water-soluble calcium salt are in a mass ratio of from 1:10 to 10:1.

16. The aqueous suspension of claim 15 , wherein the water-soluble calcium salt is an anhydrous salt or hydrate salt.

17. An aqueous suspension of precipitated calcium carbonate having a low portlandite content, obtained by a process comprising the steps of:
i) a providing a calcium oxide containing material having a calcium oxide content of at least 90 wt.-%,
ii) providing a water-soluble calcium salt as a precipitation enhancer wherein the water-soluble calcium salt is an anhydrous salt or hydrate salt,
iii) preparing a milk of lime by mixing, in any order, water, the calcium oxide containing material of step i), and the precipitation enhancer of step ii), wherein the precipitation enhancer is included in an amount from 0.01 to 25 wt.-%, based on the total weight of the calcium oxide containing material, and
iv) carbonating the milk of lime obtained from step iii) until an aqueous suspension of precipitated calcium carbonate having a portlandite content of less than 1 wt.-%, based on the total dry weight of the precipitated calcium carbonate, is obtained,
wherein a slaking additive is added before, during or after step iii), the slaking additive being selected from the group consisting of an organic acid, an organic acid salt, a sugar alcohol, a monosaccharide, a disaccharide, a polysaccharide, a gluconate, a phosphonate, a lignosulfonate, and any mixture thereof.

Assignees

• Omya Int Ag

Inventors

• Gerard Daniel E
• Gane Patrick A C

Classifications

• C01P2002/70

  defined by measured X-ray, neutron or electron diffraction data · CPC title

• C01P2004/61

  Micrometer sized, i.e. from 1-100 micrometer · CPC title

• D21H19/385

  Oxides, hydroxides or carbonates · CPC title

• C01P2004/51

  Particles with a specific particle size distribution · CPC title

• C01P2006/12

  Surface area · CPC title