Catalyst component for olefin polymerization, preparation method therefor and catalyst thereof

Patent metadata

Field	Value
Publication number	US-10150822-B2
Application number	US-201214235340-A
Country	US
Kind code	B2
Filing date	Jul 24, 2012
Priority date	Jul 26, 2011
Publication date	Dec 11, 2018
Grant date	Dec 11, 2018

Abstract

A catalyst component (A) for olefin polymerization is prepared by contacting a solid component (a) containing magnesium, titanium, halogen and an internal electron donor compound with an organosilicon compound (b), wherein the organosilicon compound (b) is one or more selected from a Si—H functional group containing chainlike polysiloxane (b1) represented by formula (I x ), a cyclic polysiloxane (b2) represented by formula (I y ) and a Si—H functional group containing organosilicon compound (b3) represented by formula (I z ). In addition, a process for preparing the catalyst component and the corresponding catalyst is described. The catalyst component and its catalyst have high catalytic activity, good hydrogen response, and good stereospecificity, the catalyst can release its activity more evenly, and the obtained polymer has significantly increased bulk density. The definitions of R 1 to R 10 , n and z in the formulae (I x ), (l y ) and (I z ) are as described in the specification.

First claim

The invention claimed is:

1. A catalyst component for olefin polymerization, wherein the catalyst component is prepared by contacting a solid component containing magnesium, titanium, halogen and an internal electron donor compound with an organosilicon compound,
wherein the organosilicon compound is one or more selected from the group consisting of a Si—H functional group containing chainlike polysiloxane represented by formula (I x ), and a Si—H functional group containing organosilicon compound represented by formula (I z ):

in the formula (I x ), R 1 -R 7 , which are identical or different, independently of each other represent one selected from the group consisting of a linear or branched alkyl group having 1 to 12 carbon atoms, a cycloalkyl group having 3 to 10 carbon atoms, and an alkaryl group or a substituted or unsubstituted aryl group having 6 to 20 carbon atoms; the degree of polymerization n is an integer of 2 to 100;
HSiR 9 z R 10 3-z   (I z )

in the formula (I z ), R 9 and R 10 , which are identical or different, independently of each other represent one selected from the group consisting of a hydrogen atom, a halogen atom, a linear or branched saturated alkyl group having 1 to 12 carbon atoms, a cycloalkyl group having 3 to 10 carbon atoms, and an alkaryl group or a substituted or unsubstituted aryl group having 6 to 20 carbon atoms; R 9 and R 10 are not simultaneously hydrogen; z is an integer of 0 to 3,
wherein the solid component is prepared by suspending the magnesium compound in an inert diluent to form a suspension and then bringing the suspension into contact with the titanium compound and the internal electron donor, and
wherein the catalyst component a content of titanium atoms is 1.0-8.0 wt %, a content of magnesium atoms is 10-70 wt %, a content of a halogen atoms is 20-86 wt %, a content of silicon atoms is 0.01-0.5 wt %, and a content of the internal electron donor compound is 2-30 wt %.

2. The catalyst component according to claim 1 , wherein an alkoxy magnesium compound represented by formula (II) or an alcohol adduct of the alkoxy magnesium compound represented by formula (II) is used as the magnesium compound for preparing the solid component,
Mg(OR 11 ) 2-y (OR 12 ) y   (II)

in the formula (II), R 11 and R 12 , which are identical or different, independently of each other represent a linear or branched alkyl group having 1 to 8 carbon atoms, and 0≤y≤2.

3. The catalyst component according to claim 1 , wherein the titanium compound used for preparing the solid component is a compound represented by formula (III),
TiX m (OR″) 4-m   (III)

in the formula (III), X is a halogen atom, R″ is a hydrocarbon group having 1 to 20 carbon atoms, m is an integer of 0 to 4; wherein the halogen is chlorine, bromine or iodine.

4. The catalyst component according to claim 3 , wherein the titanium compound is titanium tetrachloride.

5. The catalyst component according to claim 1 , wherein the internal electron donor compound used for preparing the solid component is one or more compound represented by formula (IV),

in the formula (IV), R 13 and R 14 , which are identical or different, independently of each other represent one selected from the group consisting of a linear or branched alkyl group having 1 to 12 carbon atoms, a cycloalkyl group having 3 to 10 carbon atoms, and an alkaryl group or a substituted or unsubstituted aryl group having 6 to 20 carbon atoms; R 15 , R 16 , R 17 and R 18 are all hydrogen; or three of them are hydrogen and the other one is a group selected from the group consisting of a halogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms and a linear or branched alkoxy group having 1 to 4 carbon atoms.

6. The catalyst component according to claim 5 , wherein the internal electron donor is at least one selected from the grow consisting of diethyl phthalate, di-n-butyl phthalate, diisobutyl phthalate, di-n-octyl phthalate, and diisooctyl phthalate.

7. The catalyst component according to claim 1 , wherein the organosilicon compound is a Si—H functional group containing organosilicon compound represented by the formula (I z ), which is at least one selected from the group consisting of triethylsilane, tripropylsilane, tributyl silane, tripentyl silane, trihexyl silane, triisopropylsilyl, triphenyl silane, diphenyl silane, dipropyl silane, dibutyl silane, dipentyl silane, dihexyl silane, diisopropyl silane, diisobutyl silane, diisopentyl silane, and diisohexyl silane.

8. The catalyst component according to claim 1 , wherein the organosilicon compound is a chainlike polysiloxane represented by the formula (I x ), wherein R 1 is a linear or branched alkyl group having 1 to 6 carbon atoms, a cycloalkyl group or an aryl group, and R 2 -R 7 are methyl.

9. The catalyst component according to claim 8 , wherein the chainlike polysiloxane represented by the formula (I x ) is at least one selected from the group consisting of 1,1,1,3,5,7,7,7-octamethyltetrasiloxane (n=2), polymethylhydrosiloxane, polyethylhydrosiloxane, polyphenylhydrosiloxane, and polycyclohexylhydrosiloxane.

10. The catalyst component according to claim 1 , wherein in the catalyst component, the content of titanium atoms is 1.6-4.0 wt %; the content of magnesium atoms is 15-40 wt %; the content of halogen atoms is 36-80%; the content of silicon atoms is 0.02-0.5 wt %; the content of the internal electron donor compound is 3-20 wt %.

11. A process for preparing the catalyst component according to claim 1 , the process comprising contacting the organosilicon compound with the solid component as has been already prepared into reaction.

12. A process for preparing the catalyst component according to claim 1 , wherein the organosilicon compound is added to effect the reaction during the preparation of the solid component which, in time sequence, comprises the following three steps: forming mother liquor, titanium treatment and washing;
wherein the step of forming mother liquor comprises suspending a magnesium compound in an inert diluent to form a suspension, and then bringing the suspension into contact with a titanium compound and an internal electron donor to obtain a solid dispersion system, which is called as a mother liquor;
the titanium treatment step comprises filtering the mother liquor, and suspending the resulting solid substance in a titanium tetrachloride-containing solution to effect treatment; and
the washing step comprises filtering and washing the solid substance obtained in the preceding step.

13. The process according to claim 12 , wherein the organosilicon compound is added after the step of forming the mother liquor and before the titanium treatment step during the preparation of the solid component.

14. The process according to claim 12 , wherein the organosilicon compound is added in the titanium treatment step during the preparation of the solid component.

15. The process according to claim 12 , wherein the organosilicon compound is added in the washing step after the titanium treatment step during the preparation of the solid component.

16. A catalyst for olefin polymerization, which comprises the catalyst component according to claim 1 , and further comprises an organoaluminum compound as cocatalyst, and optionally an external electron donor compound.

17. The catalyst according to claim 16 , wherein the or

Assignees

• Zhou Qilong
• Tan Zhong
• Xu Xiudong
• Yan Lian
• Song Weiwei
• Li Fengkui
• Yin Shanshan
• Yu Jinhua
• China Petroleum & Chem Corp
• Beijing Res Inst Chemical Ind China Petroleum & Chemical Corp

Inventors

• Zhou Qilong
• Tan Zhong
• Xu Xiudong
• Yan Li'An
• Song Weiwei
• Li Fengkui
• Yin Shanshan
• Yu Jinhua

Classifications

• C08F10/00

  Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond · CPC title

• C08F4/6465 Primary

  containing silicium · CPC title

• C08F110/08 Primary

  Butenes · CPC title

• C08F2500/15

  Isotactic · CPC title

• C08F2500/12

  Melt flow index or melt flow ratio · CPC title