Process for producing water-absorbent polymer particles by polymerizing droplets of a monomer solution

Patent metadata

Field	Value
Publication number	US-9944739-B2
Application number	US-201715661543-A
Country	US
Kind code	B2
Filing date	Jul 27, 2017
Priority date	Nov 21, 2012
Publication date	Apr 17, 2018
Grant date	Apr 17, 2018

Abstract

The present invention relates to a process for producing water-absorbent polymer particles by polymerizing droplets of a monomer solution comprising less than 0.3% by weight of persulfate and at least 0.05% by weight of azo initiator and thermal aftertreatment of the formed polymer particles at less than 100° C. in a fluidized bed for 60 to 300 minutes.

First claim

The invention claimed is:

1. Water-absorbent polymer particles prepared according to by polymerizing droplets of
a) at least one ethylenically unsaturated monomer which bears an acid group and optionally is at least partly neutralized,
b) at least one crosslinker,
c 1 ) from 0.01 to less than 0.3% by weight, based on monomer a), of at least one persulfate,
c 2 ) at least 0.05% by weight, based on monomer a), of at least one azo initiator,
d) optionally one or more ethylenically unsaturated monomer copolymerizable with the monomer mentioned under a),
e) optionally one or more water-soluble polymer, and
f) water,
in a surrounding heated gas phase in a reaction zone and thermal posttreatment in a fluidized bed, wherein a temperature of a gas leaving the reaction zone is less than 150° C., a temperature of the water-absorbent polymer particles during the thermal posttreatment is less than 100° C., and a residence time of the water-absorbent polymer particles in the fluidized bed is from 60 to 300 minutes.

2. Polymer particles according to claim 1 , wherein the heated gas phase is flowing cocurrent to the droplets through the reaction zone.

3. Polymer particles according to claim 1 , wherein the monomer solution comprises from 0.05 to 0.15% by weight, based on monomer a), of the at least one persulfate.

4. Polymer particles process according to claim 1 , wherein the monomer solution comprises from 0.2 to 0.5% by weight, based on monomer a), of the at least one azo initiator.

5. Polymer particles according to claim 1 , wherein the temperature of the gas leaving the reaction zone is from 110 to 120° C.

6. Polymer particles according to claim 1 , wherein the temperature of the gas entering the reaction zone is from 160 to 200° C.

7. Polymer particles according to claim 1 , wherein a gas velocity inside the reaction zone is from 0.1 to 2.5 m/s.

8. Polymer particles according to claim 1 , wherein the temperature of the water-absorbent polymer particles during the thermal posttreatment is from 60 to 80° C.

9. Polymer particles according to claim 1 , wherein the residence time of the water-absorbent polymer particles in the fluidized bed is from 120 to 240 minutes.

10. Polymer particles according to claim 1 , wherein a gas velocity inside the fluidized bed is from 0.3 to 2.5 m/s.

11. Polymer particles according to claim 1 , wherein the gas entering the fluidized bed comprises from 0.02 to 0.15 kg steam per kg of dry gas.

12. Polymer particles according to claim 1 , wherein the ethylenically unsaturated monomer which bears an acid group is an ethylenically unsaturated carboxylic acid.

13. Polymer particles according to claim 1 , wherein the ethylenically unsaturated monomer which bears an acid group is acrylic acid.

14. A fluid-absorbent article, comprising
(A) an upper liquid-pervious layer,
(B) a lower liquid-impervious layer and
(C) a fluid-absorbent core between the layer (A) and the layer (B), comprising from 5 to 90% by weight fibrous material and from 10 to 95% by weight water-absorbent polymer particles according to claim 1 ,
(D) an optional acquisition-distribution layer between (A) and (C), comprising from 80 to 100% by weight fibrous material and from 0 to 20% by weight water-absorbent polymer particles according to claim 1 ,
(E) an optional tissue layer disposed immediately above and/or below (C); and
(F) other optional components.

15. A fluid-absorbent article, comprising water-absorbent polymer particles according to claim 1 and less than 15% by weight fibrous material and/or adhesives in the absorbent core.

16. Polymer particles according to claim 1 , wherein the monomer solution comprises from 0.1 to 0.15% by weight, based on monomer a) of the persulfate.

17. Water-absorbent polymer particles having a bulk density of at least 0.65 g/cm 3 , a centrifuge retention capacity of at least 35 g/g, and a HC 60 value of at least 80.

18. Polymer particles according to claim 17 , wherein the polymer particles have a bulk density of at least 0.7 g/cm 3 .

19. Polymer particles according to claim 17 , wherein the polymer particles have a centrifuge retention capacity of at least 40 g/g.

20. Polymer particles according to claim 17 , wherein the polymer particles have a HC 60 value of at least 90.

21. A fluid-absorbent article, comprising
(A) an upper liquid-pervious layer,
(B) a lower liquid-impervious layer and
(C) a fluid-absorbent core between the layer (A) and the layer (B), comprising from 5 to 90% by weight fibrous material and from 10 to 95% by weight water-absorbent polymer particles according to claim 17 ,
(D) an optional acquisition-distribution layer between (A) and (C), comprising from 80 to 100% by weight fibrous material and from 0 to 20% by weight water-absorbent polymer particles according to claim 17 ,
(E) an optional tissue layer disposed immediately above and/or below (C); and
(F) other optional components.

Assignees

• Basf Se

Inventors

• Daniel Thomas
• Herfert Norbert
• Bauer Stephan
• Baumann Katrin
• Reinhard Birgit
• Freiberg Jürgen
• Schliwa Rudolf

Classifications

• C08F220/06 Primary

  Acrylic acid; Methacrylic acid; Metal salts or ammonium salts thereof · CPC title

• A61L15/60

  Liquid-swellable gel-forming materials, e.g. super-absorbents · CPC title

• A61L15/24

  Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds; Derivatives thereof {(A61L15/225 takes precedence)} · CPC title

• B01J20/28023

  Fibres or filaments (fibres or filaments in the form of membranes B01J20/28038; B01J20/28007 takes precedence) · CPC title

• A61L15/42

  Use of materials characterised by their function or physical properties (liquid bandages A61L26/00) · CPC title