Modified silicon oil for wax-free die casting lubricants

Patent metadata

Field	Value
Publication number	US-9968990-B2
Application number	US-201615284659-A
Country	US
Kind code	B2
Filing date	Oct 4, 2016
Priority date	Apr 7, 2014
Publication date	May 15, 2018
Grant date	May 15, 2018

Abstract

The present invention relates to a mixture of polyalkylsiloxanes obtainable through a hydrosilylation reaction wherein a mixture of monounsaturated olefins is reacted with an amount of one or more polyalkylhydrosiloxanes in the presence of a hydrosilylation catalyst. Furthermore, the invention concerns polyalkylsiloxane comprising alkyl side chains consisting of linear or branched alkyl groups with 40 to 60 carbon atoms, with 16 to 30 carbon atoms, and 6 to 15 carbon atoms. In addition, the present invention relates to water-based compositions suitable for use in metal casting processes as a mold release agent comprising a mixture of polyalkylsiloxanes, a non-ionic surfactant having a HLB value of at least 8, and less than 20 wt.-% of waxes. In addition, the present invention relates to the use of the polyalkylsiloxanes and mixtures of polyalkylsiloxanes.

First claim

The invention claimed is:

1. A mixture of polyalkylsiloxanes obtained through a hydrosilylation reaction wherein a mixture of monounsaturated olefins consisting of:
1-20 mol % of olefins with 40 to 60 carbon atoms,
1-20 mol % of olefins with 16 to 30 carbon atoms, and
60-98 mol % of olefins with 6 to 15 carbon atoms
is reacted with an amount of one or more polyalkylhydrosiloxanes in the presence of a hydrosilylation catalyst
wherein each of the one or more polyalkylhydrosiloxanes comprises a repeating unit according to the general structure (I):

wherein n indicates the number of repeating units and ranges from 5 to 10,000;
wherein the residue R 1 is selected from linear or branched alkyl groups with less than 6 carbon atoms.

2. The mixture of polyalkylsiloxanes according to claim 1 , wherein the amount of polyalkylhydrosiloxanes is at least 60% of the stoichiometric amount, but not more than the stoichiometric amount relative to the mixture of monounsaturated olefins.

3. The mixture of polyalkylsiloxanes according to claim 1 , wherein the one or more polyalkylhydrosiloxanes includes polymethylhydrosiloxanes polymethylhydrosiloxanes.

4. The mixture of polyalkylsiloxanes according to claim 1 , wherein at least 80 mol % of the mixture of monounsaturated olefins are selected from α-olefins.

5. The mixture of polyalkylsiloxanes according to claim 1 , wherein the temperature at which the mixture of monounsaturated olefins is reacted with the one or more polyalkylhydrosiloxanes is in a range of from 80° C. to 180° C. for a time sufficient to yield not more than 10 mol % Si—H bonds in the mixture of polyalkylsiloxanes.

6. The mixture of polyalkylsiloxanes according to claim 1 , wherein the hydrosilylation catalyst is a platinum catalyst.

7. The mixture of polyalkylsiloxanes according to claim 1 , wherein an inert liquid vehicle that acts as a solvent for the one or more polyalkylhydrosiloxanes and/or the mixture of monounsaturated olefins is present in an amount of less than 20 wt.-%; and/or the mixture of polyalkylsiloxanes is an oil.

8. The mixture of polyalkylsiloxanes according to claim 7 , wherein the inert liquid vehicle is present in an amount of less than 1 wt.-%; and/or the mixture of polyalkylsiloxanes is an oil.

9. The mixture of polyalkylsiloxanes according to claim 1 , wherein the mixture of polyalkylsiloxanes is an oil.

10. The mixture of polyalkylsiloxanes according to claim 1 , wherein at least 80 mol % of the repeating units of the one or more polyalkylhydrosiloxanes according to the general structure (I) have a residue R 1 that is a methyl group.

11. A water-based metal casting mold release agent composition comprising:
1) 1-50 wt.-% of a mixture of polyalkylsiloxanes according to claim 1 ,
2) 1-15 wt.-% of a non-ionic surfactant having an HLB value of at least 8, and
3) less than 20 wt.-% of waxes.

12. A polyalkylsiloxane comprising repeating units according to general structure (II):

wherein n represents the number of repeating units comprised in the polyalkylsiloxane, and n is an integer of 5 to 10,000;
wherein residue R 1 is selected from the group consisting of linear or branched alkyl groups with less than 6 carbon atoms; and
a) in 1-20% of the repeating units, R 2 is selected from the group consisting of linear or branched alkyl groups with 40 to 60 carbon atoms;
b) in 1-20% of the repeating units, R 2 is selected from the group consisting of linear or branched alkyl groups with 16 to 30 carbon atoms;
c) in 60-98% of the repeating units, R 2 is selected from the group consisting of linear or branched alkyl groups with 6 to 15 carbon atoms; and
d) in 0-10% of the repeating units, R 2 is H.

13. The polyalkylsiloxane according to claim 12 , wherein in c), R 2 is selected from the group consisting of linear or branched alkyl groups with 10 to 14 carbon atoms.

14. The polyalkylsiloxane according to claim 12 , wherein
a) in 2-10% of the repeating units, R 2 is selected from the group consisting of linear or branched alkyl groups with 40 to 60 carbon atoms;
b) in 2-15% of the repeating units, R 2 is selected from the group consisting of linear or branched alkyl groups with 16 to 30 carbon atoms,
c) in 75-96% of the repeating units, R 2 is selected from the group consisting of linear or branched alkyl groups with 6 to 15 carbon atoms.

15. The polyalkylsiloxane according to claim 12 , wherein the polyalkylsiloxane has a ratio of the repeating units according to a) to the repeating units according to b) in a range of from 2:3 to 3:2.

16. The polyalkylsiloxane according to claim 12 , wherein the polyalkylsiloxane is an oil.

17. The polyalkylsiloxane according to claim 12 , wherein R 1 of each repeating unit according to general structure (II) is a methyl group.

18. A water-based metal casting mold release agent composition comprising:
1) 1-50 wt.-% of at least one polyalkylsiloxane according to claim 12 ,
2) 1-15 wt.-% of a non-ionic surfactant having an HLB value of at least 8, and
3) less than 20 wt.-% of waxes.

19. A metal casting process comprising:
A.) applying a mold release agent to a metal-casting mold, the mold release agent comprising at least one polyalkylsiloxane selected from:
i) a polyalkylsiloxane mixture obtained through a hydrosilylation reaction wherein a mixture of monounsaturated olefins consisting of 1-20 mol % of olefins with 40 to 60 carbon atoms, 1-20 mol % of olefins with 16 to 30 carbon atoms, and 60-98 mol % of olefins with 6 to 15 carbon atoms is reacted with an amount of one or more polyalkylhydrosiloxanes in the presence of a hydrosilylation catalyst,
wherein each of the one or more polyalkylhydrosiloxanes comprises a repeating unit according to the general structure (I):

wherein n indicates the number of repeating units and ranges from 5 to 10,000; and
wherein the residue R 1 is selected from linear or branched alkyl groups with less than 6 carbon atoms;
ii) a polyalkylsiloxane comprising repeating units according to general structure (II):

wherein n represents the number of repeating units comprised in the polyalkylsiloxane, and n is an integer of 5 to 10,000;
wherein residue R 1 is selected from the group consisting of linear or branched alkyl groups with less than 6 carbon atoms;
a) in 1-20% of the repeating units, R 2 is selected from the group consisting of linear or branched alkyl groups with 40 to 60 carbon atoms;
b) in 1-20% of the repeating units, R 2 is selected from the group consisting of linear or branched alkyl groups with 16 to 30 carbon atoms;
c) in 60-98% of the repeating units, R 2 is selected from the group consisting of linear or branched alkyl groups with 6 to 15 carbon atoms; and
d) in 0-10% of the repeating units, R 2 is H;

iii) a polyalkylsiloxane comprise a repeating unit according to the following general structure (Ill):

wherein n indicates the number of r

Assignees

• Henkel Ag & Co Kgaa

Inventors

• Kok Douwe Marten
• Slagt Martijn Quico
• Odink Gerrit Jan
• Braam Johannes Hendrikus Gerhardus Franciscus

Classifications

• C10N2040/36

  Release agents {or mold release agents} · CPC title

• B29C33/64

  Silicone · CPC title

• C10M155/04

  Monomer containing boron · CPC title

• C08G77/38 Primary

  Polysiloxanes modified by chemical after-treatment · CPC title

• B22D29/00

  Removing castings from moulds, not restricted to casting processes covered by a single main group; Removing cores; Handling ingots {(B22D13/10, B22D11/124, B22D17/00 take precedence)} · CPC title