Abstract

The invention provides a heat-shrinkable polyester-based film containing ethylene terephthalate as a main constituent component and 0-5 mol % of a monomer component that can be an amorphous component based on all of the polyester resin components. The inventive film has a main shrinkage direction in the longitudinal direction, with heat shrinkage properties in the longitudinal direction and the width direction and a refractive index within specified ranges.

First claim

The invention claimed is:

1. A heat-shrinkable polyester-based film comprising ethylene terephthalate as a main constituent component and containing 0 mol % or more and 5 mol % or less of a monomer component that can be an amorphous component in the whole polyester resin components, and having a main shrinkage direction in the longitudinal direction, wherein the heat-shrinkable polyester-based film satisfies the following requirements (1) to (3):
(1) a hot water heat shrinkage rate in the longitudinal direction is 15% or more and 50% or less when the film is treated in hot water at 90° C. for 10 seconds;
(2) a hot water heat shrinkage rate in the width direction orthogonal to the longitudinal direction is 0% or more and 12% or less when the film is treated in hot water at 90° C. for 10 seconds; and
(3) a refractive index in the longitudinal direction is 1.570 or more, a refractive index in the width direction is 1.570 or more, and the refractive index in the width direction, which is the direction orthogonal to the main shrinkage direction, is higher than the refractive index in the longitudinal direction, which is the main shrinkage direction.

2. The heat-shrinkable polyester-based film according to claim 1 , wherein a tensile breaking strength in the width direction, which is the direction orthogonal to the main shrinkage direction, is 80 MPa or more and 200 MPa or less.

3. The heat-shrinkable polyester-based film according to claim 2 , wherein the film has a thickness unevenness of 11% or less in the longitudinal direction, which is the main shrinkage direction.

4. The heat-shrinkable polyester-based film according to claim 1 , wherein the film has a thickness unevenness of 11% or less in the longitudinal direction, which is the main shrinkage direction.

Assignees

• Toyo Boseki

Inventors

• Haruta Masayuki
• Mukoyama Yukinobu

Classifications

• B29C61/003

  characterised by the choice of material · CPC title

• C08J2467/02

  Polyesters derived from dicarboxylic acids and dihydroxy compounds (C08J2467/06 takes precedence) · CPC title

• C08J5/18 Primary

  Manufacture of films or sheets · CPC title

• B29K2067/00

  Use of polyesters {or derivatives thereof}, as moulding material · CPC title

• C08J2367/02

  Polyesters derived from dicarboxylic acids and dihydroxy compounds; (C08J2367/06 takes precedence) · CPC title