Seal compositions, methods, and structures for planar solid oxide fuel cells

Patent metadata

Field	Value
Publication number	US-9531015-B2
Application number	US-201614992203-A
Country	US
Kind code	B2
Filing date	Jan 11, 2016
Priority date	Nov 12, 2008
Publication date	Dec 27, 2016
Grant date	Dec 27, 2016

Abstract

A seal composition includes a first alkaline earth metal oxide, a second alkaline earth metal oxide which is different from the first alkaline earth metal oxide, aluminum oxide, and silica in an amount such that molar percent of silica in the composition is at least five molar percent greater than two times a combined molar percent of the first alkaline earth metal oxide and the second alkaline earth metal oxide. The composition is substantially free of boron oxide and phosphorus oxide. The seal composition forms a glass ceramic seal which includes silica containing glass cores located in a crystalline matrix comprising barium aluminosilicate, and calcium aluminosilicate crystals located in the glass cores.

First claim

What is claimed is:

1. A method of forming a seal comprising:
providing a substantially boron oxide and phosphorus oxide free glass powder composition comprising a first alkaline earth metal oxide, a second alkaline earth metal oxide, wherein the second alkaline earth metal oxide is different from the first alkaline earth metal oxide, aluminum oxide, and silica;
heating the composition to sinter glass particles of the glass powder;
continuing heating the composition to initiate crystallization from surfaces of the glass particles and to form a crystalline matrix comprising a first ternary aluminosilicate surrounding glass cores; and
further continuing heating the composition to form a glass ceramic seal comprising second ternary aluminosilicate crystals in the glass cores enclosed by the crystalline matrix, wherein the second ternary aluminosilicate has a different composition than the first ternary aluminosilicate crystals.

2. The method of claim 1 , wherein the step of providing the composition comprises depositing the composition on a surface of a component of a fuel cell stack.

3. The method of claim 2 , wherein the composition is provided as a paste or as a green tape on a surface of an interconnect in a solid oxide fuel cell stack.

4. The method of claim 2 , wherein silica is present in the provided composition in an amount such that molar percent of silica in the composition is at least five molar percent greater than two times a combined molar percent of the first alkaline earth metal oxide and the second alkaline earth metal oxide.

5. The method of claim 4 , wherein the provided composition comprises:
between about 5 mole percent and about 25 mole percent of the first alkaline earth metal oxide;
between about 2 mole percent and about 25 mole percent of the second alkaline earth metal oxide;
between about 5 mole percent and about 15 mole percent of the aluminum oxide;
between about 45 mole percent and about 65 mole percent of the silica;
zero to about 0.5 molar percent of boron oxide or phosphorus oxide; and
substantially no other glass formers and easily reducible species.

6. The method of claim 5 , wherein the first alkaline earth metal oxide comprises at least 80 molar percent calcium oxide and the second alkaline earth metal oxide comprises at least 80 molar percent barium oxide.

7. The method of claim 5 , wherein:
the crystalline matrix is barium rich and comprises barium aluminosilicate crystals;
the crystalline matrix encloses barium lean glass cores;
the glass cores comprise silica containing glass areas and calcium aluminosilicate crystals in the glass areas.

8. The method of claim 7 , wherein the glass particles sinter below the glass softening point, the barium aluminosilicate crystals crystallize on the surfaces of the glass particles to form the crystalline matrix and the calcium aluminosilicate crystals form in the glass cores after formation of the crystalline matrix.

9. The method of claim 1 , wherein the step of heating the composition comprises heating at a rate of between about 3° C. per minute to about 10° C. per minute to a temperature between about 900° C. and about 1000° C.

Assignees

• Bloom Energy Corp

Inventors

• Kumar Ananda H
• Nguyen Dien
• Janousek Martin
• Armstrong Tad

Classifications

• H01M8/1246

  the electrolyte consisting of oxides · CPC title

• Y02E60/50

  Fuel cells · CPC title

• H01M8/0282

  Inorganic material · CPC title

• C03C8/02 Primary

  Frit compositions, i.e. in a powdered or comminuted form · CPC title

• H01M8/0286 Primary

  Processes for forming seals · CPC title