Methods for manufacturing fuel cell electrodes and electrodes formed using the same

Patent metadata

Field	Value
Publication number	US-10847808-B2
Application number	US-201715836579-A
Country	US
Kind code	B2
Filing date	Dec 8, 2017
Priority date	Nov 2, 2017
Publication date	Nov 24, 2020
Grant date	Nov 24, 2020

Abstract

A method for manufacturing a fuel cell electrode includes forming a first mixture by mixing a first cation exchange resin, a metal catalyst, and a first solvent, powderizing the first mixture to produce a first catalyst powder comprising the metal catalyst coated with the first cation exchange resin, forming a second mixture by mixing the first catalyst powder, a second cation exchange resin, and a second solvent, powderizing the second mixture to produce a catalyst powder having a core and two or more layers of shells and being coated with the second cation exchange resin, mixing the catalyst powder having the core and two or more layers of shells with a third solvent to produce a catalyst slurry, and coating, using the catalyst slurry, to produce an electrode.

First claim

What is claimed is:

1. A method for manufacturing a fuel cell electrode, the method comprising:
forming a first mixture by mixing a first cation exchange resin, a metal catalyst, and a first solvent;
powderizing the first mixture to produce a first catalyst powder comprising the metal catalyst coated with the first cation exchange resin;
forming a second mixture by mixing the first catalyst powder, a second cation exchange resin, and a second solvent;
powderizing the second mixture to produce a catalyst powder having a core and two or more layers of shells and being coated with the second cation exchange resin;
mixing the catalyst powder having the core and two or more layers of shells with a third solvent to produce a catalyst slurry; and
coating, using the catalyst slurry, to produce an electrode.

2. The method according to claim 1 , wherein powderizing the first mixture and powderizing the second mixture is carried out using a spray dryer at a temperature of 80° C. to 200° C.

3. The method according to claim 1 , wherein the first cation exchange resin or the second cation exchange resin is selected from the group consisting of polysulfone resins, polyether ketone resins, polyether resins, polyester resins, polybenzimidazole resins, polyimide resins, polyphenylene sulfide resins, and polyphenylene oxide resins.

4. The method according to claim 1 , wherein the first cation exchange resin is a polysulfone resin having an equivalent weight of 750 or more, and the second cation exchange resin is a polysulfone resin having an equivalent weight of 700 or less.

5. The method according to claim 1 , wherein the metal catalyst includes an element selected from the group consisting of platinum, palladium, iridium, rhodium, gold, silver, cobalt and nickel.

6. The method according to claim 1 , wherein the electrode is produced by directly coating on a release paper or an electrolyte film with the catalyst slurry by spray coating, bar coating or slot-die coating.

7. The method according to claim 6 , wherein the release paper comprises a film selected from the group consisting of polyethylene naphthalate (PEN), polyethylene terephthalate (PET), and polytetrafluoroethylene (PTFE).

8. The method according to claim 1 , further comprising forming a membrane electrode assembly (MEA) by transferring the electrode to an electrolyte membrane and hot pressing.

9. The method according to claim 1 , wherein the electrode is directly coated on an electrolyte membrane.

10. The method according to claim 1 , further comprising forming a dispersed first mixture by dispersing the first mixture using a stirrer, disperser or ultrasonic disperser, wherein the powderizing the first mixture comprises drying the dispersed first mixture using a spray dryer.

11. A method for manufacturing a fuel cell electrode, the method comprising:
providing a first mixture comprising a mixture of a first cation exchange resin, a metal catalyst, and a first solvent;
coating the metal catalyst with the first cation exchange resin to produce a first catalyst powder;
providing a second mixture comprising a mixture of the first catalyst powder, a second cation exchange resin, and a second solvent;
powderizing the second mixture to produce a second catalyst powder having a core and two or more layers of shells and being coated with the second cation exchange resin, wherein an equivalent weight of the second cation exchange resin is less than an equivalent weight of the first cation exchange resin;
mixing the second catalyst powder with a third solvent to produce a catalyst slurry; and
using the catalyst slurry to produce an electrode.

12. The method according to claim 11 , wherein coating the first catalyst powder and powderizing the second mixture is carried out using a spray dryer at a temperature of 80° C. to 200° C.

13. The method according to claim 11 , wherein the first cation exchange resin or the second cation exchange resin is selected from the group consisting of polysulfone resins, polyether ketone resins, polyether resins, polyester resins, polybenzimidazole resins, polyimide resins, polyphenylene sulfide resins, and polyphenylene oxide resins.

14. The method according to claim 11 , wherein the first cation exchange resin is a polysulfone resin having an equivalent weight of 750 or more, and the second cation exchange resin is a polysulfone resin having an equivalent weight of 700 or less.

15. The method according to claim 11 , wherein the metal catalyst includes an element selected from the group consisting of platinum, palladium, iridium, rhodium, gold, silver, cobalt and nickel.

16. The method according to claim 11 , wherein the electrode is produced by directly coating on a release paper or an electrolyte film with the catalyst slurry by spray coating, bar coating, or slot-die coating, wherein the release paper comprises a film selected from the group consisting of polyethilene naftenate (PEN), polyethylene terephthalate (PET), and polytetrafluoroethylene (PTFE).

17. The method according to claim 11 , further comprising forming a membrane electrode assembly (MEA) by transferring the electrode to an electrolyte membrane and hot pressing.

18. The method according to claim 11 , further comprising forming a dispersed first mixture by dispersing the first mixture using a stirrer, disperser or ultrasonic disperser, wherein the powderizing the first mixture comprises drying the dispersed first mixture using a spray dryer.

Assignees

• Hyundai Motor Co Ltd
• Kia Motors Corp

Inventors

• Cho Yoon Hwan
• Seol Su Won
• Yang Ji Hoon
• Kim Young Taek
• Son Dae Yong

Classifications

• Y02P70/50

  Manufacturing or production processes characterised by the final manufactured product · CPC title

• H01M2008/1095

  Fuel cells with polymeric electrolytes · CPC title

• H01M4/92

  Metals of platinum group (H01M4/94 {, H01M4/9058} take precedence) · CPC title

• H01M4/9041

  Metals or alloys (H01M4/92 takes precedence) · CPC title

• H01M4/8828

  Coating with slurry or ink · CPC title