Method for manufacturing an elastomeric composition having a self-sealing property

Patent metadata

Field	Value
Publication number	US-9944775-B2
Application number	US-201113576153-A
Country	US
Kind code	B2
Filing date	Jan 21, 2011
Priority date	Jan 28, 2010
Publication date	Apr 17, 2018
Grant date	Apr 17, 2018

Abstract

Process for the manufacture of an elastomer composition having a self-sealing property which is based on at least (phr meaning parts by weight per 100 parts of solid elastomer): a solid unsaturated diene elastomer; between 30 and 90 phr of a hydrocarbon resin; from 0 to less than 30 phr of filler; between 0.5 and 15 phr of thiuram polysulphide, in which, during a first stage or stage (a), a masterbatch comprising at least the solid unsaturated diene elastomer and between 30 and 90 phr of a hydrocarbon resin is prepared by mixing these various components in a mixer at a “hot compounding” temperature or up to a “hot compounding” temperature which is greater than the softening temperature of the hydrocarbon resin.

First claim

The invention claimed is:

1. A process for the manufacture of an inflatable article, wherein the inflatable article has an internal wall, the internal wall comprises a puncture-resistant layer formed of an elastomer composition which has a self-sealing property and comprises:
a solid unsaturated diene elastomer;
between 30 and 90 phr of a hydrocarbon resin;
a total amount of between 0 phr and 10 phr filler;
between 0.5 and 15 phr of thiuram polysulphide,

wherein the process comprises:
1) preparing the elastomeric composition; and
2) incorporating the elastomeric composition into the inner wall of the inflatable article;
the step 1) comprises, during a stage (a), preparing a masterbatch comprising at least the solid unsaturated diene elastomer and the hydrocarbon resin is by mixing at least the solid unsaturated diene elastomer and the hydrocarbon in a mixer at a temperature which is greater than the softening temperature of the hydrocarbon resin.

2. The process according to claim 1 , wherein, during the stage (a), the solid unsaturated diene elastomer is brought into contact with the hydrocarbon resin in the solid state.

3. The process according to claim 1 , wherein, during the stage (a), the solid unsaturated diene elastomer is brought into contact with the hydrocarbon resin in the liquid state.

4. The process according to claim 3 , wherein the hydrocarbon resin is injected in the liquid state into the mixer.

5. The process according to claim 1 , wherein the temperature is greater than 70° C.

6. The process according to claim 1 , wherein the stage (a) is carried out in a compounding screw extruder.

7. The process according to claim 1 , wherein, during a stage (b), the thiuram polysulphide is incorporated in the masterbatch prepared in the stage (a).

8. The process according to claim 7 , wherein the stage (b) is carried out in a compounding screw extruder.

9. The process according to claim 7 , wherein the stage (b) is carried out on an external mixer of the two-roll open mill type.

10. The process according to claim 7 , wherein the temperature during the stage (b) is kept lower than the softening temperature of the hydrocarbon resin.

11. The process according to claim 7 , wherein the temperature during the stage (b) is kept lower than 130° C.

12. The process according to claim 11 , wherein the temperature during the stage (b) is kept lower than 50° C.

13. The process according to claim 7 , wherein an intermediate stage of cooling the masterbatch is inserted between said stages (a) and (b) in order to cool the masterbatch to a temperature lower than the softening temperature of the hydrocarbon resin.

14. The process according to claim 7 , wherein an intermediate stage of cooling the masterbatch is inserted between said stages (a) and (b) in order to cool the masterbatch to a temperature lower than 130° C.

15. The process according to claim 7 , wherein a liquid plasticizer having a glass transition temperature (Tg) of less than −20° C. is additionally incorporated during the stage (b).

16. The process according to claim 7 , wherein a liquid plasticizer having a glass transition temperature (Tg) of less than −20° C. is incorporated during a stage (c) subsequent to the stage (b) in the same mixer or a different mixer from that of the stage (b).

17. The process according to claim 16 , wherein the stage (c) is carried out in a compounding screw extruder.

18. The process according to claim 16 , wherein the stage (c) is carried out on an external mixer of the two-roll open mill type.

19. The process according to claim 1 , wherein the solid unsaturated diene elastomer is selected from the group consisting of polybutadienes, natural rubber, synthetic polyisoprenes, butadiene copolymers, and mixtures of such elastomers.

20. The process according to claim 19 , wherein the solid unsaturated diene elastomer is natural rubber, a polybutadiene, or a mixture of natural rubber and polybutadiene.

21. The process according to claim 1 , wherein the content of the solid unsaturated diene elastomer is greater than 50 phr.

22. The process according to claim 1 , wherein the solid unsaturated diene elastomer constitutes the only solid elastomer of the composition.

23. The process according to claim 1 , wherein the number-average molar mass Mn of the solid unsaturated diene elastomer is between 100,000 and 5,000,000 g/mol.

24. The process according to claim 1 , wherein the content of hydrocarbon resin is within a range from 45 to 75 phr.

25. The process according to claim 1 , wherein the hydrocarbon resin exhibits a glass transition temperature (Tg) of greater than 0° C.

26. The process according to claim 1 , wherein the number-average molar molecular weight Mn of the hydrocarbon resin is between 400 and 2000 g/mol.

27. The process according to claim 1 , wherein the hydrocarbon resin is selected from the group consisting of cyclopentadiene (CPD) homopolymer or copolymer resins, dicyclopentadiene (DCPD) homopolymer or copolymer resins, terpene homopolymer or copolymer resins, terpene phenol homopolymer or copolymer resins, C 5 fraction homopolymer or copolymer resins, C 9 fraction homopolymer or copolymer resins, α-methylstyrene homopolymer or copolymer resins, and mixtures thereof.

28. The process according to claim 1 , wherein the filler is introduced during a stage subsequent to stage (a).

29. The process according to claim 1 , wherein the filler consists of carbon black.

30. The process according to claim 29 , wherein the content of the filler is less than 5 phr.

31. The process according to claim 30 , wherein the content of the filler is between 0.5 and 2 phr.

32. The process according to claim 1 , wherein the content of thiuram polysulphide is between 1 and 10 phr.

33. The process according to claim 1 , wherein a liquid plasticizer having a glass transition temperature (Tg) of less than −20° C. is additionally incorporated in the composition.

34. The process according to claim 33 , wherein the content of liquid plasticizer is less than 60 phr.

35. The process according to claim 34 , wherein the content of liquid plasticizer is within a range from 5 to 40 phr.

36. The process according to claim 33 , wherein the liquid plasticizer is selected from the group consisting of liquid elastomers, polyolefin oils, naphthenic oils, paraffinic oils, DAE oils, MES oils, TDAE oils, mineral oils, vegetable oils, ether plasticizers, ester plasticizers, phosphate plasticizers, sulphonate plasticizers, and mixtures thereof.

37. The process according to claim 36 , wherein the liquid plasticizer is selected from the group consisting of liquid elastomers, polyolefin oils, vegetable oils, and mixtures thereof.

38. The process according to claim 33 , wherein the number-average molar mass Mn of the liquid plasticizer is between 400 and 90,000 g/mol.

39. The process according to claim 33 , wherein the liquid plasticizer is incorporated in the masterbatch during stage (a).

Assignees

• Voge Bozena
• Araujo Da Silva Jose Carlos
• Merino Lopez Jose
• Michelin & Cie

Inventors

• Voge Bozena
• Araujo Da Silva José Carlos
• Merino Lopez Jose

Classifications

• B29B7/7495

  for mixing rubber · CPC title

• C08K5/40

  Thiurams, {i.e. compounds containing[IMAGE cpc-sch-C08K-1011.gif] groups} · CPC title

• B29L2030/00

  Pneumatic or solid tyres or parts thereof {(conveyor belts B29L2031/7092; drive belts B29L2031/7094; fourdrinier belts B29L2031/733)} · CPC title

• C08J3/226

  using a polymer as a carrier · CPC title

• C08K5/01

  Hydrocarbons {(C08K5/0091 takes precedence)} · CPC title