Method of making structured hybrid adhesive articles including lightning strike protection sheets

Patent metadata

Field	Value
Publication number	US-10625463-B2
Application number	US-201916265211-A
Country	US
Kind code	B2
Filing date	Feb 1, 2019
Priority date	Jul 3, 2012
Publication date	Apr 21, 2020
Grant date	Apr 21, 2020

Abstract

A method is provided for making structured hybrid adhesive articles such as lightning strike protection sheets. In the embodiment for making lightning strike protection sheets, the method comprises the steps of: a) providing an adhesive article comprising: i) a base resin comprising an epoxy resin, ii) a first epoxy curative, and iii) a second epoxy curative; b) reacting the base resin with the first epoxy curative such that the first epoxy curative is substantially reacted with epoxy resin in the article and the second epoxy curative is substantially unreacted in the article; c) embossing the adhesive article with a relief pattern; d) depositing an electrically-conductive layer onto at least a portion of the embossed surface; and e) curing the adhesive article such that the second epoxy curative is substantially reacted with epoxy in the article. In some embodiments, the method additionally comprises a step of embedding a scrim in the adhesive.

First claim

We claim:

1. A method of making a lightning strike protection sheet, the method comprising the steps of:
a) providing an adhesive article comprising:
i) a base resin comprising an epoxy resin;
ii) a first epoxy curative; and
iii) a second epoxy curative;

b) reacting the base resin with the first epoxy curative to form a first polymer network such that the first epoxy curative is substantially reacted with epoxy resin in the adhesive article and the second epoxy curative is substantially unreacted in the adhesive article;
c) embossing the adhesive article with a relief pattern;
d) depositing an electrically-conductive layer onto at least a portion of the surface of the adhesive article embossed with a relief pattern, such that the electrically-conductive layer is patterned with a plurality of hill features and/or valley features; and
e) after step d), curing the adhesive article to form a second polymer network such that the second epoxy curative is substantially reacted with epoxy in the article.

2. The method according to claim 1 wherein the first and second epoxy curatives are chosen such that the second epoxy curative may remain substantially unreacted in the composition under conditions of temperature and duration that render the first epoxy curative substantially reacted with epoxy resin in the composition.

3. The method according to claim 1 , wherein the first and second epoxy curatives are chosen such that the second epoxy curative remains substantially unreacted in the composition after 24 hours at 72° F. and the first epoxy curative becomes substantially reacted with epoxy resin in the composition after 24 hours at 72° F.

4. The method according to claim 1 , wherein the first epoxy curative is a polymercaptan.

5. The method according to claim 1 , wherein the second epoxy curative is a polyamine.

6. The method according to claim 1 , wherein the base resin includes no acrylic resin.

7. The method according to claim 1 additionally comprising the step of f) embedding a scrim in the adhesive layer; prior to step c).

8. The method according to claim 1 additionally comprising the step of f) embedding a scrim in the adhesive layer; concurrent with step c).

9. The method according to claim 1 wherein step b) is carried out prior to step c).

10. The method according to claim 1 wherein step b) is carried out simultaneously with step c).

11. The method of claim 1 , wherein the electrically-conductive layer weighs at least 0.5 g/m 2 and less than 50 g/m 2 .

12. The method of claim 11 , wherein the electrically-conductive layer weighs at least 0.5 g/m 2 and less than 20 g/m 2 .

13. The method of claim 12 , wherein the electrically-conductive layer weighs at least 0.5 g/m 2 and less than 4 g/m 2 .

14. The method of claim 1 , wherein the electrically-conductive layer is patterned with a plurality of hill features having a height h between 0.1 microns and 10 mm.

15. The method of claim 14 , wherein the plurality of hill features have a height h between 1 micron and 2 mm.

16. The method of claim 15 , wherein the plurality of hill features have a height h between 6 microns and 1 mm.

17. The method of claim 1 , wherein the electrically-conductive layer is patterned with a plurality of hill features having a pitch of between 10 microns and 50 mm.

18. The method of claim 17 , wherein the plurality of hill features have a pitch of between 50 microns and 10 mm.

19. The method of claim 18 , wherein the plurality of hill features have a pitch of between 200 microns and 1 mm.

20. The method of claim 1 , wherein the electrically-conductive layer is patterned with a plurality of valley features having a depth d between 6 microns and 1 mm.

Assignees

• 3M Innovative Properties Co

Inventors

• Hebert Larry S
• Salnikov Dmitriy

Classifications

• C08G59/66

  Mercaptans · CPC title

• B29K2063/00

  Use of {EP, i.e.} epoxy resins {or derivatives thereof}, as moulding material · CPC title

• B29C59/005 Primary

  characterised by the choice of material · CPC title

• C08G59/56 Primary

  together with other curing agents · CPC title

• C09J163/00

  Adhesives based on epoxy resins; Adhesives based on derivatives of epoxy resins · CPC title