Binder composition for making self-hardening foundry molds, and method of producing foundry mold using the same

Patent metadata

Field	Value
Publication number	US-9943903-B2
Application number	US-201214342183-A
Country	US
Kind code	B2
Filing date	Aug 31, 2012
Priority date	Aug 31, 2011
Publication date	Apr 17, 2018
Grant date	Apr 17, 2018

Abstract

The present invention relates to a binder composition for making self-hardening foundry molds that is capable of improving the hardening speed of the molds and the strength of the molds, and is excellent in storage stability; and a method for producing a foundry mold, using this composition. The binder composition for making self-hardening foundry molds of the present invention is a binder composition for making self-hardening foundry molds, comprising a furan resin and an ion compound, wherein the ion compound contains at least one anion selected from the group consisting of a hydrogensulfite ion, a sulfite ion, a pyrosulfite ion, a thiosulfate ion, a thionate ion, and a dithionite ion; the content of the anion is from 0.006 to 0.60 parts by weight for 100 parts by weight of the furan resin; and the composition has a pH of 6 or less at 25° C.

First claim

The invention claimed is:

1. A binder composition for making self-hardening foundry molds, comprising a furan resin and an ion compound, wherein the ion compound contains at least one anion selected from the group consisting of a hydrogensulfite ion, a sulfite ion, a pyrosulfite ion, a thiosulfate ion, a thionate ion, and a dithionite ion; the content of the anion is from 0.006 to 0.60 parts by weight for 100 parts by weight of the furan resin; and the composition has a pH of 6 or less at 25° C.

2. The binder composition for making self-hardening foundry molds according to claim 1 , wherein a cation in the ion compound is a metal ion selected from the group consisting of elements in Groups 1, 2 and 12 of the periodic table.

3. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the anion in the ion compound is one or more selected from the group consisting of a thiosulfate ion, a hydrogensulfite ion, and a sulfite ion.

4. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the cation of the ion compound is one or more selected from the group consisting of Na ion, K ion, Mg ion, Ca ion, and Zn ion.

5. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the ion compound is one or more selected from the group consisting of sodium hydrogensulfite, potassium hydrogensulfite, sodium sulfite, sodium thiosulfate, potassium thiosulfate, magnesium thiosulfate, calcium thiosulfate, sodium tetrathionate, and sodium dithionite.

6. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the content of the anion is from 0.009 to 0.50 parts both inclusive by weight for 100 parts by weight of the furan resin effective content.

7. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the content by percentage of the anion of the ion compound in the binder composition is from 0.006 to 0.54% both inclusive by weight.

8. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the content by percentage of the ion compound in the binder composition is from 0.005 to 2.0% both inclusive by weight.

9. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the pH of the furan resin at 25° C. is less than 7.

10. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the furan resin is a resin synthesized, using an acidic catalyst having a pKa of 5.0 or less.

11. The binder composition for making self-hardening foundry molds according to claim 10 , wherein the acidic catalyst is one or more selected from the group consisting of sulfuric acid, phosphoric acid, benzenesulfonic acid, p-toluenesulfonic acid, xylenesulfonic acid, methanesulfonic acid, tartaric acid, citric acid, malic acid, glycolic acid, lactic acid, benzoic acid, and formic acid.

12. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the content by percentage of free furfuryl alcohol in the furan resin is from 20 to 98% by weight.

13. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the content by percentage of furfuryl alcohol in the binder composition is from 20% to 98% both inclusive by weight.

14. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the water content by percentage in the furan resin is from 3.0 to 30% both inclusive by weight.

15. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the content by percentage of the furan resin (furan resin effective content) is from 50 to 99% both inclusive by weight.

16. The binder composition for making self-hardening foundry molds according to claim 1 , wherein the water content by percentage is more than 6.0% by weight and 30.0% or less by weight.

17. The binder composition for making self-hardening foundry molds according to claim 1 , which has a pH of from 2 to 5.8 both inclusive at 25° C.

18. The binder composition for making self-hardening foundry molds according to claim 1 , further comprising one or more selected from the group consisting of 2,5-bishydroxymethylfuran, 2,5-bismethoxymethylfuran, 2,5-bisethoxymethylfuran, 2-hydroxymethyl-5-methoxymethylfuran, 2-hydroxymethyl-5-ethoxymethylfuran, and 2-methoxymethyl-5-ethoxymethylfuran.

19. A composition for making self-hardening foundry molds, comprising the binder composition for making self-hardening foundry molds recited in claim 1 , refractory particles, and an acidic hardener.

20. A method for producing a foundry mold, comprising the steps of mixing the binder composition for making self-hardening foundry molds recited in claim 1 , refractory particles, and an acidic hardener with each other to yield a composition for making self-hardening foundry molds, and hardening the mixture.

Assignees

• Iwamoto Ryoji
• Yoshida Akira
• Kao Corp

Inventors

• Iwamoto Ryoji
• Yoshida Akira

Classifications

• B22C1/10

  for influencing the hardening tendency of the mould material (influencing the hardening tendency of the binding agent only B22C1/16) · CPC title

• C08K3/30

  Sulfur-, selenium- or tellurium-containing compounds · CPC title

• B22C1/167 Primary

  Mixtures of inorganic and organic binding agents · CPC title

• C08L61/34

  Condensation polymers of aldehydes or ketones with monomers covered by at least two of the groups C08L61/04, C08L61/18 and C08L61/20 · CPC title

• B22C9/02

  Sand moulds or like moulds for shaped castings · CPC title