Black pigments comprising graphenic carbon particles

Patent metadata

Field	Value
Publication number	US-9988551-B2
Application number	US-201514979173-A
Country	US
Kind code	B2
Filing date	Dec 22, 2015
Priority date	Sep 30, 2011
Publication date	Jun 5, 2018
Grant date	Jun 5, 2018

Abstract

Thermally produced graphenic carbon particles for use as black pigments are disclosed. The pigments may be used in coatings and bulk articles to provide desirable jetness characteristics and absorbance at visible wavelengths.

First claim

We claim:

1. A black coating comprising:
a resin film; and
a black pigment comprising thermally produced graphenic carbon particles in an amount of from 0.01 to less than 5 weight percent based on the total dry film weight of the coating, wherein the black coating has a minimum absorbance of 80 percent throughout a wavelength range of 400 to 700 nm.

2. The black coating of claim 1 , wherein the thermally produced graphenic carbon particles comprise less than 2 weight percent.

3. The black coating of claim 1 , wherein the minimum absorbance is greater than 85 percent.

4. The black coating of claim 1 , wherein the thermally produced graphenic carbon particles have an average aspect ratio greater than 3:1 and a B.E.T. specific surface area of greater than 70 m 2 /g.

5. The black coating of claim 1 , wherein the resin film comprises a thermoset or thermoplastic film forming resin.

6. The black coating of claim 1 , wherein the thermally produced graphenic carbon particles comprise less than 1 weight percent.

7. The black coating of claim 1 , wherein the coating has a thickness of from 1 to 50 microns.

8. A black coating composition comprising:
a solvent:
a film-forming resin; and
thermally produced graphenic carbon particles in an amount of from 0.01 to less than 5 weight percent of the total solids weight of the film-forming resin and the thermally produced graphenic carbon particles, wherein the black coating composition has a minimum absorbance of 80 percent throughout a wavelength range of 400 to 700 nm when cured.

9. The black coating composition of claim 8 , wherein the thermally produced graphenic carbon particles comprise less than 2 weight percent.

10. The black coating composition of claim 8 , wherein the film-forming resin comprises a thermoset or thermoplastic film forming resin.

11. The black coating composition of claim 8 , herein the film forming resin comprises a thermoset or thermoplastic film forming resin.

12. The black coating composition of claim 8 , wherein the thermally produced graphenic carbon particles comprise less than 1 weight percent.

13. An article comprising:
a polymeric matrix; and
a black pigment dispersed in the polymeric matrix comprising thermally produced graphenic carbon particles in an amount of from 0.01 to less than 5 weight percent based on the total weight of the polymeric matrix and the thermally produced graphenic carbon particles, wherein the article has a minimum absorbance of 80 percent throughout a wavelength range of 400 to 700 nm.

14. The article of claim 13 , wherein the thermally produced graphenic carbon particles comprise less than 2 weight percent.

15. The article of claim 13 , wherein the thermally produced graphenic carbon particles comprise less than 1 weight percent.

16. A method of making a black coating composition comprising dispersing thermally produced graphenic carbon particles and a film-forming resin in a solvent, wherein the thermally produced graphenic carbon particles comprise of from 0.01 to less than 5 weight percent of the total solids weight of the film-forming resin and the thermally produced graphenic carbon particles, wherein the article ha a minimum absorbance of 80 percent throughout a wavelength range of 400 to 700 nm.

17. The method of claim 16 , wherein the thermally produced graphenic carbon particles comprise less than 2 weight percent.

18. The method of claim 16 , wherein the thermally produced graphenic carbon particles comprise less than 1 weight percent.

19. The method of claim 16 , wherein the thermally produced graphenic carbon particles are produced by introducing a methane precursor material or a hydrocarbon precursor material capable of forming a two-carbon-fragment species into a thermal zone having a temperature of greater than 3,500° C.

20. The method of claim 19 , wherein the thermally produced graphenic carbon particles are dispersed with a polymeric dispersant comprising:
a) an anchor block comprising glycidyl (meth)acrylate, 3,4-epoxycyclohexymethyl(meth)acrylate, 2-(3,4-epoxycyclohexyl)ethyl(meth)acrylate, allyl glycidyl either and mixtures thereof, reacted with a carboxylic acid comprising 3-hydroxy-2-naphthoic acid, para-nitrobenzoic acid, hexanoic acid, 2-ethyl hexanoic acid, decanoic acid and/or undecanoic acid; and
b) at least one tail block comprising at least one (meth)acrylic acid alkyl ester.

Assignees

• Ppg Ind Ohio Inc

Inventors

• Vanier Noel R
• Decker Eldon L
• Istivan Stephen B
• Hung Cheng-Hung
• Bonnett Gina R

Classifications

• B82Y40/00

  Manufacture or treatment of nanostructures · CPC title

• C01P2006/12

  Surface area · CPC title

• C01P2004/24

  Nanoplates, i.e. plate-like particles with a thickness from 1-100 nanometer · CPC title

• C01P2004/62

  Submicrometer sized, i.e. from 0.1-1 micrometer · CPC title

• C01P2004/04

  obtained by TEM, STEM, STM or AFM · CPC title