Method for preparing super absorbent polymer and super absorbent polymer prepared therefrom

Patent metadata

Field	Value
Publication number	US-9976003-B2
Application number	US-201515302845-A
Country	US
Kind code	B2
Filing date	Nov 9, 2015
Priority date	Nov 27, 2014
Publication date	May 22, 2018
Grant date	May 22, 2018

Abstract

The present invention relates to a method for preparing a super absorbent polymer. The method for preparing a super absorbent polymer according to the present invention can provide a super absorbent resin exhibiting fast absorption rate and high saline flow conductivity while having excellent absorption properties such as a centrifuge retention capacity and an absorbency under pressure, by using the polycarboxylic acid-based copolymer under pulverization of the hydrous gel phase polymer.

First claim

The invention claimed is:

1. A method for preparing a super absorbent polymer comprising the steps of:
1) carrying out thermal polymerization or photo-polymerization of a monomer composition including a water-soluble ethylene-based unsaturated monomer, a polymerization initiator and a polycarboxylic acid-based copolymer having a repeating unit represented by the following Chemical Formulas 1-a and 1-b to prepare a hydrous gel phase polymer;
2) drying the hydrous gel phase polymer;
3) pulverizing the dried polymer; and
4) surface-crosslinking the pulverized polymer;

in Chemical Formulas 1-a and 1-b,
R 1 , R 2 and R 3 are each independently hydrogen, or an alkyl group having 1 to 6 carbon atoms,
RO is an oxyalkylene group having 2 to 4 carbon atoms,
M 1 is hydrogen, or a monovalent metal or non-metal ion,
X is —COO—, or an alkyloxy group having 1 to 5 carbon atoms, or an alkyldioxy group having 1 to 5 carbon atoms,
m is an integer of 1 to 100,
n is an integer of 1 to 1000, and
p is an integer of 1 to 150, provided that when p is 2 or more, two or more repeated —RO— may be the same or different from each other.

2. The method for preparing a super absorbent polymer according to claim 1 , wherein the polycarboxylic acid-based copolymer in the step 1 is mixed in an amount of 0.001 to 5 parts by weight based on 100 parts by weight of the water-soluble ethylene-based unsaturated monomer.

3. The method for preparing a super absorbent polymer according to claim 1 , wherein the polycarboxylic acid-based copolymer has a weight average molecular weight of 500 to 1,000,000.

4. The method for preparing a super absorbent polymer according to claim 1 , wherein the drying of the step 2 is carried out at a temperature of 120° C. to 250° C.

5. The method for preparing a super absorbent polymer according to claim 1 , further comprising a step of pulverizing the hydrous gel phase polymer into a particle diameter of 1 mm to 10 mm, before the drying step of the hydrous gel phase polymer.

6. The method for preparing a super absorbent polymer according to claim 1 , wherein the pulverization of the dried polymer is carried out so that the particle diameter of the pulverized polymer becomes 150 μm to 850 μm.

7. The method for preparing a super absorbent polymer according to claim 1 , wherein the surface crosslinking is carried out at a temperature of 100 to 250° C.

8. The method for preparing a super absorbent polymer according to claim 1 , wherein the surface crosslinking is carried out with one or more crosslinking agents selected from the group consisting of ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, glycerol polyglycidyl ether, propylene glycol diglycidyl ether, polypropylene glycol diglycidyl ether, ethylene carbonate, ethylene glycol, diethylene glycol, propylene glycol, triethylene glycol, tetraethylene glycol, propanediol, dipropylene glycol, polypropylene glycol, glycerin, polyglycerin, butanediol, heptanediol, hexanediol, trimethylolpropane, pentaerythritol, sorbitol, calcium hydroxide, magnesium hydroxide, aluminum hydroxide, iron hydroxide, calcium chloride, magnesium chloride, aluminum chloride, and iron chloride.

Assignees

• Lg Chemical Ltd

Inventors

• Lee Yong Hun
• Ahn Tae Bin
• Han Chang Sun
• Seo Sung Jong

Classifications

• C08F6/008

  Treatment of solid polymer wetted by water or organic solvents, e.g. coagulum, filter cakes · CPC title

• C08F2/10

  Aqueous solvent · CPC title

• C08F20/10

  Esters · CPC title

• C08F290/062

  Polyethers · CPC title

• C08J3/075

  Macromolecular gels · CPC title