Coating composition for lubricating coating film

Patent metadata

Field	Value
Publication number	US-10294441-B2
Application number	US-201515123266-A
Country	US
Kind code	B2
Filing date	Mar 3, 2015
Priority date	Mar 4, 2014
Publication date	May 21, 2019
Grant date	May 21, 2019

Abstract

A coating composition for a lubricating coating film includes: (A) a phenolic resin; (B) an epoxy resin having an epoxy equivalent weight of 600 to 4000; and (C) at least one type of solid lubricant. The epoxy equivalent weight is generally defined by the number average molecular weight per the number of epoxy groups in a single molecule. The coating composition has a weight ratio of component (A) to the total weight of component (A) and component (B) of at least 50 weight %. A lubricating coating film, formed from the coating composition, has a high level of flexibility on surfaces of various base materials.

First claim

The invention claimed is:

1. A coating composition for a lubricating coating film, the coating composition comprising:
(A) a phenolic resin;
(B) an epoxy resin having an epoxy equivalent weight of 600 to 4000, the epoxy equivalent weight defined by the number average molecular weight per the number of epoxy groups in a single molecule; and
(C) at least one type of solid lubricant;
wherein a weight ratio of component (A) per the total weight of component (A) and component (B) is at least 50 weight %;
wherein component (C) comprises:
(C1) fluororesin comprising polytetrafluoroethylene; and
(C2) one or more types of metal oxide or metal nitride selected from titanium nitride, titanium oxide, aluminum oxide, silicon nitride, silicon dioxide, and mixtures thereof;
wherein the weight % ratio of component (C1) and (C2) is in a range of 60:40 to 85:15; and
wherein the coating composition is free of carbon fibers.

2. The coating composition according to claim 1 , wherein the epoxy equivalent weight of component (B) is 800 to 1200.

3. The coating composition according to claim 1 , wherein the weight ratio of component (A) per the total weight of component (A) and component (B) is at least 60 weight % and not more than 80 weight %.

4. The coating composition according to claim 1 , wherein component (C) further comprises at least one or more types of substances selected from polyethylene resin, polyamide resin, and mixtures thereof.

5. The coating composition according to claim 1 , wherein component (C2) comprises titanium nitride and titanium oxide.

6. The coating composition according to claim 1 , wherein component (C) is contained at an amount of 1 to 200 parts by mass per 100 parts by mass of the total weight of components (A) and (B).

7. A lubricating coating film obtained by curing the coating composition according to claim 1 .

8. A lubricating coating film obtained by curing the coating composition according to claim 1 and having an Erichsen value according to JIS Z 2247 of 8.0 mm or greater when the coating composition is cured with a film thickness of 10 to 20 μm.

9. A sliding member provided with the lubricating coating film according to claim 7 .

10. The sliding member according to claim 9 , wherein the sliding member is a crankshaft, a compressor shaft, a slide bearing, a gear, an oil pump gear, a piston, a piston ring, a piston pin, a gasket, a door lock, a guide rail, a seatbelt buckle, a brake pad, a brake pad clip, a brake shim, a brake insulator, a hinge, a screw, or a pressurization pad.

11. A method for manufacturing a sliding member provided with a base material having a surface and a lubricating coating film formed on the surface, the method comprising the steps of:
applying a coating composition onto the surface of the base material; and
heating the coating composition to form the lubricating coating film on the surface of the base material;
wherein the coating composition is according to claim 1 .

12. The method according to claim 11 , wherein the base material comprises metal.

13. The method according to claim 11 , further comprising the step of pressing or punching the base material having the lubricating coating film formed on the surface.

14. The method according to claim 11 , wherein the sliding member is a crankshaft, a compressor shaft, a slide bearing, a gear, an oil pump gear, a piston, a piston ring, a piston pin, a gasket, a door look, a guide rail, a seatbelt buckle, a brake pad, a brake pad clip, a brake shim, a brake insulator, a hinge, a screw, or a pressurization pad.

15. The method according to claim 12 , further comprising the step of pressing or punching the base material having the lubricating coating film formed on the surface.

16. The coating composition according to claim 1 , wherein component (C2) comprises one or more types of metal oxide or metal nitride selected from aluminum oxide, silicon nitride, silicon dioxide, and mixtures thereof.

17. The coating composition according to claim 1 , further comprising at least one solvent selected from methylethylketone, methyl isobutyl ketone, cyclohexanone, and mixtures thereof.

18. The coating composition according to claim 17 , wherein the solvent is present in a range of 10 to 800 parts by weight based on 100 parts by weight of the total weight of components (A) and (B).

19. The coating composition according to claim 18 , further comprising at least one pigment, wherein the pigment comprises carbon black.

20. The coating composition according to claim 19 , wherein the pigment is present in a range of 0.1 to 5 weight % based on the total weight % of the composition.

Assignees

• Dow Corning Toray Co Ltd

Inventors

• Sasaki Takahiko
• Yamaguchi Tetsuji

Classifications

• C09D163/00

  Coating compositions based on epoxy resins; Coating compositions based on derivatives of epoxy resins · CPC title

• C10N2050/02

  dissolved or suspended in a carrier which subsequently evaporates to leave a lubricant coating · CPC title

• C08K2003/2241

  Titanium dioxide · CPC title

• C10M2201/0663

  used as base material · CPC title

• C09D7/61

  inorganic · CPC title