Silicone hydrogel lenses with water-rich surfaces

Patent metadata

Field	Value
Publication number	US-10513628-B2
Application number	US-201816166379-A
Country	US
Kind code	B2
Filing date	Oct 22, 2018
Priority date	Jul 30, 2010
Publication date	Dec 24, 2019
Grant date	Dec 24, 2019

Abstract

The invention is related to a hydrated silicone hydrogel contact lens having a layered structural configuration: a lower water content silicone hydrogel core (or bulk material) completely covered with a layer of a higher water content hydrogel totally or substantially free of silicone. A hydrated silicone hydrogel contact lens of the invention possesses high oxygen permeability for maintaining the corneal health and a soft, water-rich, lubricious surface for wearing comfort.

First claim

What is claimed is:

1. A silicone hydrogel contact lens, comprising:
a silicone hydrogel bulk material covered with an outer surface hydrogel layer,

wherein the silicone hydrogel bulk material comprises (i) repeating units derived from a silicone-containing vinylic monomer, a silicone-containing vinylic macromer, a silicone-containing prepolymer, or combinations thereof, and (ii) repeating units derived from a hydrophilic vinylic monomer, and has a first water content, designated as WC SiHy , of from about 10% to about 70% by weight when being fully hydrated,
wherein the outer surface hydrogel layer comprises polymer chains derived from a copolymer which is a polymerization of a composition comprising (1) 60% by weight or less of at least one reactive vinylic monomer and (2) a phosphorylcholine-containing vinylic monomer, wherein the reactive vinylic monomer is selected from the group consisting of amino-C 1 -C 6 alkyl (meth)acrylate, C 1 -C 6 alkylamino-C 1 -C 6 alkyl (meth)acrylate, allylamine, vinylamine, amino-C 1 -C 6 alkyl (meth)acrylamide, C 1 -C 6 alkylamino-C 1 -C 6 alkyl (meth)acrylamide, acrylic acid, C 1 -C 4 alkylacrylic acid, N,N-2-acrylamidoglycolic acid, beta-methyl-acrylic acid, alpha-phenyl acrylic acid, beta-acryloxy propionic acid, sorbic acid, angelic acid, cinnamic acid, 1-carboxy-4-phenyl butadiene-1,3, itaconic acid, citraconic acid, mesaconic acid, glutaconic acid, aconitic acid, maleic acid, fumaric acid, tricarboxy ethylene, and combinations thereof, and
wherein the outer surface hydrogel layer is substantially free of silicone as characterized by having a silicon atomic percentage of 5% or less of total elemental percentage as measured by XPS analysis of the silicone hydrogel contact lens in dried state,
wherein the silicone hydrogel contact lens, when being fully hydrated, has: an oxygen transmissibility of at least 40 barrers/mm; an elastic modulus (or Young's Modulus) of from 0.3 MPa to 1.8 MPa; and an averaged water contact angle of 80 degrees or less.

2. The silicone hydrogel contact lens of claim 1 , wherein the outer surface hydrogel layer is substantially free of silicone as characterized by having a silicon atomic percentage of 4% or less of total elemental percentage as measured by XPS analysis of the silicone hydrogel contact lens in dried state.

3. The silicone hydrogel contact lens of claim 2 , wherein the outer surface hydrogel layer has a thickness of at least about 0.1 μm.

4. The silicone hydrogel contact lens of claim 2 , wherein the outer surface hydrogel layer has a thickness of from about 0.25 μm to about 15 μm.

5. The silicone hydrogel contact lens of claim 1 , wherein the outer surface hydrogel layer has a thickness of from about 0.5 μm to about 12.5 μm.

6. The silicone hydrogel contact lens of claim 5 , wherein the outer surface hydrogel layer has a water-swelling ratio of at least about 150%.

7. The silicone hydrogel contact lens of claim 1 , wherein the outer surface hydrogel layer has a thickness of from about 1 μm to about 10 μm.

8. The silicone hydrogel contact lens of claim 7 , wherein the outer surface hydrogel layer has a water-swelling ratio of at least about 150%.

9. The silicone hydrogel contact lens of claim 1 , wherein the reactive vinylic monomer is selected from the group consisting of amino-C 1 -C 6 alkyl (meth)acrylate, C 1 -C 6 alkylamino-C 1 -C 6 alkyl (meth)acrylate, allylamine, vinylamine, amino-C 1 -C 6 alkyl (meth)acrylamide, C 1 -C 6 alkylamino-C 1 -C 6 alkyl (meth)acrylamide, acrylic acid, C 1 -C 4 alkylacrylic acid, N,N-2-acrylamidoglycolic acid, and combinations thereof.

10. The silicone hydrogel contact lens of claim 9 wherein the silicone hydrogel bulk material comprises repeating units derived from a silicone-containing vinylic monomer selected from the group consisting of N-[tris(trimethylsiloxy)silylpropyl]-(meth)acrylamide, N-[tris(dimethylpropylsiloxy)-silylpropyl]-(meth)acrylamide, N-[tris(dimethylphenylsiloxy)silylpropyl] (meth)acrylamide, N-[tris(dimethylethylsiloxy)silylpropyl] (meth)acrylamide, N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl)-2-methyl acrylamide; N-(2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl) acrylamide; N,N-bis[2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy)propyl]-2-methyl acrylamide; N,N-bis[2-hydroxy-3-(3-(bis(trimethylsilyloxy)methylsilyl)propyloxy) propyl] acrylamide; N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)-2-methyl acrylamide; N-(2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl)acrylamide; N,N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]-2-methyl acrylamide; N,N-bis[2-hydroxy-3-(3-(tris(trimethylsilyloxy)silyl)propyloxy)propyl]acrylamide; N-[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]-2-methyl acrylamide; N-[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide; N,N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl) propyloxy)propyl]-2-methyl acrylamide; N,N-bis[2-hydroxy-3-(3-(t-butyldimethylsilyl)propyloxy)propyl]acrylamide; 3-methacryloxy propylpentamethyldisiloxane, tris(trimethylsilyloxy)silylpropyl methacrylate (TRIS), (3-methacryloxy-2-hydroxypropyloxy)propylbis(trimethylsiloxy)methylsilane), (3-methacryloxy-2-hydroxpropyloxy)propyltris(trimethylsiloxy)silane, 3-methacryloxy-2-(2-hydroxyethoxy)-propyloxy)propylbis(trimethylsiloxy)methylsilane, N-2-methacryloxyethyl-O-(methyl-bis-trimethylsiloxy-3-propyl)silyl carbamate, 3-(trimethylsilyl)propylvinyl carbonate, 3-(vinyloxycarbonylthio)propyl-tris(trimethyl-siloxy)silane, 3-[tris(trimethylsiloxy)silyl]propylvinyl carbamate, 3-[tris(trimethylsiloxy)silyl] propyl allyl carbamate, 3-[tris(trimethylsiloxy)silyl]propyl vinyl carbonate, t-butyldimethyl-siloxyethyl vinyl carbonate; trimethylsilylethyl vinyl carbonate, trimethylsilylmethyl vinyl carbonate, and combinations thereof.

11. The silicone hydrogel contact lens of claim 9 , wherein the silicone hydrogel bulk material comprises: (i) repeating units derived from a polysiloxane vinylic monomer, a polysiloxane vinylic macromer, or combinations thereof; and (ii) repeating units derived from a hydrophilic vinylic monomer selected from the group consisting of N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, 2-acrylamidoglycolic acid, 3-acryloylamino-1-propanol, N-hydroxyethyl acrylamide, N-[tris(hydroxymethyl)methyl]-acrylamide, N-methyl-3-methylene-2-pyrrolidone, 1-ethyl-3-methylene-2-pyrrolidone, 1-methyl-5-methylene-2-pyrrolidone, 1-ethyl-5-methylene-2-pyrrolidone, 5-methyl-3-methylene-2-pyrrolidone, 5-ethyl-3-methylene-2-pyrrolidone, 1-n-propyl-3-methylene-2-pyrrolidone, 1-n-propyl-5-methylene-2-pyrrolidone, 1-isopropyl-3-methylene-2-pyrrolidone, 1-isopropyl-5-methylene-2-pyrrolidone, 1-n-butyl-3-methylene-2-pyrrolidone, 1-tert-butyl-3-methylene-2-pyrrolidone, 2-hydroxyethylmethacrylate, 2-hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, trimethylammonium 2-hydroxy propylmethacrylate hydrochloride, aminopropyl methacrylate hydrochloride, dimethylaminoethyl methacrylate, glycerol methacrylate, N-vinyl-2-pyrrolidone, allyl alcohol, vinylpyridine, a C 1 -C 4 -alkoxy polyethylene glycol (meth)acrylate having a weight average molecular weight of up to 1500, methacrylic acid, N-vinyl formamide, N-vinyl acetamide, N-vinyl isopropylamide, N-vinyl-N-methyl acetamide, N-vinyl caprolactam, and mixtures thereof.

12. The silicone hydrogel contact lens of claim 11 , wherein the silicone hydrogel bulk material further comprises repeating units derived from a crosslinking agent.

13. The silicone hydrogel contact lens of claim 12 , wherein the crosslinking agent is selected from th

Assignees

• Novartis Ag

Inventors

• Qiu Yongxing
• Pruitt John Dallas
• Thekveli Sibichen J
• Tucker Robert Carey
• Nelson Jared

Classifications

• G02C7/04

  Contact lenses for the eyes (disinfection or sterilisation of contact lenses A61L12/00) · CPC title

• B29D11/00067 Primary

  Hydrating contact lenses · CPC title

• G02B1/10

  Optical coatings produced by application to, or surface treatment of, optical elements (G02B1/08 takes precedence) · CPC title

• C09D171/02

  Polyalkylene oxides · CPC title

• G02C2202/06

  Special ophthalmologic or optometric aspects · CPC title