Hot-rolled steel sheet for production of non-oriented electrical steel sheet and method of manufacturing same

Patent metadata

Field	Value
Publication number	US-9947446-B2
Application number	US-201314435314-A
Country	US
Kind code	B2
Filing date	Oct 11, 2013
Priority date	Oct 16, 2012
Publication date	Apr 17, 2018
Grant date	Apr 17, 2018

Abstract

The pickling loss when a hot-rolled steel sheet having a predetermined chemical composition is annealed at 1000° C. for 30 seconds in a nitrogen atmosphere and then immersed in a solution of 7% HCl at 80° C. for 60 seconds is in a range of 40 g/m 2 or more and 100 g/m 2 or less. A hot-rolled steel sheet for production of a non-oriented electrical steel sheet with not only excellent magnetic properties such as iron loss and magnetic flux density but also excellent recyclability and steel sheet surface appearance can thus be obtained.

First claim

The invention claimed is:

1. A hot-rolled steel sheet for production of a non-oriented electrical steel sheet, the hot-rolled steel sheet having 1) a chemical composition consisting of, in mass %; 0.005% or less C; 1.5% or more and 4.5% or less Si; 0.005% or less Al; 0.20% or less Mn; 0.003% or less S; 0.003% or less N; 0.03% or more and 0.2% or less P; and 0.002% or more and 0.03% or less Mo with balance being Fe and incidental impurities, and 2) a pickling loss of 40 g/m 2 or more and 100 g/m 2 or less when the hot-rolled steel sheet is subjected to annealing at 1000° C. for 30 seconds in a nitrogen atmosphere and then immersed in a solution of 7% HCl at 80° C. for 60 seconds.

2. A hot-rolled steel sheet for production of a non-oriented electrical steel sheet, the hot-rolled steel sheet having 1) a chemical composition consisting of, in mass %, 0.005% or less C; 1.5% or more and 4.5% or less Si; 0.005% or less Al; 0.20% or less Mn; 0.003% or less S; 0.003% or less N; 0.03% or more and 0.2% or less P; 0.002% or more and 0.03% or less Mo, and at least one selected from: 0.005% or more and 0.2% or less Sb; 0.005% or more and 0.2% or less Sn; and 0.05% or more and 0.5% or less Cr, with balance being Fe and incidental impurities, and 2) a pickling loss of 40 g/m 2 or more and 100 g/m 2 or less when the hot-rolled steel sheet is subjected to annealing at 1000° C. for 30 seconds in a nitrogen atmosphere and then immersed in a solution of 7% HCl at 80° C. for 60 seconds.

3. A method of manufacturing a hot-rolled steel sheet for production of a non-oriented electrical steel sheet, comprising:
heating a slab having a chemical composition consisting of, in mass %: 0.005% or less C; 1.5% or more and 4.5% or less Si; 0.005% or less Al; 0.20% or less Mn; 0.003% or less S; 0.003% or less N; 0.03% or more and 0.2% or less P; and 0.002% or more and 0.03% or less Mo with balance being Fe and incidental impurities;
hot rolling the slab to obtain a hot-rolled steel sheet; and
coiling the hot-rolled steel sheet,
wherein a finisher delivery temperature in the hot rolling is 825° C. or more and 925° C. or less, and a coiling temperature after completion of the hot rolling is 525° C. or more and 650° C. or less.

4. A method for manufacturing a hot-rolled steel sheet for production of a non-oriented electrical steel sheet, comprising:
heating a slab having a chemical composition consisting of, in mass %: 0.005% or less C; 1.5% or more and 4.5% or less Si; 0.005% or less Al; 0.20% or less Mn; 0.003% or less S; 0.003% or less N; 0.03% or more and 0.2% or less P; and 0.002% or more and 0.03% or less Mo, and at least one selected from: 0.005% or more and 0.2% or less Sb; 0.005% or more and 0.2% or less Sn; and 0.05% or more and 0.5% or less Cr, with balance being Fe and incidental impurities,
hot rolling the slab to obtain a hot-rolled steel sheet; and
coiling the hot-rolled steel sheet,
wherein a finisher delivery temperature in the hot rolling is 825° C. or more and 925° C. or less, and a coiling temperature after completion of the hot rolling is 525° C. or more and 650° C. or less.

Assignees

• Jfe Steel Corp

Inventors

• Toda Hiroaki
• Zaizen Yoshiaki
• Nakanishi Tadashi
• Oda Yoshihiko

Classifications

• C21D8/1277

  involving a particular surface treatment (C21D8/1294 takes precedence) · CPC title

• B21B15/00

  Arrangements for performing additional metal-working operations specially combined with or arranged in, or specially adapted for use in connection with, metal-rolling mills · CPC title

• H01F1/14775 Primary

  in the form of sheets · CPC title

• C22C38/12

  containing tungsten, tantalum, molybdenum, vanadium, or niobium · CPC title

• C22C38/02

  containing silicon · CPC title