Surface-coated boron nitride sintered body tool

Patent metadata

Field	Value
Publication number	US-9943911-B2
Application number	US-201514899908-A
Country	US
Kind code	B2
Filing date	Mar 20, 2015
Priority date	Apr 25, 2014
Publication date	Apr 17, 2018
Grant date	Apr 17, 2018

Abstract

A surface-coated boron nitride sintered body tool is provided, in which a cutting edge portion includes a compound sintered body and a coating layer. The compound sintered body includes cBN particles. The compound sintered body includes 45-80 vol % of cBN particles. A first particle size distribution curve of the cBN particles has one or more peaks in a range in which a particle size is 0.1-0.7 μm. A second particle size distribution curve of the cBN particles has a first peak having a maximum peak height in a range in which the particle size is 2.0-7.0 μm. An integral value ratio (I o /I t ×100) is 1-20, in the second particle size distribution curve, the integral value I o being in the range in which the particle size is 0.1-0.7 μm, and the integral value I t being in an entire range.

First claim

The invention claimed is:

1. A surface-coated boron nitride sintered body tool, in which at least a cutting edge portion includes a compound sintered body and a coating layer provided on a surface of said compound sintered body,
said compound sintered body including cubic boron nitride particles and binder particles,
said compound sintered body including 45 vol % or more and 80 vol % or less of said cubic boron nitride particles,
in a case where a particle size distribution of said cubic boron nitride particles in at least one cross section of said compound sintered body is shown by a first particle size distribution curve plotted by a horizontal axis that is divided in each prescribed particle size range and a vertical axis that shows a proportion of the number of particles in each said particle size range, said first particle size distribution curve having one or more peaks in a range in which a particle size is 0.1 μm or more and 0.7 μm or less,
in a case where the particle size distribution of said cubic boron nitride particles in at least one cross section of said compound sintered body is shown by a second particle size distribution curve plotted by a horizontal axis that is divided in each prescribed particle size range and a vertical axis that shows a proportion of an area occupied by particles in each said particle size range, said second particle size distribution curve having a first peak having a maximum peak height in a range in which the particle size is 2.0 μm or more and 7.0 μm or less,
an integral value ratio (I o /I t ×100) between an integral value I o and an integral value I t being 1 or more and 7 or less, in said second particle size distribution curve, said integral value I o being in the range in which the particle size is 0.1 μm or more and 0.7 μm or less, and said integral value I t being in an entire range,
said coating layer including an A layer that is in contact with the surface of said compound sintered body, and a B layer provided on said A layer,
said A layer being made of Al 1-s Cr s N (0.2≤s≤0.9),
said B layer being made of Ti 1-t Al t N (0.3≤t≤0.8),
said A layer having a thickness of 0.05 μm or more and 0.5 μm or less,
said B layer having a thickness of 0.2 μm or more and 5 μm or less, and
said coating layer having an entire thickness of 0.3 μm or more and 7 μm or less.

2. The surface-coated boron nitride sintered body tool according to claim 1 , wherein
said compound sintered body includes 65 vol % or more and 75 vol % or less of said cubic boron nitride particles.

3. The surface-coated boron nitride sintered body tool according to claim 1 , wherein
in an X-ray diffraction spectrum of said compound sintered body, a peak height ratio (I TiB2 /I cBN ×100) of a peak height I TiB2 of a peak belonging to a (101) plane of TiB 2 to a peak height I cBN of a peak belonging to a (111) plane of said cubic boron nitride particle is 10 or more and 25 or less.

4. The surface-coated boron nitride sintered body tool according to claim 1 , wherein said binder particles have an average particle size of 50 nm or more and 500 nm or less.

5. The surface-coated boron nitride sintered body tool according to claim 1 , wherein
in a case where a thermal conductivity of said compound sintered body is defined as X (W/m·K) and a volume content of said cubic boron nitride particles in said compound sintered body is defined as Y (vol %), X/Y is 1.2 or more.

Assignees

• Sumitomo Electric Hardmetal Corp

Inventors

• Matsuda Yusuke
• Okamura Katsumi
• Sano Kenta
• Tsukihara Nozomi
• Setoyama Makoto

Classifications

• C04B41/455

  the coating or impregnating process including a chemical conversion or reaction · CPC title

• B23B2226/125

  cubic [CBN] · CPC title

• C04B35/6261

  Milling · CPC title

• C04B35/6303

  Inorganic additives · CPC title

• B23B2228/105

  with specified thickness · CPC title