Random propylene-ethylene copolymers and process for their preparation

Patent metadata

Field	Value
Publication number	US-9676883-B2
Application number	US-201515309042-A
Country	US
Kind code	B2
Filing date	May 6, 2015
Priority date	May 6, 2014
Publication date	Jun 13, 2017
Grant date	Jun 13, 2017

Abstract

The present disclosure relates to propylene-ethylene copolymers comprising an ethylene content of 0.1-10% by weight, a molecular weight distribution (MWD), expressed in terms of Mw/Mn, of greater than 3.0 and a xylene soluble (XS) fraction content defined by values that fall below the line given by the equation XS=1.0296·e 0.435C2 . The propylene-ethylene copolymers advantageously exhibit high transparency and low melting temperatures.

First claim

What is claimed is:

1. A propylene-ethylene copolymer comprising:
an ethylene content of 0.1 to less than 10% by weight;
a molecular weight distribution (MWD), expressed in terms of Mw/Mn, of greater than 3;
a melt flow rate (MFR 230° C. 2.16 kg) for the reactor grade copolymers of 0.5-45 g/10 min;
an absence of 2,1 propylene insertions;
a xylene soluble fraction (XS) content and an ethylene content (C2) defined by values that fall below the line given by the equation:
XS= 1.0296· e 0.435C2

where:
XS=% by weight of the fraction soluble in xylene at 25° C.; and
C2=% by weight of ethylene units in the copolymer determined via NMR.

2. The propylene/ethylene copolymer of claim 1 where the content of xylene soluble fraction (XS) and ethylene content (C2) of the copolymer are such that the point defined by the content values falls below the line given by the equation:
XS= 0.969· e 0.435C2

where XS=% by weight of the fraction soluble in xylene at 25° C.; and
C2=% by weight of ethylene units in the copolymer determined via NMR.

3. The propylene/ethylene copolymer of claim 1 , where the ethylene content ranges from 0.1-5% wt.

4. The propylene/ethylene copolymer of claim 3 , where the ethylene content ranges from 1-5% wt.

5. The propylene-ethylene copolymer of claim 1 , where the catalytic residues comprise less than 5 ppm of Ti.

6. The propylene-ethylene copolymer of claim 1 , where the product of the comonomer reactivity ratio r1·r2 ranges from 1.5-3.

7. The propylene-ethylene copolymer of claim 1 , where the molecular weight distribution (MWD), as determined via gel permeation chromatography (GPC), is higher than 3.5.

8. The propylene-ethylene copolymer of claim 1 , where the content of propylene units in the form of isotactic triads (mm %) as determined via C 13 NMR, is higher than 98.3%.

9. The propylene-ethylene copolymer of claim 1 , wherein the melt flow rate (MFR, 230° C. 216 kg) of the reactor grade copolymers ranges from 0.2-45.

10. An article comprising the propylene-ethylene copolymer of claim 1 .

11. A process for the preparation of the propylene-ethylene copolymer of claim 1 , comprising polymerizing propylene with ethylene in the presence of a catalyst comprising the product of the reaction between:
(i) a solid catalyst component comprising Ti, Mg, Cl, and an internal electron donor compound comprising 0.1-50% wt. of Bi with respect to the total weight of the solid catalyst component;
(ii) an alkylaluminum compound and,
(iii) an external electron-donor compound.

12. The process of claim 2 , where the external electron donor compound is selected from silicon compounds of the formula (R 6 ) a (R 7 ) b Si(OR 8 ) c , where a is 1, b is 1, c is 2, at least one of R 6 and R 7 is selected from branched alkyl, cycloalkyl or aryl groups with 3-10 carbon atoms optionally containing heteroatoms and R 8 is a C 1 -C 10 alkyl group.

13. The process of claim 11 , where the internal electron donor compound is selected from alkyl and aryl esters of substituted aromatic polycarboxylic acids.

14. The process of claim 12 , where the external electron donor compound is dicyclopentyldimethoxysilane.

15. The process of claim 11 , where the process carried out in gas-phase in a reactor comprising at least two interconnected polymerization zones.

Assignees

• Basell Poliolefine Italia Srl

Inventors

• Piemontesi Fabrizio
• Cathelin Caroline
• Guidotti Simona
• Liguori Dario
• Morini Giampiero
• Tartari Davide
• Vitale Gianni

Classifications

• C08F210/16 Primary

  Copolymers of ethene with alpha-alkenes, e.g. EP rubbers · CPC title

• C08F2500/12

  Melt flow index or melt flow ratio · CPC title

• C08F210/06 Primary

  Propene · CPC title

• C08F2500/26

  Use as polymer for film forming · CPC title

• C08F2500/04

  Broad molecular weight distribution, i.e. Mw/Mn > 6 · CPC title