Process for preparing self-binding pigment particle suspensions

Patent metadata

Field	Value
Publication number	US-9988764-B2
Application number	US-201715584429-A
Country	US
Kind code	B2
Filing date	May 2, 2017
Priority date	Aug 31, 2011
Publication date	Jun 5, 2018
Grant date	Jun 5, 2018

Abstract

The invention relates to a process for preparing self-binding pigment particle suspensions, to a self-binding pigment particle suspension as well as to a paper product comprising self-binding pigment particles and to the use of the self-binding pigment particle suspension as filler material.

First claim

The invention claimed is:

1. Paper, plastic, paint, concrete or an agriculture product comprising self-binding pigment particles prepared by the process comprising the following steps:
a) providing an aqueous pigment material suspension, wherein the pigment of the pigment material suspension comprises calcium carbonate;
b) providing a polymeric binder, wherein the binder consists of at least one polysaccharide comprising galactose and/or mannose units;
c) mixing 0.1 wt.-% to 10 wt.-% of the binder of step b), based on the total weight of the aqueous pigment material suspension, with the aqueous pigment material suspension of step a), to obtain a mixture of the binder and the aqueous pigment material suspension; and
d) grinding the mixture of the binder and the aqueous pigment material suspension obtained in step c) to obtain a suspension of self-binding pigment particles, wherein the weight median diameter (d 50 ) of the self-binding pigment particles is less than the weight median diameter (d 50 ) of the pigment from step a).

2. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the pigment material of the pigment material suspension of step a) comprises calcium carbonate and one or more of-dolomite, magnesium, clay, talc, kaolin, aluminium hydroxide, mica, titanium dioxide, synthetic fibers or natural fibers.

3. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the pigment material of the pigment material suspension of step a) is a ground natural calcium carbonate, a precipitated calcium carbonate, a modified calcium carbonate, or any mixture thereof.

4. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the pigment material of the pigment material suspension of step a) is a ground natural calcium carbonate.

5. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the binder of step b) is at least one polysaccharide comprising galactose and mannose units.

6. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the binder of step b) is at least one polysaccharide comprising a linear chain of 1,4-linked β-D-mannopyranosyl units or a linear chain of 1,4-linked β-D-mannopyranosyl units with 1,6-linked α-D-galactopyranosyl units.

7. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the binder of step b) is at least one polysaccharide having a ratio of mannose units to galactose units from 6:1 to 1:1.

8. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the binder of step b) is at least one polysaccharide having a ratio of mannose units to galactose units from 5:1 to 1:1.

9. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the binder of step b) is at least one polysaccharide having a ratio of mannose units to galactose units from 4:1 to 1:1.

10. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the binder of step b) is at least one polysaccharide having a ratio of mannose units to galactose units from 3:1 to 1:1.

11. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the binder of step b) is in a form of a hydrocolloidal solution or a dry material.

12. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the binder of step b) is in a form of a hydrocolloidal solution having a binder concentration from 0.05 wt.-% to 10 wt.-%, based on the total weight of the solution.

13. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the binder of step b) is in a form of a hydrocolloidal solution having a binder concentration from 0.1 wt.-% to 5 wt.-%, based on the total weight of the solution.

14. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein in step c) 0.05 wt.-% to 5.0 wt.-% of the binder of step b), based on the total weight of the aqueous pigment material suspension, is mixed with the aqueous pigment material suspension of step a).

15. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein in step c) 0.1 wt.-% to 2 wt.-% of the binder of step b), based on the total weight of the aqueous pigment material suspension, is mixed with the aqueous pigment material suspension of step a).

16. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein in step c), the pigment material suspension has a solids content of 5 wt.-% to 80 wt.-%, based on the total weight of the pigment material suspension.

17. The paper, plastic, paint, concrete or an agriculture product according to claim 16 , wherein in step c), the pigment material suspension has a solids content of 10 wt.-% to 60 wt.-%, based on the total weight of the pigment material suspension.

18. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein grinding step d) is carried out at a temperature from 10° C. to 110° C.

19. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein grinding step d) is carried out until the fraction of self-binding pigment particles having a particle size of less than 1 μm is greater than 20 wt.-%, based on the total weight of the pigment particles.

20. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein grinding step d) is carried out until the fraction of self-binding pigment particles having a particle size of less than 1 μm is greater than 50 wt.-%, based on the total weight of the pigment particles.

21. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein the suspension of self-binding pigment particles obtained in step d) is concentrated such that the solids content in the suspension is from 45 wt.-% to 80 wt.-%, based on the total weight of the pigment material suspension.

22. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , wherein before or during or after step c) and/or step d) a dispersing agent is added.

23. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , which is paper.

24. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , which is plastic.

25. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , which is paint.

26. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , which is concrete.

27. The paper, plastic, paint, concrete or an agriculture product according to claim 1 , which is an agricultural product.

Assignees

• Omya Int Ag

Inventors

• Gantenbein Daniel
• Schoelkopf Joachim
• Gane Patrick A C

Classifications

• C01P2004/62

  Submicrometer sized, i.e. from 0.1-1 micrometer · CPC title

• C01P2004/64

  Nanometer sized, i.e. from 1-100 nanometer · CPC title

• C04B26/28

  Polysaccharides or derivatives thereof · CPC title

• D21H19/42

  at least partly organic · CPC title

• C09C1/0009

  Pigments for ceramics (C09C1/0015, C09C1/0078 take precedence) · CPC title