Method for producing a shaped body and shaped body that can be produced thereby

Patent metadata

Field	Value
Publication number	US-9970083-B2
Application number	US-201414889907-A
Country	US
Kind code	B2
Filing date	May 5, 2014
Priority date	May 7, 2013
Publication date	May 15, 2018
Grant date	May 15, 2018

Abstract

A method for producing a shaped body from a metallic infiltrated composite, includes a first step in which a shaped body framework, some regions of which have an open pore framework structure, is produced from a powder or from a powder mixture having a primary component of a first metal or of a first metal alloy, in that the powder or the powder mixture is applied in layers, at least partially locally melted at predefined sites by a selective beam melting method and binds together upon solidification. In a second step, the shaped body framework is infiltrated with a melt of a second metal or metal alloy which melts at a lower temperature than the first metal or metal alloy.

First claim

The invention claimed is:

1. A process for producing a shaped body from a metallic infiltrated composite, the process comprising the following steps:
producing a shaped body framework having a predominantly open-pore framework structure at least in some regions from a powder or a powder mixture having a primary component composed of molybdenum or tungsten or a molybdenum or tungsten alloy, by constructing the shaped body framework layer by layer with superposed layers and forming each layer by applying the powder or powder mixture without an addition of organic binders or organic fluxes in a layer, at least partially locally melting the powder or powder mixture at predetermined sites by a selective beam melting method and solidification of the powder or powder mixture; and
infiltrating the shaped body framework with a melt of copper or a copper alloy having a lower melting temperature than the molybdenum or tungsten or the molybdenum or tungsten alloy.

2. The process according to claim 1 , which further comprises adjusting a porosity or pore size of the framework structure by the selective beam melting method so as to be spatially different.

3. The process according to claim 1 , which further comprises providing the shaped body with a chemical composition gradient in one or more than one spatial direction.

4. The process according to claim 1 , which further comprises forming at least one recess having a geometrically predetermined shape in the framework structure by not melting powder particles in a corresponding region and removing loose powder particles from the framework structure after the production of the framework structure and prior to the infiltration with the melt.

5. The process according to claim 1 , which further comprises forming at least one recess having a geometrically predetermined shape in the shaped body.

6. The process according to claim 1 , wherein the second metal or second metal alloy has good thermal conductivity.

7. The process according to claim 1 , wherein the selective beam melting method is selective laser melting or selective electron beam melting.

8. A shaped body formed from an infiltrated composite, the shaped body comprising:
an open-pore framework structure having at least a partial region composed of molybdenum or tungsten or a molybdenum or tungsten alloy, said framework structure having a porosity changing locally in at least two spatial directions; and
a solidified melt of copper or a copper alloy at least partly filling pores in said open-pore framework structure, said copper or copper alloy having a lower melting temperature than said molybdenum or tungsten or said molybdenum or tungsten alloy.

9. The shaped body according to claim 8 , wherein said framework structure has recesses with a volume having a lowest extent in any direction of at least 100 μm.

10. The shaped body according to claim 8 , wherein the shaped body has recesses with a volume having a lowest extent in any direction of at least 100 μm.

11. The shaped body according to claim 8 , wherein at least part of the shaped body has a chemical composition with a two-dimensional gradient.

Assignees

• Plansee Se

Inventors

• Kestler Heinrich
• Tabernig Bernhard

Classifications

• B22F2999/00

  Aspects linked to processes or compositions used in powder metallurgy · CPC title

• B23K26/0006

  taking account of the properties of the material involved (B23K26/32, B23K26/40 take precedence) · CPC title

• B23K15/0086

  welding for purposes other than joining, e.g. build-up welding · CPC title

• B22F2207/17

  density or porosity gradients · CPC title

• B22F3/11

  Making porous workpieces or articles · CPC title