Method of applying a thermal barrier coating to a metallic article and a thermal barrier coated metallic article

Patent metadata

Field	Value
Publication number	US-9963774-B2
Application number	US-201514836502-A
Country	US
Kind code	B2
Filing date	Aug 26, 2015
Priority date	Sep 19, 2014
Publication date	May 8, 2018
Grant date	May 8, 2018

Abstract

A thermal barrier coated metallic article includes a platinum-group metal enriched outer layer on the article. The surface of the outer layer has a microstructure including a plurality of projections extending away from the metallic article. A thin adherent layer of oxide is formed on the outer layer of the metallic article. A ceramic coating is provided on the oxide layer on the surface on and around the projections. The ceramic coating includes a plurality of columnar ceramic grains which extend through the full thickness of the ceramic coating. The grains are arranged in clusters separated by gaps. The grains deposited around the projections are generally blocked. The projections reduce the stress in the ceramic coating near the interface with the adherent layer of oxide and also reduce the stress in the adherent layer of oxide and hence increase the working life of the thermal barrier coating system.

First claim

The invention claimed is:

1. A method of applying a thermal barrier coating to a metallic article comprising the steps of:
(a) providing a plurality of projections extending away from the surface of the metallic article,
(b) creating a thin adherent layer of oxide on the metallic article, and
(c) applying a ceramic coating to the oxide layer on the surface of the metallic article such that the ceramic coating deposits on the surface of the metallic article on and around the projections, applying the ceramic coating as a plurality of columnar ceramic grains extending substantially perpendicularly away from the metallic article, a plurality of the columnar ceramic grains nucleating on and extending from the oxide layer on the projections on the metallic article, a plurality of the columnar ceramic grains nucleating on and extending from the oxide layer around the projections on the metallic article, a plurality of the columnar ceramic grains extending from the oxide layer on the projections on the metallic article extending through the full thickness of the ceramic coating, a plurality of the columnar ceramic grains extending from the oxide layer around the projections on the metallic article only extending part way through the full thickness of the ceramic coating, one or more columnar ceramic grains growing from each projection, the columnar ceramic grains growing together from a respective one of the projections being arranged in a cluster of columnar ceramic grains and the clusters of columnar ceramic grains being separated by gaps,
wherein step (a) comprises forming the plurality of projections by power beam sculpturing.

2. A method of applying a thermal barrier coating to a metallic article comprising the steps of:—
(a) providing a plurality of projections extending away from the surface of the metallic article,
(b) creating a thin adherent layer of oxide on the metallic article, and
(c) applying a ceramic coating to the oxide layer on the surface of the metallic article such that the ceramic coating deposits on the surface of the metallic article on and around the projections, applying the ceramic coating as a plurality of columnar ceramic grains extending substantially perpendicularly away from the metallic article, a plurality of the columnar ceramic grains nucleating on and extending from the oxide layer on the projections on the metallic article, a plurality of the columnar ceramic grains nucleating on and extending from the oxide layer around the projections on the metallic article, a plurality of the columnar ceramic grains extending from the oxide layer on the projections on the metallic article extending through the full thickness of the ceramic coating, a plurality of the columnar ceramic grains extending from the oxide layer around the projections on the metallic article only extending part way through the full thickness of the ceramic coating, one or more columnar ceramic grains growing from each projection, the columnar ceramic grains growing together from a respective one of the projections being arranged in a cluster of columnar ceramic grains and the clusters of columnar ceramic grains being separated by gaps,
wherein step (a) comprises providing a bond coating on the metallic article, the surface of the bond coating on the metallic article having a plurality of projections extending away from the metallic article, and the bond coating is deposited by applying the bond coating by electroplating and then heat treating the bond coating, step (b) comprises creating a thin adherent layer of oxide on the bond coating, and step (c) comprises applying a ceramic coating to the oxide layer on the surface of the bond coating.

3. The method of applying a thermal barrier coating to a metallic article as claimed in claim 2 , further comprising the steps of:
(a-1) applying a layer of platinum-group metal to the metallic article, applying the platinum-group metal by an electroplating process, heat treating the platinum-group-metal coated metallic article to diffuse the platinum-group metal into the metallic article to create a platinum-group metal enriched outer layer on the metallic article, the surface of the platinum-group metal enriched outer layer on the metallic article having a microstructure comprising a plurality of projections extending away from the metallic article,
(b-1) creating a thin adherent layer of oxide on the platinum-group metal enriched outer layer of the metallic article, and
(c-1) applying a ceramic coating to the oxide layer on the surface of the bond coating such that the ceramic coating deposits on the surface of the bond coating on and around the projections, applying the ceramic coating as a plurality of columnar ceramic grains extending substantially perpendicularly away from the metallic article, a plurality of the columnar ceramic grains nucleating on and extending from the oxide layer on the projections on the bond coating, a plurality of the columnar ceramic grains nucleating on and extending from the oxide layer around the projections on the bond coating, a plurality of the columnar ceramic grains extending from the oxide layer on the projections on the bond coating extending through the full thickness of the ceramic coating, a plurality of the columnar ceramic grains extending from the oxide layer around the projections on the bond coating only extending part way through the full thickness of the ceramic coating, one or more columnar ceramic grains growing from each projection, the columnar ceramic grains growing together from a respective one of the projections being arranged in a cluster of columnar ceramic grains and the clusters of columnar ceramic grains being separated by gaps.

4. The method of applying a thermal barrier coating to a metallic article as claimed in claim 3 , wherein at least some of the projections extend between 10 μm and 25 μm from the surface of the platinum enriched surface layer immediately adjacent to the projections.

5. The method of applying a thermal barrier coating to a metallic article as claimed in claim 3 , wherein the metallic article comprises a superalloy substrate, the superalloy substrate comprises a gamma phase and gamma prime phase, the platinum-group metal enriched outer layer comprises a platinum-group metal enriched gamma phase and a platinum-group metal enriched gamma prime phase.

6. The method of applying a thermal barrier coating to a metallic article as claimed in claim 3 , wherein the metallic article comprises a superalloy substrate and an overlay coating on the superalloy substrate, the superalloy substrate comprises gamma phase and gamma prime phase, the platinum-group metal enriched outer layer comprises a platinum-group metal enriched overlay layer and a platinum-group metal aluminide layer on the platinum-group metal enriched overlay layer.

7. The method of applying a thermal barrier coating to a metallic article as claimed in claim 3 , wherein the heat treatment is carried out at a temperature in the range of 1100° C. to 1200° C. dependent upon the solution heat treatment temperature appropriate for the superalloy article.

8. The method of applying a thermal barrier coating to a metallic article as claimed in claim 3 , wherein the platinum-group metal comprises platinum.

9. The method of applying a thermal barrier coating to a metallic article as claimed in claim 8 , wherein the thickness of the layer of platinum as applied before heat treatment being greater than 3 μm and less than 12.5 μm.

10. The method of applying a thermal barrier coating to a metallic article as claimed in claim 3 , wherein the ceramic coating is applied by a method selected from the group consisting of electron beam physical vapour deposition and plasma s

Assignees

• Rolls Royce Plc

Inventors

• Rickerby David Stafford
• Jones Robert Edward
• Chalk Christine

Classifications

• F05D2300/2118

  Zirconium oxides · CPC title

• B23K2101/001

  Turbines · CPC title

• C23C28/3455

  with a refractory ceramic layer, e.g. refractory metal oxide, ZrO2, rare earth oxides or a thermal barrier system comprising at least one refractory oxide layer · CPC title

• B23K15/00

  Electron-beam welding or cutting · CPC title

• F05D2230/90

  Coating; Surface treatment · CPC title