Silicone polymer emulsions

Patent metadata

Field	Value
Publication number	US-9976105-B2
Application number	US-44510207-A
Country	US
Kind code	B2
Filing date	Oct 9, 2007
Priority date	Oct 10, 2006
Publication date	May 22, 2018
Grant date	May 22, 2018

Abstract

Silicone oil-in-water emulsions containing a polysiloxane containing polymer is prepared by first preparing a polysiloxane containing polymer by the polymerization of siloxane containing monomers and/or oligomers in the presence of an inert organopoly siloxane and/or an organic fluid, a suitable catalyst and optionally an end-blocking agent; and quenching the reaction if required. If required one or more surfactants may be introduced into the polysiloxane containing polymer to form a homogenous oil phase. Water is then added (in an amount of 0.1-10 percent by weight based on total oil phase weight) to the homogenous oil phase to form a water-in-oil emulsion. Shear is applied to the water-in-oil emulsion to cause inversion of the water-in-oil emulsion to an oil-in-water emulsion. Finally, if required the oil-in-water emulsion can be diluted by adding more water.

First claim

The invention claimed is:

1. A method of making silicone oil-in-water emulsions containing a polysiloxane containing polymer, said method comprising the steps of:
(i) preparing a polysiloxane containing polymer by the polymerisation of siloxane containing monomers and/or oligomers in the presence of an inert organopolysiloxane and/or an organic fluid, a suitable catalyst and optionally an end-blocking agent, wherein the polysiloxane containing polymer is of the following general formula
R (3-a) R 1 a SiO[(R 2 SiO) b (RR 1 SiO) c ]SiR (3-a) R 1 a   (1)

wherein each R is the same or different and is an alkyl group containing 1 to 8 carbon atoms or a phenyl group; R 1 is a hydroxy group, a hydrolysable group, or an unsaturated organic group; a is zero or 1; b is an integer; c is zero or an integer; and the sum of b+c is equal to a value of at least 500;
(ii) optionally quenching the polymerisation process;
wherein the inert fluid is retained within the resulting polysiloxane containing polymer in an amount of from 5 to 70% w/w;

(iii) optionally introducing one or more surfactants into the polysiloxane containing polymer to form a homogenous oil phase;
(iv) adding water to the homogenous oil phase to form a water-in-oil emulsion, the water being added in an amount of 0.1 to 10 percent by weight based on the total oil phase weight;
(v) applying shear to the water-in-oil emulsion to cause inversion of the water-in-oil emulsion to an oil-in-water emulsion; and
(vi) optionally diluting the oil-in-water emulsion by adding more water.

2. The method according to claim 1 , wherein the inert fluid is an organic extender and/or plasticizer and/or a natural oil.

3. The method according to claim 1 , wherein the inert fluid is a cyclic siloxane having from 2 to 20 silicon atoms.

4. The method according to claim 1 , wherein the inert fluid comprises a silicone cyclic and the silicone is a polydimethyl gum.

5. The method according to claim 1 , wherein the inert fluid is a trialkylsilyl terminated polydialkylsiloxane having a viscosity of from 0.65 to 10000 mPa·s at 25° C.

6. The method according to claim 1 , wherein the polysiloxane containing polymer is prepared via a polymerisation process selected from the group of polycondensation, chain extension, polyaddition, and ring opening.

7. The method according to claim 1 , wherein the catalyst is part of the surfactant used for emulsification.

8. The method according to claim 7 , wherein the polysiloxane containing polymer is prepared via a polycondensation reaction and the catalyst is dodecylbenzenesulphonic acid.

9. The method according to claim 1 , wherein the homogenous oil phase is from 1000 to 100000 mPa·s at 25° C.

10. The method according to claim 1 , wherein the sum of b+c is equal to a value of at least 1500.

11. The method according to claim 1 , wherein the inert fluid is a cyclic siloxane having from 2 to 20 silicon atoms.

12. The method according to claim 1 , wherein the inert fluid is a trialkylsilyl terminated polydialkylsiloxane having a viscosity of from 0.65 to 10000 mPa·s at 25° C.

13. A method of making silicone oil-in-water emulsions containing a polysiloxane containing polymer, said method comprising the steps of:
(i) preparing a polysiloxane containing polymer by the polymerisation of siloxane containing monomers and/or oligomers in the presence of an inert fluid, wherein the inert fluid has a viscosity of from 0.65 mPa·s to 10000 mPa·s at 25° C. and is selected from an organopolysiloxane extender or plasticiser, an organic extender or plasticiser, or a cyclic siloxane comprising between 3 and 20 silicon atoms, a catalyst and optionally an end-blocking agent, wherein the polysiloxane containing polymer is of the following general formula
R (3-a) R 1 a SiO[(R 2 SiO) b (RR 1 SiO) c ]SiR (3-a) R 1 a   (1)

wherein each R is the same or different and is an alkyl group containing 1 to 8 carbon atoms or a phenyl group; R 1 is a hydroxy group, a hydrolysable group, or an unsaturated organic group; a is zero or 1; b is an integer; c is zero or an integer; and the sum of b+c is equal to a value of at least 200;
(ii) optionally quenching the polymerisation process;
wherein the inert fluid is retained within the resulting polysiloxane containing polymer in an amount of from 5 to 70% w/w;

(iii) optionally introducing one or more surfactants into the polysiloxane containing polymer to form a homogenous oil phase;
(iv) adding water to the homogenous oil phase to form a water-in-oil emulsion, the water being added in an amount of 0.1 to 10 percent by weight based on the total oil phase weight;
(v) applying shear to the water-in-oil emulsion to cause inversion of the water-in-oil emulsion to an oil-in-water emulsion; and
(vi) optionally diluting the oil-in-water emulsion by adding more water.

14. The method according to claim 1 , wherein the polysiloxane is a polydimethyl gum.

15. The method according to claim 1 , wherein the polysiloxane containing polymer is prepared via a polymerisation process selected from the group of polycondensation, chain extension, polyaddition, and ring opening, and the catalyst is part of the surfactant used for emulsification.

16. The method according to claim 1 , wherein the inert fluid is retained within the resulting polysiloxane containing polymer in an amount of from 5 to 60% w/w.

Assignees

• Barnes Kathleen
• Jensen Jary David
• Rochlitz Walker L
• Stammer Andreas
• Dow Silicones Corp

Inventors

• Barnes Kathleen
• Jensen Jary David
• Rochlitz Walker L
• Stammer Andreas

Classifications

• C10M2229/045

  containing silicon-to-hydroxyl bonds · CPC title

• C10M2229/0455

  used as base material · CPC title

• D06M15/643

  containing silicon in the main chain · CPC title

• A61K8/062

  Oil-in-water emulsions · CPC title

• A61Q19/10

  Washing or bathing preparations · CPC title