Sidewall for tire

Patent metadata

Field	Value
Publication number	US-9976014-B2
Application number	US-201113582837-A
Country	US
Kind code	B2
Filing date	Mar 17, 2011
Priority date	Mar 18, 2010
Publication date	May 22, 2018
Grant date	May 22, 2018

Abstract

The invention relates to a tire sidewall, at least one portion of which has a rubber composition based on at least a diene elastomer, a crosslinking system and a reinforcing filler, wherein the content of reinforcing filler in the composition varies from 20 to 40 parts by weight per hundred parts of elastomer, phr, with a volume fraction of reinforcing filler in the composition ranging from 8.0% to 13.0%, and in that this reinforcing filler comprises predominantly a carbon black or a mixture of carbon blacks with a BET specific surface area ranging from 50 m 2 /g to 69 m 2 /g.

First claim

The invention claimed is:

1. A tire sidewall, comprising at least one portion having a rubber composition based on at least:
a diene elastomer,
a crosslinking system, and
a reinforcing filler,
wherein the content of reinforcing filler in the rubber composition varies from 20 to 40 parts by weight per hundred parts of elastomer, phr,
wherein the volume fraction of reinforcing filler in the rubber composition ranges from 8.0% to 13.0%, and
wherein this reinforcing filler comprises predominantly a carbon black or a mixture of carbon blacks, the BET specific surface area of which ranges from 50 m 2 /g to 69 m 2 /g.

2. The tire sidewall according to claim 1 , wherein the carbon black or the mixture of carbon blacks with a BET specific surface area ranging from 50 m 2 /g to 69 m 2 /g is mixed with one or more other organic or inorganic reinforcing fillers.

3. The tire sidewall according to claim 1 , wherein the carbon black or the mixture of carbon blacks with a BET specific surface area ranging from 50 m 2 /g to 69 m 2 /g constitutes at least 85% by weight of the reinforcing filler.

4. The tire sidewall according to claim 3 , wherein the carbon black or the mixture of carbon blacks constitutes at least 95% of the reinforcing filler.

5. The tire sidewall according to claim 1 , wherein the carbon black or the mixture of carbon blacks with a BET specific surface area ranging from 50 m 2 /g to 69 m 2 /g constitutes 100% of the reinforcing filler.

6. The tire sidewall according to claim 1 , wherein the carbon black or the mixture of carbon blacks with a BET specific surface area ranging from 50 m 2 /g to 69 m 2 /g has a COAN oil absorption number ranging from 80 ml/100 g to 120 ml/100 g.

7. The tire sidewall according to claim 1 , wherein the proportion of reinforcing filler in the composition varies from 20 phr to 35 phr.

8. The tire sidewall according to claim 7 , wherein the proportion of reinforcing filler in the composition varies from 25 phr to 30 phr.

9. The tire sidewall according to claim 7 , wherein the volume fraction of the reinforcing filler in the composition varies from 8.0% to 10.0%.

10. The tire sidewall according to claim 9 , wherein the volume fraction of the reinforcing filler in the composition varies from 8.7% to 9.4%.

11. The tire sidewall according to claim 1 , wherein the rubber composition comprises a mixture of elastomers composed of 30 to 55% of natural rubber, of a synthetic polyisoprene or of a mixture of natural rubber and of a synthetic polyisoprene, and of 45 to 70% of a diene elastomer chosen from polybutadienes, styrene-butadiene copolymers, isoprene-butadiene copolymers, isoprene-styrene copolymers and isoprene-butadiene-styrene terpolymers and mixtures thereof.

12. The tire sidewall according to claim 11 , wherein said diene elastomer is a polybutadiene.

13. The tire sidewall according to claim 12 , wherein the polybutadiene is a cis-1,4-polybutadiene.

14. The tire sidewall according to claim 1 , wherein the rubber composition comprises a plasticizer.

15. The tire sidewall according to claim 1 , wherein the at least one portion of sidewall is located on an outer face of the sidewall.

16. The tire sidewall according to claim 1 , wherein the at least one portion of sidewall extends over the entire distance from the crown to the bead.

17. A tire comprising a sidewall according to claim 1 .

18. A process for preparing a tire sidewall composition based on at least a diene elastomer, a crosslinking system and a reinforcing filler, wherein the content of reinforcing filler in the composition varies from 20 to 40 phr with a volume fraction of reinforcing filler in the composition ranging from 8.0% to 13.0%, and wherein this reinforcing filler comprises predominantly a carbon black or a mixture of carbon blacks with a BET specific surface area ranging from 50 m 2 /g to 69 m 2 /g, comprising:
thermomechanically kneading the diene elastomer and the reinforcing filler until a maximum temperature of between 110° C. and 190° C. is reached;
cooling the mixture down to a temperature below 100° C.;
then incorporating the crosslinking system;
kneading everything until a maximum temperature below 110° C. is reached in order to obtain a rubber composition,
calendering or extruding the rubber composition.

19. The process according to claim 18 , wherein the proportion of the reinforcing filler in the composition varies from 20 phr to 35 phr.

20. The process according to claim 19 , wherein the proportion of reinforcing filler in the composition varies from 25 phr to 30 phr.

21. The process according to claim 19 , wherein the volume fraction of the reinforcing filler in the composition varies from 8.0% to 10.0%.

22. The process according to claim 21 , wherein the volume fraction of reinforcing filler is from 8.7% to 9.4%.

23. The process according to claim 18 , wherein the carbon black or the mixture of carbon blacks with a BET specific surface area ranging from 50 m 2 /g to 69 m 2 /g constitutes at least 85% by weight of the reinforcing filler.

Assignees

• Hennebert Guillaume
• Lapra Arnaud
• Michelin & Cie
• Michelin Rech Tech

Inventors

• Hennebert Guillaume
• Lapra Arnaud

Classifications

• B60C1/0025 Primary

  Compositions of the sidewalls · CPC title

• C08L2666/08

  Homopolymers or copolymers according to C08L7/00 - C08L21/00; Derivatives thereof · CPC title

• C08L9/00 Primary

  Compositions of homopolymers or copolymers of conjugated diene hydrocarbons · CPC title

• C08K5/01

  Hydrocarbons {(C08K5/0091 takes precedence)} · CPC title

• Y02T10/862

  Cross-Sectional Technologies · mapped topic