Elastic artificial leather and production method therefor

Patent metadata

Field	Value
Publication number	US-10465338-B2
Application number	US-201314381072-A
Country	US
Kind code	B2
Filing date	Feb 26, 2013
Priority date	Feb 29, 2012
Publication date	Nov 5, 2019
Grant date	Nov 5, 2019

Abstract

A production method of an elastically stretchable artificial leather which includes a step of making microfiberizable fibers into a web; a step of entangling the obtained web to produce an entangled nonwoven fabric; a step of converting the microfiberizable fibers in the nonwoven fabric to microfine fibers, thereby producing a substrate for artificial leather; a step of producing an artificial leather by using the obtained substrate for artificial leather; and a step wherein the obtained artificial leather is brought into close contact with an elastomer sheet stretched in a machine direction by 5 to 40%; the artificial leather is allowed to shrink in the machine direction simultaneously with allowing the elastomer sheet to shrink in the machine direction by relaxing elongation of the elastomer sheet; the artificial leather is heat-treated in shrunk state; and then the artificial leather is peeled off from the elastomer sheet.

First claim

What is claimed is:

1. An elastically stretchable artificial leather consisting of only one entangled fiber body comprising microfine fibers with an average single fiber fineness of 0.9 dtex or less,
wherein the elastically stretchable artificial leather has a wave-like structure comprising the microfine fibers which extends continuously or discontinuously along a machine direction on a cross-section taken in parallel to both a thickness direction and the machine direction, and satisfies (A) and (B):
(A) a stress F 5% at 5% elongation is from 0.1 to 20 N/2.5 cm; and
(B) a ratio of a stress F 20% at 20% elongation and the stress F 5% , F 20% /F 5% , is 5 or more, as determined from a stress-elongation curve in the machine direction obtained according to the method of JIS L 1096 (1999) 8.14.1 A for elastic artificial leather,
wherein the elastically stretchable artificial leather has an apparent density ranging from 0.481 g/cm 3 to 0.80 g/cm 3 .

2. The elastically stretchable artificial leather according to claim 1 , wherein the elastically stretchable artificial leather further satisfies the following requirement (C):
(C) a ratio of a slope S 20% of a tangent line to the curve at 20% elongation and a slope S 5% of a tangent line to the curve at 5% elongation, S 20% /S 5% , is 1.2 or more.

3. The elastically stretchable artificial leather according to claim 1 , wherein the elastically stretchable artificial leather further satisfies the following requirement (D):
(D) a maximum slope S 0 to 5%/max of tangent lines to the curve from zero elongation to 5% elongation is 8 or less.

4. The elastically stretchable artificial leather according to claim 1 , wherein the stress F 20% at 20% elongation is 30 to 200 N/2.5 cm.

5. The elastically stretchable artificial leather according to claim 1 , wherein the elastically stretchable artificial leather further satisfies the following requirement (F):
(F) a stress F 10% at 10% elongation is 5 to 60 N/2.5 cm.

6. The elastically stretchable artificial leather according to claim 1 , wherein the stress F 20% at 20% elongation is 50 to 190 N/2.5 cm.

7. The elastically stretchable artificial leather according to claim 1 , wherein the stress F 20% at 20% elongation is 80 to 180 N/2.5 cm.

8. The elastically stretchable artificial leather according to claim 1 , wherein the ratio F 20% /F 5% , is 20 or more.

9. The elastically stretchable artificial leather according to claim 2 , wherein the ratio S 20% /S 5% , is 5 or more.

10. The elastically stretchable artificial leather according to claim 3 , wherein the maximum slope S 0 to 5%/max of tangent lines to the curve from zero elongation to 5% elongation is 3 or less.

11. The elastically stretchable artificial leather according to claim 5 , wherein the stress F 10% at 10% elongation is 10 to 40 N/2.5 cm.

12. The elastically stretchable artificial leather according to claim 1 , wherein the wave-like structure is a micro wave-like structure.

13. The elastically stretchable artificial leather according to claim 1 , wherein:
a number of pitch in 1 mm interval in the machine direction of the wave-like structure is 2.2 or more; and
an average height of the wave-like structure is 50 to 350 μm.

14. The elastically stretchable artificial leather according to claim 1 , wherein the entangled fiber body comprises an elastic polymer.

15. The elastically stretchable artificial leather according to claim 14 , wherein the elastic polymer is a coagulated product of an aqueous emulsion of polyurethane.

16. The elastically stretchable artificial leather according to claim 1 , wherein the microfine fiber is a non-elastic fiber.

17. The elastically stretchable artificial leather according to claim 16 , wherein the non-elastic fiber is a polyester fiber.

18. The elastically stretchable artificial leather according to claim 1 , wherein the wave-like structure is formed by a shrinking treatment in the machine direction and a heat treatment.

19. The elastically stretchable artificial leather according to claim 1 , wherein the elastically stretchable artificial leather has an elongation factor of 50 or less when calculated from the following formula (1):
Elongation factor=5% circular modulus in machine direction/thickness  (1).

20. The elastically stretchable artificial leather according to claim 1 , wherein a ratio of a load at 30% elongation in the machine direction to a load at 5% elongation in the machine direction is 5 or more.

21. The elastically stretchable artificial leather according to claim 1 , wherein the elastically stretchable artificial leather is produced by a shrinking treatment in the machine direction and a heat treatment.

22. The elastically stretchable artificial leather according to claim 1 , wherein the elastically stretchable artificial leather has an elongation [(deformation by stretching/length before stretching)×100] of 10 to 40% in the machine direction at a load of 40 N/cm.

23. The elastically stretchable artificial leather according to claim 1 , wherein the elastically stretchable artificial leather consisting of only one entangled fiber body comprising microfine fibers with an average single fiber fineness of 0.9 dtex or less.

24. A method of producing the elastically stretchable artificial leather of claim 1 , the method comprising:
forming microfiberizable fibers into a web;
entangling the obtained web to produce an entangled nonwoven fabric;
converting the microfiberizable fibers in the nonwoven fabric to the microfine fibers, thereby producing a substrate for artificial leather;
producing an artificial leather from the obtained substrate for artificial leather;
bringing the obtained artificial leather into close contact with an elastomer sheet stretched in a machine direction by 5 to 40%;
shrinking the artificial leather in the machine direction simultaneously with the elastomer sheet by relaxing elongation of the elastomer sheet to obtain an artificial leather in shrunk state,
heat treating the artificial leather in shrunk state; and
peeling the heat treated artificial leather off from the elastomer sheet thereby producing the elastically stretchable artificial leather.

25. The method according to claim 24 , wherein the method further comprises impregnating an elastic polymer into the entangled nonwoven fabric or the substrate for artificial leather and then coagulating the impregnated elastic polymer.

26. The method according to claim 24 , wherein
the elastomer sheet is stretched in the machine direction by utilizing a difference between inner and outer circumferences of the curved elastomer sheet that is run in contact with a surface of a cylinder, or by utilizing an elongation when compressing the elastomer sheet; and
the elastomer sheet is shrunk in the machine direction by relaxing the stretched state, thereby allowing the artificial leather to shrink in the machine direction.

27. The method according to claim 26 , wherein the elastomer sheet runs along a cylinder while holding the artificial leather therebetween, thereby allowing a surface in contact with the artificial leather to shrink in the machine direction.

28. The method according to claim 27 , wherein an apparent coefficient of dynamic friction between the elastomer sheet and the artificial leather is from 0.8 to 1.7 and a coefficient of dynamic friction between the cyli

Assignees

• Kuraray Co

Inventors

• Fujisawa Michinori
• Maeda Yukio
• Inoue Kazumasa
• Nomura Yasutoshi
• Ashida Tetsuya
• Watanabe Hisaichi

Classifications

• D06N2211/28

  Artificial leather · CPC title

• D06N2209/1635

  Elasticity · CPC title

• D06N3/0036

  Polyester fibres (for elastomeric fibres D06N3/0025) · CPC title

• D06N3/0031

  Retractable fibres; Shrinking of fibres during manufacture · CPC title

• D06N3/0011

  using non-woven fabrics · CPC title