Press-hardened sheet metal component with at least one predetermined breaking point, and component assembly and motor vehicle body with such a sheet metal component

Patent metadata

Field	Value
Publication number	US-10662498-B2
Application number	US-201715591336-A
Country	US
Kind code	B2
Filing date	May 10, 2017
Priority date	Dec 19, 2014
Publication date	May 26, 2020
Grant date	May 26, 2020

Abstract

A sheet metal component that is made of a press-hardened steel sheet material and is to be used as a vehicle body component for a motor vehicle, is provided. The sheet metal component has at least one overhardened component region which is provided to act as a predetermined breaking point in the event of being subject to a crash load. A component assembly and a motor vehicle body, which have at least one such press-hardened sheet metal component, are also provided.

First claim

What is claimed is:

1. A vehicle sheet metal component made of a press-hardened steel sheet material, comprising:
at least one overhardened component region in the vehicle sheet metal component, wherein the at least one overhardened component region defines a predetermined breaking point in the vehicle sheet metal component in an event of the vehicle sheet metal component being subject to a crash load and wherein the vehicle sheet metal component is a transverse support of a motor vehicle,
wherein the at least one overhardened component region is a region or surface section of the vehicle sheet metal component in which the press-hardened steel sheet material has a higher hardness and a lower ductility than other regions of the vehicle sheet metal component.

2. The vehicle sheet metal component according to claim 1 , wherein
outside the at least one overhardened component region, the steel sheet material has different strengths than a strength of the at least one overhardened component region.

3. The vehicle sheet metal component according to claim 1 , wherein
in the at least one overhardened component region, the steel sheet material has a strength that is at least by 100 MPa above the highest strength outside the at least one overhardened component region.

4. The vehicle sheet metal component according to claim 1 , wherein
in the at least one overhardened component region, the steel sheet material has a strength that is at least by 200 MPa above the highest strength outside the at least one overhardened component region.

5. The vehicle sheet metal component according to claim 1 , wherein
in the at least one overhardened component region, the steel sheet material has a strength that is at least by 300 MPa above the highest strength outside the at least one overhardened component region.

6. The vehicle sheet metal component according to claim 1 , wherein
in the at least one overhardened component region, the steel sheet material has a strength that is at least by 400 MPa above the highest strength outside the at least one overhardened component region.

7. The vehicle sheet metal component according to claim 1 , wherein
in the at least one overhardened component region, the steel sheet material has a strength of at least 1,600 MPa.

8. The vehicle sheet metal component according to claim 1 , wherein
in the at least one overhardened component region, the steel sheet material has a strength of at least 1,700 MPa.

9. The vehicle sheet metal component according to claim 1 , wherein
in the at least one overhardened component region, the steel sheet material has a strength of at least 1,800 MPa.

10. The vehicle sheet metal component according to claim 1 , wherein
in the at least one overhardened component region, the steel sheet material has a strength of at least 1,900 MPa.

11. The vehicle sheet metal component according to claim 1 , wherein
the at least one overhardened component region extends from an outer edge of the sheet metal component to at least one other outer edge of the sheet metal component.

12. The vehicle sheet metal component according to claim 1 , wherein
the sheet metal component has a substantially homogeneous sheet metal thickness.

13. A component assembly for a motor vehicle body, comprising:
at least one press-hardened sheet metal component according to claim 1 , wherein
in an event of being subject to a crash load, the at least one press-hardened sheet metal component is tearable and/or breakable in at least one overhardened component region in order to deflect collision energy in a targeted manner into one or more other components.

14. The component assembly according to claim 13 , further comprising:
additional components joined with the at least one press-hardened sheet metal component, which include at least one of castings, sheet metal parts, profile parts or plastic composite parts.

15. A motor vehicle body for a passenger car, comprising:
at least one press-hardened sheet metal component according to claim 1 ; and/or
at least one component assembly, comprising:
at least one press-hardened sheet metal component, wherein
in an event of being subject to a crash load, the at least one press-hardened sheet metal component is tearable and/or breakable in at least one overhardened component region in order to deflect collision energy in a targeted manner into one or more other components.

16. The vehicle sheet metal component according to claim 1 , wherein
the at least one overhardened component region has reduced ductility and/or increased embrittlement compared to the steel sheet material outside the at least one overhardened component region.

17. The vehicle sheet metal component according to claim 1 , wherein
the at least one overhardened component region is generated by way of a cooling device of a press-hardening tool to produce the press-hardened steel sheet material.

18. A vehicle sheet metal component made of a press-hardened steel sheet material, comprising:
at least one overhardened component region which is provided to act as a predetermined breaking point in an event of being subject to a crash load, wherein
outside the at least one overhardened component region, the steel sheet material has a substantially homogeneous strength, which ranges from 1,300 MPa to 1,500 MPa.

19. The vehicle sheet metal component according to claim 18 , wherein
outside the at least one overhardened component region, the steel sheet material has different strengths than a strength of the at least one overhardened component region.

Assignees

• Bayerische Motoren Werke Ag

Inventors

• Becker Juergen
• Kupetz Bernd

Classifications

• C22C38/002

  containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60 · CPC title

• B21D53/88

  other parts for vehicles, e.g. cowlings, mudguards · CPC title

• C21D9/46 Primary

  for sheet metals · CPC title

• B62D21/15 Primary

  having impact absorbing means, e.g. a frame designed to permanently or temporarily change shape or dimension upon impact with another body (bumpers B60R19/02; shock absorbers in general F16F) · CPC title

• C21D1/673

  for die quenching · CPC title