Method for producing oxide catalyst, and method for producing unsaturated nitrile

Patent metadata

Field	Value
Publication number	US-9950313-B2
Application number	US-201615563381-A
Country	US
Kind code	B2
Filing date	Mar 30, 2016
Priority date	Mar 31, 2015
Publication date	Apr 24, 2018
Grant date	Apr 24, 2018

Abstract

The present invention provides a method for producing an oxide catalyst comprising Mo, V, Sb, and Nb for use in a gas-phase catalytic oxidation reaction or a gas-phase catalytic ammoxidation reaction of propane or isobutane, the method comprising: a preparation step of preparing a first aqueous mixed solution containing Mo, V, and Sb; a mixing step of mixing the first aqueous mixed solution with a support raw material comprising silica sol, and a Nb raw material to obtain a second aqueous mixed solution; a drying step of drying the second aqueous mixed solution to obtain a dry powder; and a calcination step of calcining the dry powder to obtain the oxide catalyst, wherein the support raw material comprises 25% by mass or more, based on SiO 2 , of the silica sol having an average primary particle size of 3.0 nm or larger and smaller than 11 nm based on a total amount of the support raw material, and the silica sol comprises 55% or more of silica sol particles having a primary particle size of smaller than 11 nm.

First claim

What is claimed is:

1. A method for producing an oxide catalyst comprising Mo, V, Sb, and Nb for use in a gas-phase catalytic oxidation reaction or a gas-phase catalytic ammoxidation reaction of propane or isobutane, the method comprising:
a preparation step of preparing a first aqueous mixed solution containing Mo, V, and Sb;
a mixing step of mixing the first aqueous mixed solution with a support raw material comprising silica sol, and a Nb raw material to obtain a second aqueous mixed solution;
a drying step of drying the second aqueous mixed solution to obtain a dry powder; and
a calcination step of calcining the dry powder to obtain the oxide catalyst, wherein
the support raw material comprises 25% by mass or more, based on SiO 2 , of the silica sol having an average primary particle size of 3.0 nm or larger and smaller than 11 nm based on a total amount of the support raw material, and the silica sol comprises 55% or more of silica sol particles having a primary particle size of smaller than 11 nm.

2. The method for producing the oxide catalyst according to claim 1 , wherein the oxide catalyst has a composition represented by following formula (1):
MoV a Sb b Nb c Z d O n   (1)

wherein Z represents at least one element selected from the group consisting of W, La, Ce, Yb, and Y; a, b, c, and d represent values in ranges of 0.01≤a≤0.35, 0.01≤b≤0.35, 0.01≤c≤0.20, and 0.00≤d≤0.10, respectively; and n represents a value that satisfies balance among valences.

3. The method for producing the oxide catalyst according to claim 2 , wherein in the formula (1), (a/b) is 0.50 or more and 0.98 or less.

4. The method for producing the oxide catalyst according to claim 1 , wherein the oxide catalyst comprises 30% by mass or more and 70% by mass or less of a support based on the total amount of the oxide catalyst.

5. The method for producing the oxide catalyst according to claim 1 , wherein the support raw material further comprises powder silica.

6. The method for producing the oxide catalyst according to claim 1 , wherein the support raw material comprises 30% by mass or more and 70% by mass or less, based on SiO 2 , of the silica sol based on the total amount of the support raw material.

7. A method for producing unsaturated nitrile, comprising a production step of producing unsaturated nitrile by a gas-phase catalytic ammoxidation reaction of propane or isobutane in presence of an oxide catalyst comprising Mo, V, Sb, and Nb for use in a gas-phase catalytic oxidation reaction or a gas-phase catalytic ammoxidation reaction of propane or isobutane, and
wherein the oxide catalyst is prepared by a method comprising:
a preparation step of preparing a first aqueous mixed solution containing Mo, V, and Sb;
a mixing step of mixing the first aqueous mixed solution with a support raw material comprising silica sol, and a Nb raw material to obtain a second aqueous mixed solution;
a drying step of drying the second aqueous mixed solution to obtain a dry powder; and
a calcination step of calcining the dry powder to obtain the oxide catalyst, wherein
the support raw material comprises 25% by mass or more based on SiO 2 , of the silica sol having an average primary particle size of 3.0 nm or larger and smaller than 11 nm based on a total amount of the support raw material, and the silica sol comprises 55% or more of silica sol particles having a primary particle size of smaller than 11 nm.

Assignees

• Asahi Chemical Ind

Inventors

• Miike Satoshi
• Tateno Eri
• Ishii Yusuke

Classifications

• C07C253/24

  by ammoxidation of hydrocarbons or substituted hydrocarbons · CPC title

• B01J37/08

  Heat treatment {(B01J37/0009, B01J37/0018 take precedence)} · CPC title

• B01J23/30 Primary

  Tungsten · CPC title

• B01J2523/00

  Constitutive chemical elements of heterogeneous catalysts · CPC title

• B01J23/002 Primary

  Mixed oxides other than spinels, e.g. perovskite · CPC title