Method of producing die, die, and interior component of vehicle

Patent metadata

Field	Value
Publication number	US-10954601-B2
Application number	US-201715465025-A
Country	US
Kind code	B2
Filing date	Mar 21, 2017
Priority date	Apr 8, 2016
Publication date	Mar 23, 2021
Grant date	Mar 23, 2021

Abstract

A method of producing a die for forming an interior component of a vehicle includes: setting a temperature of a plating bath in a range from 25 to 40° C.; immersing at least a forming surface on a base for the die in the plating bath; and feeding a current to the base with a current density in a range from 20 to 80 A/dm2 until a metal layer is formed on the forming surface.

First claim

The invention claimed is:

1. A die for forming an interior component of a vehicle, the die comprising:
a base portion;
a forming surface on the base portion for forming a pattern on a surface of the interior component,
the forming surface including:
first recesses for forming an emboss pattern on the surface of the interior component;
second recesses smaller than the first recesses, wherein the second recesses are recessed from surfaces of the first recesses; and
third recesses smaller than the second recesses, wherein the third recesses are recessed from surfaces of the second recesses,
a metal layer that includes grains, wherein the grains have a mean grain size of 5 μm or smaller,
the metal layer covering the forming surface and including protrusions on a surface of the metal layer, wherein each of the protrusions is defined by a corresponding one of the grains, wherein
the protrusions are smaller than the third recesses,
each of the protrusions has a base dimension that is less than dimensions of openings of the third recesses,
the first recess, the second recesses, and the third recesses are formed over an entire area of the forming surface,
a plurality of the second recesses are located within each of the first recesses,
a plurality of the third recesses are located within each of the second recesses, and
a plurality of the protrusions are disposed in each of the third recesses wherein the individual metal grains cooperate to form the third recesses.

2. The die according to claim 1 , wherein the plurality of the protrusions are coupled to one another.

3. The die according to claim 1 , wherein the first recesses are separated from each other.

4. The die according to claim 1 , wherein the second recesses are separated from each other.

5. The die according to claim 3 , wherein
some of the second recesses are located-between the first recesses.

6. The die according to claim 4 , wherein
some of the third recesses are located between the second recesses.

7. A method of producing a die according to claim 1 for forming an interior component of a vehicle, the method comprising:
setting a temperature of a plating bath in a range from 25 to 40° C.;
immersing at least a forming surface on a base for the die in a plating bath; and
feeding a current to the forming surface with a current density in a range from 20 to 80 A/dm 2 until a metal layer is formed on the forming surface.

8. The method according to claim 7 , further comprising etching a base surface of the base before immersing the forming surface in the plating bath, wherein the base surface is a base for the forming surface.

9. The method according to claim 8 , wherein the etching uses an electroetching.

10. The method according to claim 7 , further comprising sandblasting the base surface before immersing the forming surface in the plating bath.

11. The method according to claim 9 , wherein
the etching includes:
immersing at least the base surface in the plating bath;
connecting the base surface in the plating bath to a positive terminal of a power source; and
connecting an electrode in the plating bath to a negative terminal of the power source, and
the feeding the current to the forming surface includes:
connecting the forming surface in the plating bath to the negative terminal of the power source; and
connecting the electrode in the plating bath to the positive terminal of the power source.

12. The method according to claim 11 , further comprising:
applying an acid-resistant material to the base surface in a pattern corresponding to a pattern to be formed on a surface of the interior component of the vehicle before immersing the base surface in the plating bath; and
immersing at least the base surface in an acid solution before immersing the base surface in the plating bath.

Assignees

• Toyota Boshoku Kk

Inventors

• Higuchi yasuhito

Classifications

• C25F3/06 Primary

  of iron or steel · CPC title

• B60R13/0243

  Doors · CPC title

• C23F1/40

  for etching other metallic material · CPC title

• C25D5/36 Primary

  of iron or steel · CPC title

• C25D3/08

  Deposition of black chromium {, e.g. hexavalent chromium, CrVI} · CPC title