Seal compositions, methods, and structures for planar solid oxide fuel cells

Patent metadata

Field	Value
Publication number	US-10087103-B2
Application number	US-201615357694-A
Country	US
Kind code	B2
Filing date	Nov 21, 2016
Priority date	Nov 12, 2008
Publication date	Oct 2, 2018
Grant date	Oct 2, 2018

Abstract

A seal composition includes a first alkaline earth metal oxide, a second alkaline earth metal oxide which is different from the first alkaline earth metal oxide, aluminum oxide, and silica in an amount such that molar percent of silica in the composition is at least five molar percent greater than two times a combined molar percent of the first alkaline earth metal oxide and the second alkaline earth metal oxide. The composition is substantially free of phosphorus oxide. The seal composition forms a glass ceramic seal which includes silica containing glass cores located in a crystalline matrix comprising barium aluminosilicate, and calcium aluminosilicate crystals located in the glass cores.

First claim

What is claimed is:

1. A seal composition comprising:
a first alkaline earth metal oxide;
a second alkaline earth metal oxide, wherein the second alkaline earth metal oxide is different from the first alkaline earth metal oxide;
aluminum oxide; and
silica in an amount such that molar percent of silica in the composition is at least five molar percent greater than two times a combined molar percent of the first alkaline earth metal oxide and the second alkaline earth metal oxide;
wherein the composition is substantially free of phosphorus oxide.

2. The composition of claim 1 , wherein the composition comprises:
between about 5 molar percent and about 25 molar percent of the first alkaline earth metal oxide;
between about 2 molar percent and about 25 molar percent of the second alkaline earth metal oxide;
less than 6 molar percent boron oxide;
between about 5 molar percent and about 15 molar percent of the aluminum oxide; and
between about 45 molar percent and about 65 molar percent of the silica.

3. The composition of claim 2 , wherein the first alkaline earth metal oxide comprises at least 80 molar percent calcium oxide and the second alkaline earth metal oxide comprises at least 80 molar percent barium oxide.

4. The composition of claim 2 , wherein a molar ratio of the first alkaline earth metal oxide to the second alkaline earth metal oxide in the composition is between about 5:1 and about 1:5.

5. The composition of claim 2 , wherein the composition comprises zero to about 0.5 molar percent of phosphorus oxide and 1.5 to 6 molar percent boron oxide.

6. The composition of claim 5 , wherein the composition consists of barium oxide, calcium oxide, alumina, boron oxide, potassium oxide and silica, and the composition is substantially free of other glass formers and easily reducible species.

7. The composition of claim 6 , wherein the composition comprises zero to about 0.5 molar percent of arsenic oxide, lead oxide or zinc oxide.

8. The composition of claim 2 , wherein the composition further comprises less than 5 molar percent of at least one of a fluxing agent or a bulk nucleation agent.

9. The composition of claim 1 , wherein the composition is in glass powder form.

10. The composition of claim 1 , wherein the composition comprises a glass ceramic seal located in a fuel cell stack.

Assignees

• Bloom Energy Corp

Inventors

• Kumar Ananda H
• Nguyen Dien
• Janousek Martin
• Armstrong Tad

Classifications

• H01M8/0282

  Inorganic material · CPC title

• H01M2008/1293

  Fuel cells with solid oxide electrolytes · CPC title

• C03C2205/00

  Compositions applicable for the manufacture of vitreous enamels or glazes · CPC title

• H01M8/0286

  Processes for forming seals · CPC title

• C03C10/0036

  containing SiO2, Al2O3 and a divalent metal oxide as main constituents · CPC title