Color metallic pigment, method for producing same, and coating composition and cosmetic containing same

Patent metadata

Field	Value
Publication number	US-9982139-B2
Application number	US-201113812462-A
Country	US
Kind code	B2
Filing date	Jun 8, 2011
Priority date	Jul 28, 2010
Publication date	May 29, 2018
Grant date	May 29, 2018

Abstract

A color metallic pigment according to the present invention contains at least a metallic pigment, an amorphous silicon oxide film layer that is formed on the surface of the metallic pigment, a metal oxide layer that is formed on the surface of the amorphous silicon oxide film layer and contains a metal oxide other than silicon oxide, and metal particles that are formed on the surface of the metal oxide layer, wherein the metal particles are so formed as to directly cover a part of the metal oxide layer.

First claim

The invention claimed is:

1. A color metallic pigment comprising at least a metallic pigment, an amorphous silicon oxide film layer that is formed on the surface of the metallic pigment, a metal oxide layer that is formed on the surface of the amorphous silicon oxide film layer and comprises a metal oxide other than silicon oxide, and metal particles that are formed on the surface of the metal oxide layer,
wherein the amorphous silicon oxide film layer has a thickness of 10 to 500 nm,
wherein the metal oxide layer has a thickness of 0.1 to 10 nm and consists of an oxide of one element selected from the group consisting of Mg, Sn, Zn, Co, Ni, Fe, Zr, Ti, and Ce,
wherein the metal particles are so formed as to directly cover a part of the metal oxide layer,
the surface of the metal oxide layer has a region on which the metal particles are not formed,
the region corresponds to the spacing between the metal particles,
the spacing is greater than or equal to 0.1 and less than or equal to 10 nm, and
the metal particles have an average particle diameter of less than or equal to 50 nm,
wherein the strength of the metal particle adhesion as well as the water and weather resistance are enhanced.

2. The color metallic pigment according to claim 1 , wherein each of the metal particles comprises at least one element selected from the group consisting of Cu, Ni, and Ag.

3. A method for producing the color metallic pigment as recited in claim 1 , comprising at least the steps of:
hydrolyzing an organosilicon compound in a solvent mainly containing a hydrophilic solvent and having a metallic pigment dispersed therein to allow amorphous silicon oxide to be deposited on the metallic pigment, thereby forming an amorphous silicon oxide film layer on the surface of the metallic pigment;
allowing a metal oxide layer comprising a metal oxide other than silicon oxide to be deposited on the surface of the amorphous silicon oxide film layer, thereby forming the metal oxide layer; and
forming metal particles on the surface of the metal oxide layer by an electroless plating method.

4. The method for producing the color metallic pigment according to claim 3 , wherein the metal oxide layer comprises an oxide of at least one element selected from the group consisting of Mg, Sn, Zn, Co, Ni, Fe, Zr, Ti, and Ce.

5. A coating composition containing at least the color metallic pigment as recited in claim 1 .

6. A cosmetic containing at least the color metallic pigment as recited in claim 1 .

7. The color metallic pigment of claim 1 , wherein an average particle diameter of the metallic pigment is in the range of 2 to 300 μm.

8. The color metallic pigment of claim 7 , wherein a ratio of the average particle diameter A to an average thickness B (A/B) of the metallic pigment is within the range of 5 to 1000.

9. A color metallic pigment which consists essentially of:
a metallic pigment, an amorphous silicon oxide film layer disposed on the surface of the metallic pigment, a metal oxide layer, other than silicon oxide, disposed on the surface of the amorphous silicon oxide film layer, and metal particles disposed on the surface of the metal oxide layer,
wherein the amorphous silicon oxide film layer has a thickness of 10 to 500 nm,
wherein the metal oxide layer has a thickness of 0.1 to 10 nm and consists essentially of an oxide of at least one element selected from the group consisting of Mg, Sn, Zn, Co, Ni, Fe, Zr, Ti and Ce,
wherein the metal particles comprise at least one element selected from the group consisting of Cu, Ni and Ag and are disposed to directly cover a part of the metal oxide layer, whereby the surface of the metal oxide layer has a region on which the metal particles are not formed, said region corresponding to a spacing between the metal particles which is greater than or equal to 0.1 nm and less than or equal to 10 nm, and the metal particles have an average particle diameter of 5 to 50 nm, and
wherein the strength of the metal particle adhesion as well as the water and weather resistance are enhanced.

10. The color metallic pigment of claim 9 , wherein the metallic pigment is selected from the group consisting of Al, Cu, Zn, Ti, Fe, Ni, Cr, and alloys thereof.

11. The color metallic pigment of claim 10 , wherein the metallic pigment has an average, longer particle diameter of 2 to 300 μm.

12. The color metallic pigment of claim 11 , wherein the metallic pigment has a thickness of 0.01 to 5 μm.

13. The color metallic pigment of claim 9 , wherein a ratio of the average particle diameter A to the average thickness B (A/B) is 5 to 1000.

14. The color metallic pigment of claim 1 , wherein the metal particles are formed as a single layer.

15. The color metallic pigment of claim 1 , wherein the metal particles are not in contact with each other.

Assignees

• Hashizume Yoshiki
• Morimitsu Taro
• Nakao Takayuki
• Toyo Aluminium Kk

Inventors

• Hashizume Yoshiki
• Morimitsu Taro
• Nakao Takayuki

Classifications

• A61K8/0258

  Layered structure · CPC title

• A61K8/27

  Zinc; Compounds thereof · CPC title

• A61K2800/412

  Microsized, i.e. having sizes between 0.1 and 100 microns · CPC title

• C09C1/006

  consisting of a metal or an alloy · CPC title

• C09D5/36

  Pearl essence, e.g. coatings containing platelet-like pigments for pearl lustre · CPC title