Kit of parts for producing a glass ionomer cement, process of production and use thereof

Patent metadata

Field	Value
Publication number	US-10548818-B2
Application number	US-201615745565-A
Country	US
Kind code	B2
Filing date	Jul 18, 2016
Priority date	Jul 21, 2015
Publication date	Feb 4, 2020
Grant date	Feb 4, 2020

Abstract

The application relates to a kit of parts for preparing a glass ionomer composition for dental use, the kit comprising a Paste A and a Paste B, Paste A comprising water, acid-reactive inorganic filler C, non acid-reactive filler A, Paste B comprising water, polyacid, complexing agent, non acid-reactive filler B, the mean particle size of non acid-reactive filler B being larger than the mean particle size of non acid-reactive filler A, the water content of the composition obtained when mixing Paste A and Paste B being below 20 wt.-%. The application also relates to a device for storing such a kit of parts and the use of the kit of parts and/or the device for preparing a dental cement, dental filling material, dental core build up material or dental root channel filling material.

First claim

The invention claimed is:

1. A kit of parts for preparing a glass ionomer composition for dental use, the kit comprising: a Paste A and a Paste B,
Paste A comprising:
water in an amount from 5 to 18 wt.-%;
an acid-reactive inorganic filler C in an amount from 20 to 90 wt.-%, the acid-reactive inorganic filler C having a mean particle size in the range from 3 to 10 μm and being selected from metal oxides, metal hydroxides, hydroxyapatite, aluminosilicate glasses, fluoroaluminosilicate glasses and mixtures thereof; and
a non acid-reactive filler A in an amount from 1 to 50 wt.-%, the non acid-reactive filler A having a mean particle size in the range from 10 nm to 500 nm and being selected from silica, alumina, titania, zirconia and mixtures thereof; and

Paste B comprising:
water in an amount from 7 to 20 wt.-%;
a polyacid in an amount from 3 to 70 wt.-%;
a complexing agent in an amount from 0.1 to 12 wt.-%; and
a non acid-reactive filler B in an amount from 5 to 60 wt.-%, the non acid-reactive filler B having a mean particle size in the range from 1 to 10 μm and being selected from quartz, kaolin, silica, alumina, titania, zirconia and mixtures thereof;

wt.-% with respect to the weight of the respective Paste A or Paste B,
wherein neither Paste A nor Paste B comprising polymerizable component(s) in an amount above 1 wt.-% with respect to the weight of the composition obtained when mixing Paste A and Paste B.

2. The kit of parts of claim 1 , the water content of Paste A being lower than the water content of Paste B.

3. The kit of parts of claim 1 , the non acid-reactive filler A being characterized by the following feature:
pH value of a dispersion of 1 g filler stirred in 10 ml de-ionized water for 5 minutes: between 4 and 7.

4. The kit of parts of claim 1 , the non acid-reactive filler B being characterized by the following feature:
pH value of a dispersion of 1 g filler stirred in 10 ml de-ionized water for 5 minutes: between 4 and 7.

5. The kit of parts of claim 1 , the acid-reactive inorganic filler C being characterized by the following feature:
pH value of a dispersion of 1 g filler stirred in 10 ml de-ionized water for 5 minutes: between 6 and 10.

6. The kit of parts of claim 1 , the acid-reactive inorganic filler C the being selected from basic metal oxides, metal hydroxides, hydroxyapatite, aluminosilicate glasses, fluoroaluminosilicate glasses, glasses having a Si/Al ratio by wt.-% of below 1.5 and mixtures thereof.

7. The kit of parts of claim 6 , Paste A being characterized by at least one or more of the following parameters:
viscosity: from 200 to 50,000 at 28° C., measured at a shear rate of 1 s −1 ;
density: from 1.9 to 2.8 g/cm 3 ;
pH value: from 7 to 10 determined with a pH electrode for 1 g Paste A dispersed in 10 ml de-ionized water and stirred for 5 minutes.

8. The kit of parts of claim 1 , Paste B being characterized by at least one or more of the following parameters:
viscosity: from 1,000 to 50,000 at 28° C., measured at a shear rate of 1 s −1 ;
density: from 1.5 to 2.0 g/cm 3 ;
pH value: from 1 to 4 determined with a pH electrode for 1 g of Paste B dispersed in 10 ml de-ionized water and stirred for 5 minutes.

9. The kit of parts of claim 1 , neither Paste A nor Paste B comprising at least one or more or all of the following components:
polymerizable component(s) in an amount above about 1 wt.-%;
initiator component(s) suitable to cure polymerizable component(s) in an amount above 1 wt.-%;
inhibitior(s) in an amount above 1 wt.-%;
desiccant(s) in an amount above 1 wt.-%, wt.-% with respect to the weight of the respective Paste A or Paste B.

10. A hardened composition for dental use, the hardened composition being obtainable by mixing Paste A and Paste B of the kit of parts described in claim 1 to obtain a mixture, and letting the mixture harden, the hardened composition being characterized by at least one or more of the following parameters:
Flexural strength: above 20 MPa determined according to EN-ISO 9917-2:2010;
Compressive strength: above 100 MPa determined according to EN-ISO 9917-1/2007.

11. A device for storing the kit of parts described in claim 1 , the device comprising two compartments, Compartment A and Compartment B, Compartment A containing Paste A and Compartment B containing Paste B, Compartment A and Compartment B both comprising a nozzle or an interface for receiving an entrance orifice of a static mixing tip.

Assignees

• 3M Innovative Properties Co

Inventors

• Jahns Michael
• Braun Peter
• Peez Robert
• Mikulla Markus
• Guggenberger Rainer A

Classifications

• A61K6/77

  Glass · CPC title

• A61K6/54

  Filling; Sealing · CPC title

• A61K6/889 Primary

  Polycarboxylate cements; Glass ionomer cements · CPC title

• A61K6/818

  comprising zirconium oxide · CPC title

• A61K6/75 Primary

  Apatite · CPC title