Three-dimensional nanosized porous metal oxide electrode material of lithium ion battery and preparation method thereof

Patent metadata

Field	Value
Publication number	US-9985273-B2
Application number	US-201113816710-A
Country	US
Kind code	B2
Filing date	Jun 27, 2011
Priority date	Aug 13, 2010
Publication date	May 29, 2018
Grant date	May 29, 2018

Abstract

A preparation method of a three-dimensional nanosized porous metal oxide electrode material of lithium ion battery, which soaks a dried polymer colloidal crystal microsphere template in a metal salt solution as a precursor solution for a period of time, and obtains a precursor template complex after filtration and drying; heats the precursor template complex to a certain temperature at a low heating rate and keeps the temperature, and then obtains the three-dimensional nanosized porous metal oxide electrode material of lithium ion battery after cooling to room temperature. A metal oxide electrode material is manufactured, with the three-dimensional nanosized porous metal oxide electrode material thereby improving the ionic conductivity of the negative electrode material of lithium ion battery, and shortens the diffusion path of the lithium ions during an electrochemical reaction process, and improves the rate discharge performance of lithium ion battery greatly.

First claim

We claim:

1. A preparation method of a three-dimensional nanosized porous metal oxide electrode material for a lithium ion battery, wherein the method comprises the following steps:
(1) soaking a dried polymer microsphere colloid crystal template composed of microspheres with a size of 275±10 nm in a metal salt solution as a precursor, where the metal salt solution is selected from a group consisting of: an ethylene glycol/methanol mixed solution of Fe 3+ , an ethylene glycol/methanol mixed solution of Fe 3+ and Co 2+ with a total metal ion concentration of 1.5 mols/Liter (the molar ratio, Fe 3+ : Co 2+ =2:1), and an ethanol solution of SnCl 2 .2H 2 O with a total metal ion concentration of 0.5 mol/L, where the soaking is conducted for 5-10 hours, and obtaining a polystyrene (PS) precursor template complex after filtration and drying; and
(2) heating the polystyrene (PS) precursor template complex to a temperature that falls in a range of 450-600° C. at a rate of 1-5° C./min and keeping the temperature in the range of 450-600° C. for 10 hours, and then obtaining based on the selected precursor, respectively, from step 1—at least one of a-Fe 2 O 3 , CoFe 2 O 4 , or SnO 2 ordered three-dimensional nanosized porous metal oxide electrode material for the lithium ion battery after cooling to room temperature, wherein an aperture of the three-dimensional nanosized porous metal oxide electrode material has an aperture size of from 105 to 225 nm and an aperture wall thickness of from 20 to 30 nm and the least one of a-Fe 2 O 3 , CoFe 2 O 4 , or SnO 2 ordered three-dimensional nanosized porous metal oxide electrode material having an initial discharge capacity of at least 1704 mAh·g −1 and a coulombic efficiency of at least 80% after 20 cycles.

2. The preparation method of a three-dimensional nanosized porous metal oxide electrode material for a lithium ion battery according to claim 1 , wherein the polymer microsphere template is prepared by the following method: preparing a polymer microsphere emulsion with the polymer emulsion polymerization method, and then obtaining the polymer microsphere template with ordered arrangement by co-precipitation or centrifugation.

3. The preparation method of a three-dimensional nanosized porous metal oxide electrode material for a lithium ion battery according to claim 2 , wherein the polymer microsphere emulsion is a polystyrene microsphere emulsion.

Assignees

• Sun Jiangming
• Zhao Tiepeng
• Xu Zhigang
• Wang Yanbing
• Wang Gang
• Zhang Ming
• Xie Shirong
• Shenjiang Electric Vehicle Co

Inventors

• Sun Jiangming
• Zhao Tiepeng
• Xu Zhigang
• Wang Yanbing
• Wang Gang
• Zhang Ming
• Xie Shirong

Classifications

• H01M4/0497

  Chemical precipitation · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M4/0471 Primary

  involving thermal treatment, e.g. firing, sintering, backing particulate active material, thermal decomposition, pyrolysis · CPC title

• H01M4/131

  Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx · CPC title

• H01M4/1391

  of electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx · CPC title