Abstract

The invention concerns an extruded composite containing wood fibre material and polymer. The wood fibre material is wood material where the knot or branch content is at least 10 w-%, or bark, or would material into which extract material obtained by extracting knots, branches or bark has been absorbed. The amount of the polymer is 5-25% from the weight of the composite. The composite has high hardness, and reduced moisture absorption and swelling properties. It can be used as constructional material.

First claim

The invention claimed is:

1. An extruded composite comprising:
a wood fibre material in an amount of 60 to 90 weight % of the extruded composite, wherein the wood fibre material is a pine heartwood material having a knot content between at least about 20 weight % and up to about 78.5 weight %;
a polymer in an amount of at least 5 weight % and up to 25 weight % of the extruded composite;
an optional coupling agent comprising maleic anhydride grafted polypropylene; and
an optional lubricant;
wherein the extruded composite is substantially devoid of a filler material comprising fibre glass, talc, calcium carbonate, zinc borate, melamine, and aluminium trihydrate.

2. The extruded composite of claim 1 , wherein the polymer is polyalkylene or biopolymer.

3. The extruded composite of claim 2 , wherein the polymer is polyalkylene chosen from polypropylene or polyethylene.

4. The extruded composite of claim 2 , wherein the polymer is biopolymer chosen from starch or polylactic acid.

5. The extruded composite of claim 1 , wherein the amount of polymer is between about 10 weight % and about 17 weight % of the extruded composite.

6. The extruded composite of claim 5 , wherein the polymer is polypropylene or polyethylene.

7. The extruded composite of claim 1 , wherein the extruded composite is used in a manufactured material chosen from a construction material, a decorative material, a packaging material, a transport material or a furniture material.

Assignees

• Pynnoenen Janne
• Myyrylaeinen Matti
• Mayes Duncan
• Silen Jouko
• Stora Enso Oyj

Inventors

• Pynnönen Janne
• Myyryläinen Matti
• Mayes Duncan
• Silen Jouko

Classifications

• B27N3/28

  characterised by using extrusion presses · CPC title

• B27N3/007 Primary

  and at least partly composed of recycled material · CPC title

• C08L97/02 Primary

  Lignocellulosic material, e.g. wood, straw or bagasse {(manufacture of articles made from lignocellulosic material by dry processes B27N)} · CPC title