Liquid film based on silane-terminated polymers

Patent metadata

Field	Value
Publication number	US-9957415-B2
Application number	US-201414553683-A
Country	US
Kind code	B2
Filing date	Nov 25, 2014
Priority date	Dec 19, 2008
Publication date	May 1, 2018
Grant date	May 1, 2018

Abstract

A composition that includes at least one silane-functional polymer P and 20 to 60% by weight of aluminum hydroxide or magnesium hydroxide or mixture thereof, is disclosed. The composition has a viscosity of 500 to 20,000 mPa·s measured according to DIN 53018 at a temperature of 20° C. The composition is suitable as a liquid membrane and has very good flammability properties, i.e., it is difficult to ignite and is self-extinguishing.

First claim

What is claimed is:

1. A liquid composition that is suitable for applying as a fluid to a substrate to form a liquid membrane, the liquid composition comprising:
a) at least one silane-functional polyurethane polymer P2 that is completely free of isocyanate groups; and
b) 20 to 60% by weight of aluminum hydroxide, magnesium hydroxide or a combination thereof;
wherein the liquid composition has a viscosity of 500 to 20,000 mPa·s that is measured according to DIN 53018 at a temperature of 20° C. and a shear rate of 10 s −1 ,
wherein the at least one silane-functional polyurethane polymer P2 is obtained by a reaction of an isocyanatosilane IS with a polymer which has functional end groups which are reactive to isocyanate groups, wherein the reaction is performed in a stoichiometric ratio of (a number of groups which are reactive to isocyanate groups):a number of isocyanate groups) of 1:1 or in an excess of the number of groups which are reactive to isocyanate groups compared to the number of isocyanate groups, and
wherein the composition does not contain any volatile organic solvents.

2. The composition according to claim 1 , wherein the isocyanatosilane IS is a compound of Formula (V)

wherein
the radical R 1 stands for a linear or branched, monovalent hydrocarbon radical with 1 to 8 C atoms;
the radical R 2 stands for an acyl radical or for a linear or branched, monovalent hydrocarbon radical with 1 to 5 C atoms;
the radical R 3 stands for a linear or branched, divalent hydrocarbon radical with 1 to 12 C atoms, which optionally has cyclic and/or aromatic portions, and optionally one or more heteroatoms; and
a stands for a value of 0 or 1 or 2.

3. The composition according to claim 1 , wherein the polymer which has functional end groups which are reactive to isocyanate groups, is a polyoxyalkylene polyol.

4. The composition according to claim 2 , wherein the isocyanatosilane IS is selected from the group consisting of isocyanatomethyltrimethoxysilane, isocyanatomethyldimethoxymethylsilane, 3-isocyanatopropyltrimethoxysilane, 3-isocyanatopropyldimethoxymethylsilane, and an analog thereof with ethoxy or isopropoxy groups instead of methoxy groups on silicon.

5. The composition according to claim 1 , wherein the composition has a viscosity of 500 to 15,000 mPa·s measured according to DIN 53018 at a temperature of 20° C. and a shear rate of 10 s −1 .

6. The composition according to claim 1 , wherein the composition has a viscosity of 500 to 10,000 mPa·s measured according to DIN 53018 at a temperature of 20° C. and a shear rate of 10 s −1 .

7. A method of applying a film, comprising applying the composition of claim 1 in liquid form to a substrate.

8. The method of claim 7 , wherein the substrate is a structure, and the composition is for sealing the structure.

9. A method for the production of a film for sealing a substrate, the method comprising:
i) providing a composition according to claim 1 ;
ii) applying the composition in a liquid state to the substrate to be sealed;
iii) curing of the applied composition by means of moisture to form a film.

10. The method according to claim 9 , wherein the composition is applied to the substrate using a roller, a paintbrush, a knife, a disk, a coating knife, a rubber slide, or a spraying device.

11. The method according to claim 9 , wherein the composition is applied in multiple layers.

12. A film formed from the method according to claim 9 .

13. The composition according to claim 1 , wherein the composition has a viscosity of 2,000 to 15,000 mPa·s that is measured according to DIN 53018 at a temperature of 20° C. and a shear rate of 10 s −1 .

14. The composition according to claim 1 , wherein the composition has a viscosity of 4,000 to 10,000 mPa·s that is measured according to DIN 53018 at a temperature of 20° C. and a shear rate of 10 s −1 .

15. The composition according to claim 2 , wherein in Formula (V), a is 0, wherein the composition has a viscosity of 4,000 to 10,000 mPa·s that is measured according to DIN 53018 at a temperature of 20° C. and a shear rate of 10 s −1 .

16. The composition according to claim 1 , wherein the composition does not contain a thixotropic agent.

17. A liquid composition that is suitable for applying as a fluid to a substrate to form a liquid membrane, the liquid composition comprising:
a) at least one silane-functional polymer P2; and
b) 20 to 60% by weight of aluminum hydroxide, magnesium hydroxide or a combination thereof;
wherein the liquid composition has a viscosity of 500 to 20,000 mPa·s that is measured according to DIN 53018 at a temperature of 20° C. and a shear rate of 10 s −1 ,
wherein the at least one silane-functional polymer P2 is obtained by a reaction of an isocyanatosilane IS with a polymer which has functional end groups which are reactive to isocyanate groups, wherein the reaction is performed in a stoichiometric ratio of (a number of groups which are reactive to isocyanate groups):(a number of isocyanate groups) of 1:1 or in an excess of the number of groups which are reactive to isocyanate groups compared to the number of isocyanate groups, and
wherein the composition does not contain a thixotropic agent.

18. The liquid composition according to claim 1 , wherein the liquid composition includes 30 to 55% by weight of the aluminum hydroxide, magnesium hydroxide, or the combination thereof.

19. The liquid composition according to claim 1 , wherein the liquid composition includes 40 to 50% by weight of the aluminum hydroxide, magnesium hydroxide, or the combination thereof.

20. The liquid composition according to claim 1 , wherein the composition has a viscosity of 500 to 20,000 mPa·s that is measured according to DIN 53018 at a temperature of 20° C. and a shear rate of 100 s −1 .

Assignees

• Sika Tech Ag

Inventors

• Pusel Thomas
• Teysseire Raphael
• Tenisch Willi
• Strauss Susanne
• Jucker Barbara
• Zilg Carsten

Classifications

• C08K5/521

  Esters of phosphoric acids, e.g. of H3PO4 · CPC title

• C08K3/22

  of metals · CPC title

• C08K13/02

  Organic and inorganic ingredients · CPC title

• C09D175/04 Primary

  Polyurethanes · CPC title

• C08L2203/16

  used for films · CPC title