Lithium cell electrode using surface-modified copper foil current collector

Patent metadata

Field	Value
Publication number	US-10597783-B2
Application number	US-201715471029-A
Country	US
Kind code	B2
Filing date	Mar 28, 2017
Priority date	Mar 28, 2017
Publication date	Mar 24, 2020
Grant date	Mar 24, 2020

Abstract

A copper foil, intended for use as a current collector in a lithium-containing electrode for a lithium-based electrochemical cell, is subjected to a series of chemical oxidation and reduction processing steps to form a field of integral copper wires extending outwardly from the surfaces of the current collector (and from the copper content of the foil) to be coated with a resin-bonded porous layer of particles of active electrode material. The copper wires serve to anchor thicker layers of porous electrode material and enhance liquid electrolyte contact with the electrode particles and the current collector to improve the energy output of the cell and its useful life.

First claim

The invention claimed is:

1. A method of re-shaping at least a selected area of a flat surface of a copper foil to enhance the subsequent application of a layer of a porous resin-bonded coating of particles of electrode material for a lithium electrochemical cell; the method comprising:
reacting the selected area of the flat copper surface with an aqueous solution of a hydroxide ion-containing and a copper metal oxidant-containing composition at a predetermined temperature and for a predetermined period of time to react with a portion of the copper at the flat surface of the copper foil to form a field of wires or wire-like protrusions of copper hydroxide, each copper hydroxide wire being anchored at one end to un-reacted copper at the surface of the copper foil, the copper hydroxide wires extending outwardly from the un-reacted copper surface, the field of copper hydroxide wires extending over the selected area of the copper surface of the copper foil;
heating the field of copper hydroxide wires in air to convert the copper hydroxide wires to a field of copper oxide wires; and
reacting the field of copper oxide wires with hydrogen to convert the copper oxide wires to a field of copper wires;
the surface of the copper foil being thus prepared for the subsequent application of the porous resin-bonded coating of particles of electrode material to either (i) the field of copper wires, or (ii) to the formed field of copper oxide wires.

2. A method of re-shaping at least a selected portion of the flat surface of the copper foil as stated in claim 1 in which the copper wires have lengths in the range from two micrometers to thirty micrometers.

3. A method of re-shaping at least a selected portion of the flat surface of the copper foil as stated in claim 1 in which the selected area of the copper surface is initially reacted with an aqueous solution of ammonium persulfate and hydroxide ions to form the field of copper hydroxide wires.

4. A method of re-shaping at least a selected portion of the flat surface of the copper foil as stated in claim 3 in which the concentration of ammonium persulfate in the aqueous solution is in the range of 0.02 M to 0.12 M.

5. A method of re-shaping at least a selected portion of the flat surface of the copper foil as stated in claim 1 in which the selected area of the copper surface is initially reacted with an aqueous solution of ammonium persulfate and sodium hydroxide for a period up to two hours to form the field of copper hydroxide wires.

6. A method of re-shaping at least a selected portion of the flat surface of the copper foil as stated in claim 1 in which the field of copper hydroxide wires is heated in air at a temperature in the range of 60° C. to 90° C. to convert the copper hydroxide wires to the field of copper oxide wires.

7. A method of re-shaping at least a selected portion of the flat surface of the copper foil as stated in claim 1 in which the field of copper oxide wires is heated under hydrogen gas at a temperature of 120° C. to 150° C. to convert the copper oxide wires to the field of copper wires.

8. A method of forming an electrode comprising a copper foil current collector for a lithium ion-processing electrochemical cell, in which method a selected surface area of the copper foil is modified preparatory to the subsequent application of a layer of a porous resin-bonded coating of particles of electrode material for the lithium electrochemical cell to the selected surface area of the copper foil; the method comprising:
reacting the selected area of the surface of the copper foil with an aqueous solution of a hydroxide ion-containing and oxidizing composition at a predetermined temperature and for a predetermined period of time to react with a portion of the copper foil at the surface of the copper foil to form wires or wire-like protrusions of copper hydroxide, each copper hydroxide wire being anchored at one end to remaining un-reacted copper at the surface of the copper foil, the copper hydroxide wires extending outwardly from the un-reacted copper surface and forming a field of the wires over the selected area of the copper surface of the copper foil;
heating the field of copper hydroxide wires in air to convert the copper hydroxide wires to a field of copper oxide wires;
reacting the field of copper oxide wires with hydrogen gas to convert the copper oxide wires to a field of copper wires; and
applying the porous resin-bonded coating of particles of electrode material to either (i) the field of copper wires, or to (ii) the field of copper oxide wires and thereafter reacting the copper oxide wires with hydrogen to convert them to a field of copper wires which are filled with the particles of electrode material.

9. A method of forming an electrode comprising a copper foil current collector for a lithium ion-processing electrochemical cell as stated in claim 8 in which the copper wires have lengths in the range from two micrometers to thirty micrometers.

10. A method of forming an electrode comprising a copper foil current collector for a lithium ion-processing electrochemical cell as stated in claim 8 in which
a liquid-based slurry, comprising particles of lithium electrode material and a binder resin, is applied onto and into the field of copper wires to form a porous layer of particulate electrode material that surrounds the copper wires and is resin-bonded to the copper wires and to the remaining copper surface of the current collector foil, the porosity of the porous layer of particulate electrode material being sufficient to permit exposure of portions of the copper wires and the remaining copper surface of the current collector foil to a subsequently applied liquid electrolyte used in the operation of the electrode in the lithium electrochemical cell.

11. A method of forming an electrode comprising a copper foil current collector for a lithium ion-processing electrochemical cell as stated in claim 8 in which
a liquid-based slurry comprising particles of lithium electrode material and a binder resin, is applied onto and into the field of copper oxide wires to form a porous layer of particulate electrode material that surrounds the copper oxide wires and is resin-bonded to the copper oxide wires and to the remaining copper surface of the current collector foil, and
the copper oxide wires are then reduced to copper wires by reaction with hydrogen, the porosity of the porous layer of particulate electrode material permitting exposure of portions of the copper wires and the remaining copper surface of the current collector foil to a subsequently applied liquid electrolyte used in the operation of the electrode in its lithium electrochemical cell.

12. A method of forming an electrode comprising a copper foil current collector for a lithium electrochemical cell as stated in claim 8 in which
a surface of a porous layer of resin-bonded active particulate electrode material is pressed against the field of copper wires such that the copper wires penetrate through the surface of the porous layer and into the porous layer leaving buffer space between the penetrated surface of the applied layer and the remaining copper surface of the current collector foil, the porosity of the porous layer of resin-bonded particulate electrode material permitting exposure of portions of the copper wires and the remaining copper surface of the current collector foil to a subsequently applied liquid electrolyte used in the operation of the electrode in its lithium electrochemical cell.

13. A method of forming an electrode comprising a copper foil current collector for a lithium ion-processing electrochemical cell as stated in

Assignees

• Gm Global Tech Operations Llc

Inventors

• Liu Haijing
• Yu Zhiqiang
• Que Xiaochao

Classifications

• H01M4/667 Primary

  in the form of layers, e.g. coatings · CPC title

• H01M4/0404 Primary

  by coating on electrode collectors · CPC title

• H01M4/668

  Composites of electroconductive material and synthetic resins · CPC title

• C23C18/1295 Primary

  with after-treatment of the deposited inorganic material · CPC title

• C23C18/1208

  Oxides, e.g. ceramics · CPC title