Control of polymer network structures via nanogels

Patent metadata

Field	Value
Publication number	US-10968300-B2
Application number	US-201716311121-A
Country	US
Kind code	B2
Filing date	Jun 23, 2017
Priority date	Jun 23, 2016
Publication date	Apr 6, 2021
Grant date	Apr 6, 2021

Abstract

A method of increasing a polymerization reaction rate of a base monomer composition that has slow free-radical polymerization kinetics. The method comprises combining an effective amount of a nanogel to the base monomer composition to form a monomer-nanogel mixture having a polymerization reaction rate that is greater than the polymerization reaction rate of the base monomer composition when subjected to an identical free-radical polymerization reaction conducted under identical conditions. The base monomer composition comprises one or more slow-kinetic monomers with slow free radical polymerization kinetics in which <25% of the double bonds are converted within the first 10 mintes of said reaction. The nanogel is soluble in the base monomer composition. The nanogel is derived from a nanogel-forming monomer mixture that comprises: at least one monovinyl monomer; at least one divinyl monomer; a chain transfer agent; and an initiator.

First claim

What is claimed is:

1. A method of increasing a polymerization reaction rate of a base monomer composition, the method comprising combining an effective amount of a nanogel with the base monomer composition to form a monomer-nanogel mixture;
wherein the base monomer composition comprises a monomer selected from the group consisting of methyl methacrylate (MMA), n-butyl acrylate, isobornyl acrylate, and combinations thereof; and
wherein the nanogel is soluble in the base monomer composition and wherein the nanogel is derived from a nanogel-forming monomer mixture that comprises:
at least one monovinyl monomer;
at least one divinyl monomer;
a chain transfer agent; and
an initiator.

2. The method of claim 1 , wherein the nanogel has an effective diameter in a range of about 1.5 nm to about 50 nm.

3. The method of claim 1 , wherein the nanogel has a molecular weight in a range of about 5 kDa to about 200 kDa.

4. The method of claim 1 , wherein the effective amount of a nanogel corresponds to a nanogel loading of at least 1 weight %, based on the weight of the monomer-nanogel mixture.

5. The method of claim 1 , wherein the free-radical polymerization reaction is photo-initiated or thermal-initiated.

6. The method of claim 1 , wherein the free-radical polymerization reaction is photo-initiated.

7. The method of claim 1 , wherein nanogel is selected from the group consisting of a non-reactive nanogel, a reactive nanogel, partially reactive nanogel, and combinations thereof.

8. The method of claim 7 , wherein nanogel is a non-reactive nanogel.

9. The method of claim 8 , wherein the non-reactive nanogel is at a nanogel loading not exceeding about 50 wt %, based on the weight of the monomer-nanogel mixture.

10. The method of claim 8 , wherein the non-reactive nanogel is at a nanogel loading in a range of about 5 wt % to about 25 wt %, based on the weight of the monomer-nanogel mixture.

11. The method of claim 8 , wherein the non-reactive nanogel is at a nanogel loading in a range of about 50 wt % to about 75 wt %, based on the weight of the monomer-nanogel mixture.

12. The method of claim 7 , wherein nanogel is a reactive nanogel.

13. The method of claim 12 , wherein the reactive nanogel is at a nanogel loading not exceeding 25 wt %, based on the weight of the monomer-nanogel mixture.

14. The method of claim 12 , wherein the reactive nanogel is at a nanogel loading in a range of about 1 wt % to about 10 wt %, based on the weight of the monomer-nanogel mixture.

15. The method of claim 12 , wherein the reactive nanogel is at a nanogel loading in a range of about 25 wt % to about 50 wt %, based on the weight of the monomer-nanogel mixture.

16. The method of claim 7 , wherein nanogel is a partially reactive nanogel.

17. The method of claim 12 , wherein the reactive nanogel is selected from the group consisting of thiol-functionalized nanogels.

18. The method of claim 1 , wherein the nanogel has an effective diameter(s) in a range selected from the group consisting of about 1 nm to about 200 nm, about 1 nm to about 100 nm, and about 1 nm to about 50 nm.

19. The method of claim 1 , wherein the chain transfer agent is selected from the group consisting of monofunctional thiols, difunctional thiols, trifunctional thiols, tetrafunctional thiols, pentafunctional thiols, hexafunctional thiols, octafunctional thiols, and bis(borondifluorodimethylglyoximate) cobaltate (II).

20. The method of claim 1 , wherein said chain transfer agent is selected from the group consisting of propyl mercaptan, butyl mercaptan, hexyl mercaptan, octyl mercaptan, dodecanethiol, thioglycolic acid, methylbenzenethiol, dodecanethiol, mercaptopropionic acid, 2-ethyl hexyl thioglycolate, octylthioglycolate, mercaptoethanol, mercaptoundecanoic acid, thiolactic acid, thiobutyric acid, trimethylol propane tris(3-mercaptopropionate), pentaerythritol tetra(3-mercaptopropionate), pentaerythritol tetrathioglycolate, pentaerythritol tetrathiolactate, pentaerythritol tetrathiobutyrate, dipentaerythritol hexa(3-mercaptopropionate), di pentaerythritol hexathioglycolate, tripentaerythritol octa(3-mercaptopropionate), and tripentaerythritol octathioglycolate.

21. A monomer-nanogel mixture according to claim 1 .

22. A method for preparing a polymer, the method comprising polymerizing the monomer-nanogel mixture according to claim 1 .

23. A polymer derived from the monomer-nanogel mixture according to claim 1 .

Assignees

• Univ Colorado Regents

Inventors

• Stansbury Jeffrey W
• Nair Devatha P
• Lewis Steven H

Classifications

• C08F2/48

  by ultraviolet or visible light · CPC title

• C08F220/1811

  C10or C11-(Meth)acrylate, e.g. isodecyl (meth)acrylate, isobornyl (meth)acrylate or 2-naphthyl (meth)acrylate · CPC title

• C08F220/1804

  C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate · CPC title

• C08F2/04

  Polymerisation in solution (C08F2/32 takes precedence) · CPC title

• C08F220/14 Primary

  Methyl esters {, e.g. methyl (meth)acrylate} · CPC title