Method for producing carbon fibers from polyacrylonitrile (PAN) polymers with low polydispersity index (PDI)

Patent metadata

Field	Value
Publication number	US-9957645-B2
Application number	US-201414549764-A
Country	US
Kind code	B2
Filing date	Nov 21, 2014
Priority date	Dec 23, 2013
Publication date	May 1, 2018
Grant date	May 1, 2018

Abstract

A method for synthesizing polyacrylonitrile (PAN) polymer with a narrow molecular weight distribution is disclosed. The preferred PAN polymer has a PDI (Mw/Mn) of about 2 or less. Such PAN polymer is synthesized by controlled/living radical polymerization using a special RAFT (Reversible Addition-Fragmentation Chain Transfer) agent. Also disclosed is a method for producing carbon fibers from PAN polymer with low PDI.

First claim

What is claimed is:

1. A method for producing a carbon fiber, comprising:
a) combining acrylonitrile (AN) monomer with a solvent, at least one co-monomer, and a thiocarbonylthio compound to form a solution;
b) heating the solution to a temperature within the range of 40° C.-85° C.; and
c) adding an initiator to the heated solution to affect polymerization reaction, thereby forming a polymer solution comprising polyacrylonitrile (PAN) polymer,
wherein polymerization is affected by controlled/living radical polymerization, in which the thiocarbonylthio compound functions as a Reversible Addition/Fragmentation Chain Transfer (RAFT) agent,
wherein the thiocarbonylthio compound is selected from the following structures:

where Z 1 is selected from:
—CH 2 —(CH 2 ) 10 —CH 3 ; —(CH 2 ) n —CH 3 , n=0-20;
—C(CH 3 ) m —COOH, m=1-2; —C(CH 3 ) m —COOCH 3 , m=1-2;
—C(CH 3 ) m —COOC 2 H 5 , m=1-2;
R 1 is selected from:

R′ 1 is selected from: —CN;

x=0-1;
R″ 1 is selected from: H; —CH 3 ; —(CH 2 ) m —COOH, m=1-2;
R′″ 1 is H or —CH 3

where Z 2 is selected from:

R is selected from: F, Cl, CN, OCH 3 ;
R 2 is selected from:

R′ 2 is selected from: —CN;

x=0-1;
—C(CH 3 ) m —COOCH 3 , m=1-2;
—C(CH 3 ) m —COOC 2 H 5 , m=1-2;
R″ 2 is selected from: H; —CH 3 ; —(CH 2 ) m —COOH, m=1-2;
R′″ 2 is H or —CH 3

where Z 3 is selected from: —CH 2 —(CH 2 ) 10 —CH 3 ; —(CH 2 ) y —CH 3 , y=1-20;
R 3 is selected from: —CH 2 —(CH 2 ) 10 —CH 3 ; —(CH 2 ) y —CH 3 , y=1-20,
wherein the PAN polymer has a polydispersity index (PDI) of about 2 or less and a molecular weight within the range of 60 kg/mole to 500 kg/mole;
d) spinning the polymer solution by wet spinning or air-gap spinning to form a PAN fiber precursor;
e) oxidizing the PAN fiber precursor; and
f) carbonizing the oxidized fiber precursor.

2. The method of claim 1 , wherein the PAN polymer has a molecular weight within the range of 115 kg/mole to 180 kg/mole.

3. The method according to claim 1 , wherein the PAN polymer has a PDI (Mw/Mn) of 1.2 to 1.9.

4. The method according to claim 1 , wherein the solvent is selected from the group consisting of: dimethyl sulfoxide (DMSO), dimethyl formamide (DMF), and dimethyl acetamide (DMAc), a mixture of zinc chloride (ZnCl 2 ) and water, and a mixture of sodium thiocyanate (NaSCN) and water.

5. The method according to claim 1 , wherein the at least one co-monomer is selected from the group consisting of: vinyl-based acids, vinyl-based esters, and vinyl derivatives.

6. The method of claim 5 , wherein the at least one co-monomer is selected from the group consisting of: methacrylic acid (MAA), acrylic acid (AA), itaconic acid (ITA), methacrylate (MA), methyl methacrylate (MMA), vinyl acetate (VA), ethyl acrylate (EA), butyl acrylate (BA), ethyl methacrylate (EMA), vinyl imidazole (VIM), acrylamide (AAm), diacetone acrylamide (DAAm).

7. The method according to claim 1 , wherein the initiator is an azo compound or an organic peroxide.

8. The method according to claim 7 , wherein the initiator is selected from the group consisting of: azobisisobutyronitrile (AIBN), azobiscyanovaleric acid (ACVA), 2,2′-azobis-(2,4-Dimethyl) valeronitrile (ABVN), dilauroyl peroxide (LPO), ditertbutul peroxide (TBPO), diisopropyl peroxydicarbonate (IPP).

9. The method according to claim 1 , wherein the thiocarbonylthio compound is selected from:
a) 2-cyano-2-propyl dodecyl trithiocarbonate (CPDTC)

and
b) bis-dodecylsufanylthiocarbonyl disulfide (BDSTD)

10. The method of claim 1 , wherein the polymer solution of PAN polymer for spinning has a polymer concentration within the range of 5%-28% by weight based on the total weight of the solution.

11. The method of claim 1 , wherein oxidizing is carried out within the temperature range of 200° C.-300° C.

12. The method of claim 1 , wherein carbonizing includes pre-carbonization in an inert gas at a lower first temperature within the range of 300° C.-900° C., followed by carbonization at a higher second temperature within the temperature range of 700° C.-1650° C., said second temperature being higher than the first temperature.

Assignees

• Cytec Ind Inc

Inventors

• Tang Longgui
• Thomas Alan D
• Harmon Billy D

Classifications

• C08F2/06 Primary

  Organic solvent · CPC title

• D01F9/22 Primary

  from polyacrylonitriles · CPC title

• C08F220/44

  Acrylonitrile · CPC title

• C08F6/003

  from polymer solutions, suspensions, dispersions or emulsions without recovery of the polymer therefrom · CPC title

• B29D99/0078

  Producing filamentary materials · CPC title