Cemented carbide, cutting tool containing the same, and method of manufacturing cemented carbide

Patent metadata

Field	Value
Publication number	US-10961609-B2
Application number	US-201816341795-A
Country	US
Kind code	B2
Filing date	Apr 16, 2018
Priority date	Apr 19, 2017
Publication date	Mar 30, 2021
Grant date	Mar 30, 2021

Abstract

Cemented carbide contains first hard-phase particles containing WC, second hard-phase particles which contain carbonitride containing at least Ti and Nb, and a metallic binder phase containing an iron-group element. The second hard-phase particle includes a granular core portion and a peripheral portion which covers at least a part of the core portion. The core portion contains composite carbonitride expressed as Ti1-X-YNbXWYC1-ZNZ, where Y is not smaller than 0 and not greater than 0.05 and Z is not smaller than 0.3 and not greater than 0.6. The peripheral portion is different in composition from the core portion.

First claim

The invention claimed is:

1. Cemented carbide comprising:
first hard-phase particles containing WC;
second hard-phase particles which contain carbonitride containing at least Ti and Nb; and
a metallic binder phase containing an iron-group element,
the second hard-phase particle including a granular core portion and a peripheral portion which covers at least a part of the core portion,
the core portion containing composite carbonitride expressed as Ti 1-X-Y Nb X W Y C 1-Z N Z , where Y is not smaller than 0 and not greater than 0.05 and Z is not smaller than 0.3 and not greater than 0.6, and
the peripheral portion being different in composition from the core portion,
wherein the peripheral portion is composed to be higher in content of W than the core portion.

2. The cemented carbide according to claim 1 , wherein
X is not smaller than 0.1 and not greater than 0.6.

3. The cemented carbide according to claim 1 , wherein
X is not smaller than 0.1 and not greater than 0.2.

4. The cemented carbide according to claim 1 , wherein
X is not smaller than 0.4 and not greater than 0.6.

5. The cemented carbide according to claim 1 , wherein
in the core portion, a total amount of V, Cr, and Mo occupied in a total amount of Ti, Nb, W, V, Cr, and Mo is smaller than 2 atomic %.

6. The cemented carbide according to claim 1 , wherein
the core portion has a particle size at 50% in a number-based cumulative distribution not greater than 1.5 μm.

7. The cemented carbide according to claim 1 , wherein
a volume ratio of the core portion in the cemented carbide is not lower than 2 volume % and not higher than 20 volume %.

8. A cutting tool comprising the cemented carbide according to claim 1 .

9. The cutting tool according to claim 8 , the cutting tool comprising:
a substrate composed of the cemented carbide; and
a coating film which covers the substrate.

10. A method of manufacturing cemented carbide according to claim 1 , the method comprising:
a first step of obtaining powders of composite carbonitride expressed as Ti 1-X-Y Nb X W Y C 1-Z N Z ;
a second step of obtaining mixed powders by mixing the powders of the composite carbonitride, WC powders, and powders of an iron-group element;
a third step of obtaining a formed material by pressing the mixed powders; and
a fourth step of obtaining a sintered material by sintering the formed material,
Y being not smaller than 0 and not greater than 0.05,
Z being not smaller than 0.3 and not greater than 0.6,
the first step including
a first operation of obtaining third powders by mixing first powders containing two elements of Ti and Nb or three elements of Ti, Nb, and W and second powders containing at least graphite,
a second operation of obtaining a granulated material by granulating the third powders,
a third operation of obtaining a powder precursor composed of the composite carbonitride by subjecting the granulated material to heat treatment at a temperature not lower than 1800° C. in an atmosphere containing nitrogen gas, and
a fourth operation of obtaining the powders of the composite carbonitride by breaking the powder precursor.

Assignees

• Sumitomo Electric Industries

Inventors

• Michiuchi Masato
• FUKAE Kosuke

Classifications

• B22F1/16

  Metallic particles coated with a non-metal (coated with lubricating or binding agents or with organic material B22F1/10) · CPC title

• C22C1/051

  Making hard metals based on borides, carbides, nitrides, oxides or silicides; Preparation of the powder mixture used as the starting material therefor · CPC title

• C22C1/05

  Mixtures of metal powder with non-metallic powder (C22C1/08 takes precedence) · CPC title

• B22F2998/10

  Processes characterised by the sequence of their steps · CPC title

• B22F2005/001

  Cutting tools, earth boring or grinding tool other than table ware · CPC title