Heat-shrinkable polyester film and package

Patent metadata

Field	Value
Publication number	US-10035335-B2
Application number	US-201515300774-A
Country	US
Kind code	B2
Filing date	Mar 3, 2015
Priority date	Apr 1, 2014
Publication date	Jul 31, 2018
Grant date	Jul 31, 2018

Abstract

The invention provides a heat shrinkable polyester film which has (1) a hot-water heat shrinkage of not less than 55% and not more than 90% in a main shrinking direction of the film when dipped in hot water at 98° C.; (2) a hot-water heat shrinkage of not less than −5% and not more than 12% in a direction orthogonal to the main shrinking direction of the film when dipped in hot water at 98° C.; (3) a difference in specific heat capacity ΔC p between at a lower and a higher temperature than Tg of not less than 0.1 J/(g·° C.) and not more than 0.7 J/(g·° C.) when a reverse heat flow is measured with a temperature modulated DSC; and (4) a tensile breaking strength of not less than 70 MPa and not more than 150 MPa in the direction orthogonal to the main shrinking direction of the film.

First claim

The invention claimed is:

1. A heat shrinkable polyester film which satisfies the following requirements (1) to (4):
(1) the film has a hot-water heat shrinkage of not less than 55% and not more than 90% in a main shrinking direction of the film when dipped in hot water at 98° C. for 10 seconds;
(2) the film has a hot-water heat shrinkage of not less than −5% and not more than 12% in a direction orthogonal to the main shrinking direction of the film when dipped in hot water at 98° C. for 10 seconds;
(3) the film has a difference in specific heat capacity ΔC p between at a lower and a higher temperature than Tg of not less than 0.1 J/(g·° C.) and not more than 0.7 J/(g·° C.) when a reverse heat flow is measured with a temperature modulated DSC; and
(4) the film has a tensile breaking strength of not less than 70 MPa and not more than 150 MPa in the direction orthogonal to the main shrinking direction of the film.

2. A package formed by covering at least a part of an outer periphery of an object to be packaged with a label obtained from the heat-shrinkable polyester film according to claim 1 and then shrinking the label on the covered object by heat.

3. The heat-shrinkable polyester film according to claim 1 , wherein the film has a maximum shrinkage stress of not less than 2 MPa and not more than 14 MPa in the main shrinking direction of the film measured with hot air at 90° C., and a shrinkage stress of not less than 60% and not more than 100% of the maximum shrinkage stress 30 seconds after measurement start.

4. A package formed by covering at least a part of an outer periphery of an object to be packaged with a label obtained from the heat-shrinkable polyester film according to claim 3 and then shrinking the label on the covered object by heat.

5. The heat-shrinkable polyester film according to claim 3 , wherein the film has a right-angled tearing strength per unit thickness of not less than 180 N/mm and not more than 350 N/mm in the direction orthogonal to the main shrinking direction of the film after being shrunk by 10% in the main shrinking direction in hot water at 80° C.

6. A package formed by covering at least a part of an outer periphery of an object to be packaged with a label obtained from the heat-shrinkable polyester film according to claim 5 and then shrinking the label on the covered object by heat.

7. The heat-shrinkable polyester film according to claim 5 , which is biaxially drawn in the main shrinking direction and in the direction orthogonal to the main shrinking direction.

8. A package formed by covering at least a part of an outer periphery of an object to be packaged with a label obtained from the heat-shrinkable polyester film according to claim 7 and then shrinking the label on the covered object by heat.

9. The heat-shrinkable polyester film according to claim 3 , which is biaxially drawn in the main shrinking direction and in the direction orthogonal to the main shrinking direction.

10. A package formed by covering at least a part of an outer periphery of an object to be packaged with a label obtained from the heat-shrinkable polyester film according to claim 9 and then shrinking the label on the covered object by heat.

11. The heat-shrinkable polyester film according to claim 1 , wherein the film has a right-angled tearing strength per unit thickness of not less than 180 N/mm and not more than 350 N/mm in the direction orthogonal to the main shrinking direction of the film after being shrunk by 10% in the main shrinking direction in hot water at 80° C.

12. A package formed by covering at least a part of an outer periphery of an object to be packaged with a label obtained from the heat-shrinkable polyester film according to claim 11 and then shrinking the label on the covered object by heat.

13. The heat-shrinkable polyester film according to claim 11 , which is biaxially drawn in the main shrinking direction and in the direction orthogonal to the main shrinking direction.

14. A package formed by covering at least a part of an outer periphery of an object to be packaged with a label obtained from the heat-shrinkable polyester film according to claim 13 and then shrinking the label on the covered object by heat.

15. The heat-shrinkable polyester film according to claim 1 , which is biaxially drawn in the main shrinking direction and in the direction orthogonal to the main shrinking direction.

16. A package formed by covering at least a part of an outer periphery of an object to be packaged with a label obtained from the heat-shrinkable polyester film according to claim 15 and then shrinking the label on the covered object by heat.

Assignees

• Toyo Boseki

Inventors

• Haruta Masayuki
• Ishimaru Shintaro

Classifications

• Y10T428/31786

  Of polyester [e.g., alkyd, etc.] · CPC title

• B65D75/00

  Packages comprising articles or materials partially or wholly enclosed in strips, sheets, blanks, tubes or webs of flexible sheet material, e.g. in folded wrappers (bundles of articles held together by packaging elements for convenience of storage or transport, e.g. portable segregating carrier for plural receptacles such as beer cans or pop bottles, or bales of material B65D71/00) · CPC title

• B32B2309/04

  Time · CPC title

• B29K2067/00

  Use of polyesters {or derivatives thereof}, as moulding material · CPC title

• C08L67/02

  Polyesters derived from dicarboxylic acids and dihydroxy compounds (C08L67/06 takes precedence) · CPC title