Stabilized fluoride phosphor for light emitting diode (LED) applications

Patent metadata

Field	Value
Publication number	US-10608148-B2
Application number	US-201815994105-A
Country	US
Kind code	B2
Filing date	May 31, 2018
Priority date	May 31, 2018
Publication date	Mar 31, 2020
Grant date	Mar 31, 2020

Abstract

A stabilized fluoride phosphor for light emitting diode (LED) applications includes a particle comprising manganese-activated potassium fluorosilicate and an inorganic coating on each of the particles. The inorganic coating comprises a silicate. A method of making a stabilized fluoride phosphor comprises forming a reaction mixture that includes particles comprising a manganese-activated potassium fluorosilicate; a reactive silicate precursor; a catalyst; a solvent; and water in an amount no greater than about 10 vol. %. The reaction mixture is agitated to suspend the particles therein. As the reactive silicate precursor undergoes hydrolysis and condensation in the reaction mixture, an inorganic coating comprising a silicate is formed on the particles. Thus, a stabilized fluoride phosphor is formed.

First claim

The invention claimed is:

1. A method of making a stabilized fluoride phosphor, the method comprising:
forming a reaction mixture comprising:
particles comprising a manganese-activated potassium fluorosilicate,
a reactive silicate precursor,
a catalyst,
a solvent, and
water in an amount no greater than about 10 vol. %, and

agitating the reaction mixture to suspend the particles therein,
wherein, as the reactive silicate precursor undergoes hydrolysis and condensation in the reaction mixture, an inorganic coating comprising a silicate is formed on each of the particles, thereby forming a stabilized fluoride phosphor.

2. The method of claim 1 , wherein the agitating employs a technique selected from the group consisting of: magnetic stirring, overhead stirring with an impeller, orbital shaking, and tumbling.

3. The method of claim 1 , wherein the reactive silicate precursor comprises a silane selected from the group consisting of: tetraethylorthosilicate (TEOS), tetramethylorthosilicate (TMOS), and tetrapropylorthosilicate (TPOS), and
wherein the catalyst comprises a nonaqueous catalyst.

4. The method of claim 3 , wherein the nonaqueous catalyst comprises an organic amine.

5. The method of claim 1 , wherein the solvent is dried prior to incorporation in the reaction mixture.

6. The method of claim 1 , wherein the reactive silicate precursor comprises an organosilane precursor.

7. The method of claim 1 , wherein, prior to adding the catalyst, the solvent, and the water to the reaction mixture, an organosilane precursor is added to the reaction mixture to bond with the particles and act as adhesion promoter for formation of the inorganic coating.

8. The method of claim 1 , further comprising adding a reactive metal oxide precursor comprising boron, aluminum or titanium to the reaction mixture.

9. The method of claim 1 , further comprising removing the stabilized fluoride phosphor from the reaction mixture,
wherein, outside the reaction mixture, hydrolysis and condensation continues, the inorganic coating thereby continuing to form.

10. The method of claim 1 , further comprising heating the stabilized fluoride phosphor at an elevated temperature in a range from about 200° C. to about 700° C. to densify the inorganic coating.

11. A stabilized fluoride phosphor for light emitting diode (LED) applications, the stabilized fluoride phosphor comprising:
particles comprising manganese-activated potassium fluorosilicate;
an inorganic coating on each of the particles, the inorganic coating comprising a silicate, and
a fluoride coating under the inorganic coating.

12. The stabilized fluoride phosphor of claim 11 , wherein the fluoride coating comprises potassium fluorosilicate without an activator, or another fluoride compound.

13. The stabilized fluoride phosphor of claim 11 , wherein the silicate comprises a multicomponent silicate including aluminum, boron, and/or titanium.

14. The stabilized fluoride phosphor of claim 11 , wherein the inorganic coating further comprises an oxide of aluminum, boron, and/or titanium.

15. The stabilized fluoride phosphor of claim 11 , wherein the silicate comprises SiO x , where 0.5≤x≤2.5.

16. The stabilized fluoride phosphor of claim 11 , wherein the inorganic coating comprises a thickness in the range from about 5 nm to about 2 microns.

17. The stabilized fluoride phosphor of claim 16 , wherein the thickness is in a range from about 0.1 micron to about 2 microns.

18. The stabilized fluoride phosphor of claim 11 , wherein the inorganic coating further comprises Si—OH groups.

19. The stabilized fluoride phosphor of claim 11 , comprising an infrared absorption spectrum wherein a ratio of an absorption intensity of a SiO x signal to an absorption intensity of a SiF 6 2− signal is in a range from about 0.05 to about 2.5.

20. A light emitting device comprising:
a blue light emitting diode (LED) chip having a dominant wavelength of 420 nm to 490 nm in optical communication with a wavelength conversion material comprising the stabilized fluoride phosphor of claim 11 for down conversion of light emitted from the blue LED chip.

21. The light emitting device of claim 20 exhibiting narrow-band red light emission with a peak emission wavelength in a range from 610 nm to 660 nm and comprising a full-width-at-half-maximum (FWHM) of less than 45 nm.

22. The light emitting device of claim 20 , wherein the wavelength conversion material further comprises a plurality of quantum dots.

23. The light emitting device of claim 20 , wherein the wavelength conversion material further comprises a yellow phosphor exhibiting yellow light emission with a peak emission wavelength in a range from 575 nm to 600 nm.

24. The light emitting device of claim 23 , wherein the yellow light emission has a full-width-at-half-maximum (FWHM) of less than 60 nm, the yellow light emission being narrow band yellow light emission.

25. The light emitting device of claim 20 , wherein the wavelength conversion material further comprises a green phosphor exhibiting green light emission with a peak emission wavelength in a range from 498 nm to 550 nm.

26. The light emitting device of claim 25 , wherein the green light emission has a full-width-at-half-maximum (FWHM) of less than 60 nm, the green light emission being narrow band green light emission.

27. The light emitting device of claim 20 used in at least one of the following: indoor lighting products; display backlighting for televisions, monitors, tablets or smart phones; and horticultural lighting products.

Assignees

• Cree Inc

Inventors

• Gresback Ryan
• Lotito Kenneth
• Mu Linjia

Classifications

• C09K11/617

  Silicates · CPC title

• C09K11/025 Primary

  non-luminescent particle coatings or suspension media · CPC title

• H01L33/44

  Electricity · mapped topic

• H01L33/502 Primary

  Electricity · mapped topic

• H01L33/005

  Electricity · mapped topic