Method of high-temperature nickel-based bolts based on damage tolerance theory

Patent metadata

Field	Value
Publication number	US-10132732-B2
Application number	US-201615528241-A
Country	US
Kind code	B2
Filing date	Jun 1, 2016
Priority date	May 25, 2016
Publication date	Nov 20, 2018
Grant date	Nov 20, 2018

Abstract

The invention relates to a design method of high-temperature nickel-based bolts based on damage tolerance theory, comprising the following steps: S 1 : acquiring operating parameters for the design; S 2 : selecting a material for bolts; S 3 : acquiring mechanical properties of the materials; S 4 : determining a pretension stress σ p of a single bolt; S 5 : determining the service stress σ s under the steady state; S 6 : determining the number n, the effective cross-section area A and the distribution of bolts; S 7 : determining a maximum allowable crack dimension; S 8 : calculating the maximum allowable service stress σ th using the crack propagation threshold K th at the design temperature; S 9 : comparing the service stress σ s and the maximum allowable service stress σ th , if σ s is smaller than σ th , then the bolts are safe in the design life; otherwise, return to step S 4 and reduce the pretension stress σ p .

First claim

The invention claimed is:

1. A design method for generating and using a configuration of high-temperature nickel-based bolts for fastening a material included as part of an engineering design, said method comprising the following steps:
S1: obtaining a first configuration of bolts, wherein the first configuration of bolts is obtained by—
S1.1: acquiring operating parameters for the engineering design, the parameters including: a design temperature T; an environmental medium; a design life; a designation, structure and size of the material to be fastened; and a force P needed to fulfill a fastening function between the first configuration of bolts and the material to be fastened;
S1.2: selecting a bolt material for the bolts of the first configuration according to the design temperature T and the environmental medium in step S1.1;
S1.3: acquiring mechanical properties of the material of the bolts in the first configuration, including: linear expansion coefficients α b and α v of the bolt material and the material to be fastened, respectively; elastic modulus E, tensile property, stress relaxation property, and crack propagation threshold K th of the bolt material at the design temperature;
S1.4: determining a first pretension stress σ p1 for a single bolt from the first configuration of bolts according to the bolt material selected in step S1.2, wherein the first pretension stress σ p1 is determined as σ p1 =0.5 σ y , where σ y represents a yield strength of the bolt material;
S1.5: determining a residual stress or after stress relaxation in the design life at the design temperature T in step S1.1, wherein σ r is obtained by referring to a database of material properties, or by extrapolating or interpolating a relaxation curve obtained by a high-temperature relaxation test and plotted; calculating a thermal stress σ t under steady state according to σ t =E(α v −α b )T; and determining a first service stress σ s1 under steady state, wherein σ s1 is the smaller one between σ r and the larger one of σ p1 +σ t and σ p1 ;
S1.6: determining a number and an effective cross-section area A of the bolts in the first configuration of bolts;
S1.7: determining a maximum allowable crack dimension for any one of the bolts from the first configuration of bolts according to a specification for nondestructive examination on the bolts;
S1.8: calculating a maximum allowable service stress σ th using the crack propagation threshold K th at the design temperature T by assuming that a growth direction of the crack determined in step S1.7 is perpendicular to a loaded direction of the bolt, wherein the σ th can be represented by σ th =K th /(√{square root over (πa)} F I ), where F I is a dimensionless quantity obtained by referring to a handbook of stress intensity factors or by finite element calculation, and a is a length of the crack;
S1.9: comparing the first service stress σ s1 of step S1.5 and the maximum allowable service stress σ th of step S1.8;

S2: determining whether the first configuration of bolts can be used in the engineering design to fasten the material to be fastened, wherein said determining step is based on the comparison of service stresses in step S1.9;
S3: generating a second configuration of bolts for the engineering design, wherein the second configuration of bolts is generated by—
S3.1: selecting a second pretension stress σ p2 for a single bolt from the second configuration of bolts according to the bolt material selected in step S1.2, wherein the second pretension stress σ p2 is less than the first pretension stress σ p1 ;
S3.2: determining a second service stress σ s2 under steady state, wherein σ s2 is the smaller one between σ r and the larger one of σ p2 +σ t and σ p2 ;
S3.3: determining a number and an effective cross-section area A of the bolts in the second configuration of bolts;
S3.4: comparing the second service stress σ s2 and the maximum allowable service stress σ th determined in step S1.8, wherein if σ s2 is less than σ th , then the second configuration of bolts is available for use in the engineering design;

S4: selecting the second configuration of bolts for use in the engineering design to fasten the material to be fastened, wherein the second configuration of bolts has a higher fracture resistance than the first configuration of bolts; and
S5: fastening the material to be fastened using the bolts from the second configuration of bolts selected in step S4.

2. The method of claim 1 , wherein the linear expansion coefficients are obtained using a thermal dilatometer; the elastic modulus E is obtained using a dynamic thermomechanical analysis; the tensile property is obtained by tensile tests at the design temperature; the stress relaxation property is obtained by relaxation testing at the design temperature; crack propagation threshold K th at the design temperature is obtained as follows: crack growth tests are carried out using compact tensile specimens to obtain a curve of initial stress intensity factor vs. crack initiation time, and the curve is extrapolated or interpolated to obtain the crack propagation threshold K th in the design life.

3. The method of claim 2 , wherein crack propagation threshold K th in the design life is obtained from short-time crack growth tests at the design temperature, wherein the curve of initial stress intensity factor vs. crack initiation time can be fitted using K=Bt i φ , where K is stress intensity factor, t i represents crack initiation time, B and φ are material parameters obtained by fitting the test results, and wherein the stress intensity factor K calculated by putting the design life into the fitted equation is the crack propagation threshold K th .

4. The method of claim 1 , wherein in step S1.7, the maximum allowable crack dimension is determined by taking into consideration the following factors: the minimum detectable size of defects by the nondestructive examination technique, the examination cost and the manufacture cost.

5. The method of claim 4 , wherein the nondestructive examination technique includes visual examination, magnetic powder examination and ray examination.

6. The method of claim 1 , wherein the material to be fastened comprises a steam valve for a steam turbine.

7. The method of claim 6 , wherein the bolts comprise valve bolts.

8. The method of claim 1 , wherein in step S1.3, the mechanical properties of the materials are obtained by referring to a database of material properties; or by material testing.

9. The method of claim 1 , wherein in step S1.6, the number and the effective cross-section area A of the bolts in the first configuration of bolts are designed according to P=nAσ s using the first service stress σ s1 obtained in step S1.5 in view of the size of the sealing face and the force P.

Assignees

• Univ East China Science & Tech
• Shanghai Turbine Company Ltd

Inventors

• Xuan Fuzhen
• Tan Jianping
• Gong Jianguo
• Liu Xia

Classifications

• G01M99/00

  Subject matter not provided for in other groups of this subclass · CPC title

• F16B1/00

  Devices for securing together, or preventing relative movement between, constructional elements or machine parts · CPC title

• G01N3/18 Primary

  Performing tests at high or low temperatures · CPC title

• G01N33/20 Primary

  Metals · CPC title

• B21H1/00

  Making articles shaped as bodies of revolution (rolling tubes B21B17/00 - B21B25/00) · CPC title