Composition for electric wire coating material, insulated electric wire, and wire harness

Patent metadata

Field	Value
Publication number	US-10102940-B2
Application number	US-201515504304-A
Country	US
Kind code	B2
Filing date	Aug 3, 2015
Priority date	Aug 22, 2014
Publication date	Oct 16, 2018
Grant date	Oct 16, 2018

Abstract

Provided is an insulated electric wire, a wire harness, and a composition for an electric wire coating material with which the amount of a filler, which is the flame retardant, can be reduced as much as possible without using electron beam crosslinking, the composition having a high heat resistance, a high gel fraction, flexibility, and good workability of assembling a wire harness. An electric wire coating material is made of a composition comprising (A) a silane-grafted polyolefin obtained by grafting a silane coupling agent onto a polyolefin having a density of 0.855 to 0.885 g/cm 3 , (B) an unmodified polyolefin having a density of 0.890 to 0.955 g/cm 3 , (C) a modified polyolefin modified by one or more functional groups selected from a carboxylic acid group, an acid anhydride group, an amino group, an acrylic group, a methacrylic group, and an epoxy group, (D) a bromine-based flame retardant and antimony trioxide, (E) a crosslinking catalyst batch, (F) zinc oxide and an imidazole-based compound, or zinc sulfide, (G) an antioxidant, (H) a metal deactivator, and (I) a lubricant.

First claim

The invention claimed is:

1. A composition for an electric wire coating material comprising:
(A) a silane-grafted polyolefin obtained by grafting a silane coupling agent onto a polyolefin having a density of 0.855 to 0.885 g/cm 3 , wherein the polyolefin before silane grafting has a density of 0.865 to 0.885 g/cm 3 , a degree of crystallinity of 10 to 25%, a melt flow rate at 190° C. under a load of 2.16 kg of 0.5 to 5 g/10 minutes, a Shore A hardness of 55 to 80, a flexural modulus of 3 to 50 MPa, and a gel fraction of the silane-grafted polyolefin is 80 to 95%;
(B) an unmodified polyolefin having a density of 0.890 to 0.955 g/cm 3 , a melt flow rate at 190° C. under a load of 2.16 kg of 0.5 to 5 g/10 minutes, a flexural modulus of 50 to 1000 MPa, and a density of 0.910 to 0.930 g/cm 3 ;
(C) a modified polyolefin modified by one or more functional groups selected from a carboxylic acid group, an acid anhydride group, an amino group, an acrylic group, a methacrylic group, and an epoxy group;
(D) a bromine-based flame retardant and antimony trioxide, the bromine-based flame retardant having a melting point of 200° C. or more, or being either ethylene bis(tetrabromophthalimide) or ethylene bis(pentabromophenyl);
(E) a crosslinking catalyst;
(F) zinc oxide and an imidazole-based compound, or zinc sulfide;
(G) an antioxidant comprised of hindered phenol having a melting point of 200° C. or more;
(H) a metal deactivator comprised of a salicylic acid derivative; and
(I) a lubricant comprised of one or more selected from derivatives of erucic acid, oleic acid, and stearic acid, or polyethylene-based paraffin wax.

2. The composition for an electric wire coating material according to claim 1 , wherein the composition contains:
the (A) silane-grafted polyolefin in an amount of 30 to 90 parts by mass,
the (B) unmodified polyolefin and the (C) modified polyolefin in an amount of 10 to 70 parts by mass in total,
with respect to 100 parts by mass of the total of the (A), (B), and (C),
the (D) bromine-based flame retardant and antimony trioxide in an amount of 10 to 70 parts by mass in total,
as the (E) crosslinking catalyst, a crosslinking catalyst batch in an amount of 2 to 20 parts by mass, the crosslinking catalyst batch comprising a dispersion containing the crosslinking catalyst in an amount of 0.5 to 5 parts by mass with respect to 100 parts by mass of a polyolefin,
the (F) zinc oxide and imidazole-based compound each in an amount of 1 to 15 parts by mass, or zinc sulfide in an amount of 1 to 15 parts by mass,
the (G) antioxidant in an amount of 1 to 10 parts by mass,
the (H) metal deactivator in an amount of 1 to 10 parts by mass, and
the (I) lubricant in an amount of 1 to 10 parts by mass.

3. The composition for an electric wire coating material according to claim 1 , wherein:
the silane-grafted polyolefin and the unmodified polyolefin are one or more selected from very-low-density polyethylene, linear low-density polyethylene, and low-density polyethylene.

4. An insulated electric wire comprising an electric wire coating material obtained by subjecting the composition for an electric wire coating material according to claim 1 to water crosslinking.

5. The insulated electric wire according to claim 4 , wherein:
the composition for an electric wire coating material according to claim 1 comprises:
an a component containing the (A) silane-grafted polyolefin;
a b component containing the (B) unmodified polyolefin, the (C) modified polyolefin, the (D) bromine-based flame retardant and antimony trioxide, the (F) zinc oxide and imidazole-based compound, or zinc sulfide, the (G) antioxidant, the (H) metal deactivator, and the (I) lubricant; and
a c component containing the crosslinking catalyst batch of the (E) crosslinking catalyst,
the a component, the b component, and the c component being mixed and molded as the electrical wire coating material, and the molded electrical wire coating material being subjected to water crosslinking.

6. A wire harness comprising:
the insulated electric wire according to claim 4 .

Assignees

• Autonetworks Technologies Ltd
• Sumitomo Wiring Systems
• Sumitomo Electric Industries

Inventors

• Shimada Tatsuya
• Nakano Seigou

Classifications

• C08K13/02

  Organic and inorganic ingredients · CPC title

• C08K3/22

  of metals · CPC title

• C08F230/08

  containing silicon · CPC title

• C09D123/06

  Polyethylene · CPC title

• C08K5/03

  aromatic {, e.g. C6H5-CH2-Cl} · CPC title