Water-soluble polyvinyl alcohol blend film, related methods, and related articles

Patent metadata

Field	Value
Publication number	US-10913832-B2
Application number	US-201916679600-A
Country	US
Kind code	B2
Filing date	Nov 11, 2019
Priority date	Oct 13, 2014
Publication date	Feb 9, 2021
Grant date	Feb 9, 2021

Abstract

Disclosed herein are water-soluble films including a polyvinyl alcohol (PVOH) resin blend and optionally one or more additional components such as plasticizers, fillers, surfactants, and other additives. Also disclosed herein are articles including the water-soluble film and containing a composition such as a household care composition. The PVOH resin blend includes a PVOH copolymer including one or more types of anionic monomer units such as a PVOH terpolymer and a PVOH polymer such as a partially or completely hydrolyzed PVOH homopolymer. When the PVOH copolymer and PVOH polymer are blended in particular proportions and/or selected with regard to various criteria related to the 4% solution viscosity of one or both of the PVOH polymer(s) and PVOH copolymer(s), the resulting water-soluble film formed from the PVOH resin blend exhibits substantially improved aqueous dissolution properties.

First claim

What is claimed:

1. A method of forming an article, wherein the method comprises the steps of:
providing a water-soluble film, wherein the film defines an interior pouch container volume and comprises:
a polyvinyl alcohol (PVOH) resin blend comprising: a first PVOH copolymer comprising an anionic monomer unit, the first PVOH copolymer having a first 4% solution viscosity at 20° C. (μ 1 ); and a second PVOH polymer consisting essentially of vinyl alcohol monomer units and optionally vinyl acetate monomer units, the second PVOH polymer having a second 4% solution viscosity at 20° C. (μ 2 );
wherein:
(A) an absolute viscosity difference |μ 2 −μ 1 | for the first PVOH copolymer and the second PVOH polymer is in a range of 0 cP to about 10 cP, and the first PVOH copolymer is present in an amount in a range of about 30 wt. % to about 90 wt. % of total PVOH polymers and PVOH copolymers in the film; or
(B) an absolute viscosity difference |μ 2 −μ 1 | for the first PVOH copolymer and the second PVOH polymer is in a range of 0 cP to about 10 cP, and the anionic monomer unit is present in the film in an amount in a range of about 1.0 mol. % to about 4.2 mol. % of total PVOH polymers and PVOH copolymers in the film;

filling the container volume with a composition, wherein:
the composition is selected from the group consisting of (b1) a household care composition proximal to the film, wherein the first PVOH copolymer is present in an amount of at least 65 wt. % of total PVOH polymers and PVOH copolymers in the film, (b2) a composition other than a household care composition proximal to the film, and (b3) a household care composition proximal to the film, wherein the first PVOH copolymer is present in an amount of less than 65 wt. % of total PVOH polymers and PVOH copolymers in the film, and
the household care composition is selected from the group consisting of liquid detergent compositions, hard surface cleaning compositions, laundry detergent gels, bleach and laundry additives, fabric enhancer compositions, shampoos, body washes, and combinations thereof; and

sealing the film to form a sealed compartment, wherein the sealed compartment contains the composition.

2. The method of claim 1 , wherein the composition is (b1) the household care composition proximal to the film, wherein the first PVOH copolymer is present in an amount of at least 65 wt. % of total PVOH polymers and PVOH copolymers in the film.

3. The method of claim 1 , wherein the composition is (b2) the composition other than a household care composition proximal to the film.

4. The method of claim 1 , wherein the composition is (b3) the household care composition proximal to the film, wherein the first PVOH copolymer is present in an amount of less than 65 wt. % of total PVOH polymers and PVOH copolymers in the film.

5. The method of claim 1 , wherein:
(A) the absolute viscosity difference |μ 2 −μ 1 | for the first PVOH copolymer and the second PVOH polymer is in a range of 0 cP to about 10 cP, and the first PVOH copolymer is present in an amount in a range of about 30 wt. % to about 90 wt. % of total PVOH polymers and PVOH copolymers in the film.

6. The method of claim 1 , wherein:
(B) the absolute viscosity difference |μ 2 −μ 1 | for the first PVOH copolymer and the second PVOH polymer is in a range of 0 cP to about 10 cP, and the anionic monomer unit is present in the film in an amount in a range of about 1.0 mol. % to about 4.2 mol. % of total PVOH polymers and PVOH copolymers in the film.

7. The method of claim 1 , wherein the second PVOH polymer consists of vinyl alcohol monomer units and optionally vinyl acetate monomer units.

8. The method of claim 1 , wherein the second PVOH polymer is present in an amount in a range of about 10 wt. % to about 70 wt. % of total PVOH polymers and PVOH copolymers in the film.

9. The method of claim 1 , wherein the anionic monomer unit is present in the film in an amount in a range of about 1.0 mol. % to about 4.2 mol. % of total PVOH polymers and PVOH copolymers in the film.

10. The method of claim 1 , wherein the anionic monomer is selected from the group consisting of vinyl acetic acid, maleic acid, monoalkyl maleate, dialkyl maleate, monomethyl maleate, dimethyl maleate, maleic anyhydride, fumaric acid, monoalkyl fumarate, dialkyl fumarate, monomethyl fumarate, dimethyl fumarate, fumaric anyhydride, itaconic acid, monomethyl itaconate, dimethyl itaconate, itaconic anhydride, vinyl sulfonic acid, allyl sulfonic acid, ethylene sulfonic acid, 2-acrylamido-1-methylpropanesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, 2-methylacrylamido-2-methylpropanesulfonic acid, 2-sufoethyl acrylate, alkali metal salts of the foregoing, esters of the foregoing, and combinations thereof.

11. The method of claim 1 , wherein the anionic monomer is selected from the group consisting of acrylamido methylpropanesulfonic acids, alkali metal salts thereof, and combinations thereof.

12. The method of claim 1 , wherein the anionic monomer is selected from the group consisting of monomethyl maleate, alkali metal salts thereof, and combinations thereof.

13. The method of claim 1 , wherein the anionic monomer unit is present in first PVOH copolymer in an amount in a range of about 2 mol. % to about 10 mol. %.

14. The method of claim 13 , wherein the anionic monomer unit is present in first PVOH copolymer in an amount in a range of about 5 mol. % to about 10 mol. %.

15. The method of claim 14 , wherein the anionic monomer unit is present in an amount in a range of about 3 mol. % to about 4.2 mol. % of total PVOH polymers and PVOH copolymers in the film.

16. The method of claim 1 , wherein the PVOH resin blend consists essentially of the first PVOH copolymer and the second PVOH polymer.

17. The method of claim 1 , wherein a viscosity difference (μ 2 −μ 1 ) for the first PVOH copolymer and the second PVOH polymer is in a range from about 0 cP to about 10 cP.

18. The method of claim 1 , wherein the first viscosity μ 1 is in a range of about 4 cP to about 24 cP.

19. The method of claim 1 , wherein the second viscosity μ 2 is in a range of about 4 cP to about 24 cP.

20. The method of claim 1 , wherein the water-soluble film has a residue value of about 45 wt. % or less as measured by the Dissolution Chamber Test.

21. The method of claim 1 , wherein the first PVOH copolymer and the second PVOH polymer each independently have a degree of hydrolysis in a range of about 75% to about 99%.

22. The method of claim 1 , wherein the PVOH resin blend comprises a third PVOH polymer.

23. The method of claim 1 , wherein the water-soluble film further comprises at least a third water-soluble polymer which is other than a PVOH polymer.

24. The method of claim 23 , wherein the third water-soluble polymer is selected from the group consisting of polyethyleneimines, polyvinyl pyrrolidones, polyalkylene oxides, polyacrylamides, cellulose ethers, cellulose esters, cellulose amides, polyvinyl acetates, polyamides, gelatines, methylcelluloses, carboxymethylcelluloses and salts thereof, dextrins, ethylcelluloses, hydroxyethyl celluloses, hydroxypropyl methylcelluloses, maltodextrins, starches, modified starches, guar gum, gum Acacia, xanthan gum, carrageenan, polyacrylates and salts thereof, copolymers thereof, blends thereof, and combinations thereof.

25. The method of claim 1 , wherein the water-soluble film further comprises one or more components selected from t

Assignees

• Monosol Llc

Inventors

• Friedrich Steven G
• Lee David M
• Yogan Thomas J
• Labeque Regine

Classifications

• C08L29/04

  Polyvinyl alcohol; Partially hydrolysed homopolymers or copolymers of esters of unsaturated alcohols with saturated carboxylic acids · CPC title

• C08J5/18 Primary

  Manufacture of films or sheets · CPC title

• C11D17/00

  Detergent materials or soaps characterised by their shape or physical properties (shaping soap C11D13/14) · CPC title

• B65D75/08

  with the ends of the tube closed by folding · CPC title

• C08J2329/04

  Polyvinyl alcohol; Partially hydrolysed homopolymers or copolymers of esters of unsaturated alcohols with saturated carboxylic acids · CPC title