Polarity-enhanced ductile polymer fibers for concrete micro-reinforcement

Patent metadata

Field	Value
Publication number	US-10131579-B2
Application number	US-201514983771-A
Country	US
Kind code	B2
Filing date	Dec 30, 2015
Priority date	Dec 30, 2015
Publication date	Nov 20, 2018
Grant date	Nov 20, 2018

Abstract

Cementitious mixtures, such as concrete, can be reinforced by adding one or more ductile but strong synthetic copolymer microfibers to the mixture. The synthetic copolymer microfibers improve local energy dissipation and bear load, taking the driving force for crack propagation away from the crack tip and thus reinforcing the cementitious mixture against the propagation of microscopic cracks. The resulting mixtures have an improved balance of strength properties.

First claim

What is claimed is:

1. A cementitious mixture comprising:
a mineral cement; and
a first population of microfibers formed from a first synthetic copolymer and a second population of microfibers formed from a second synthetic copolymer, different from said first copolymer, wherein both the first and second synthetic copolymers comprise from about 1 mol % to about 25 mol % of one of ethylene or propylene monomeric units, and from about 75 mol % to about 99.5 mol % of the other of ethylene or propylene monomeric units.

2. The cementitious mixture of claim 1 , which is a wet or a dry mixture.

3. The cementitious mixture of claim 1 , which is a cured concrete.

4. The cementitious mixture of claim 1 , wherein the microfibers have exposed polar groups having chemical affinity with minerals present in curing or cured cementitious mixtures.

5. The cementitious mixture of claim 1 , wherein at least one of the microfibers is lightly cross-linked by being subjected to radiation.

6. The cementitious mixture of claim 1 , wherein said microfibers have diameters of less than about 1 mm and aspect ratios from about 5:1 to about 50:1.

7. The cementitious mixture of claim 1 , further comprising one or more of sand, fly ash, fine and/or coarse aggregates, blast furnace slag, pozzolans, fumed silica, wetting agents, air entrainers, air detrainers, corrosion inhibitors, set accelerators or set retarders.

8. A process for reinforcing a cementitious matrix comprising adding polymeric microfibers to a mineral cement to form a cementitious premixture, wherein the polymeric microfibers comprise a first population of microfibers formed from a first synthetic copolymer and a second population of microfibers formed from a second synthetic copolymer, different from said first copolymer, and wherein the first and second synthetic copolymers both comprise from about 1 mol % to about 25 mol % of one of ethylene or propylene monomeric units, and from about 75 mol % to about 99.5 mol % of the other of ethylene or propylene monomeric units.

9. The process of claim 8 , wherein the microfibers have exposed polar groups having chemical affinity with minerals present in curing cementitious mixtures.

10. The process of claim 8 , wherein at least one of the microfibers is lightly cross-linked by being subjected to radiation.

11. The process of claim 8 , wherein said microfibers have diameters of less than about 1 mm and aspect ratios from about 5:1 to about 50:1.

12. The process of claim 8 , further comprising adding one or more of sand, fly ash, fine and/or coarse aggregates, blast furnace slag, pozzolans, fumed silica, wetting agents, air entrainers, air detrainers, corrosion inhibitors, set accelerators or set retarders to said cementitious premixture.

13. The process of claim 8 , wherein the cementitious premixture is a wet or a dry mixture.

Assignees

• Furmanski Jevan
• Exxonmobil Res & Eng Co

Inventors

• Furmanski Jevan

Classifications

• C04B16/0625

  Polyalkenes, e.g. polyethylene · CPC title

• C04B16/0633 Primary

  Polypropylene · CPC title

• C04B16/0616

  from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds · CPC title

• C04B28/02 Primary

  containing hydraulic cements other than calcium sulfates · CPC title

• C04B20/0052

  Mixtures of fibres of different physical characteristics, e.g. different lengths · CPC title